Polypropylene composite material for automobile internal ornament, preparation method thereof and internal ornament

A composite material and automotive interior technology, which is applied in the field of interior parts, polypropylene composite materials and their preparation, can solve problems such as difficult to wipe clean dust, and achieve excellent mechanical properties, improved performance, and excellent surface scratch resistance Effect

Active Publication Date: 2013-07-24
GREAT WALL MOTOR CO LTD
View PDF2 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these polypropylene automotive interior parts tend to absorb dust

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polypropylene composite material for automobile internal ornament, preparation method thereof and internal ornament
  • Polypropylene composite material for automobile internal ornament, preparation method thereof and internal ornament

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] The components of the polypropylene material for automobile interior decoration of the present embodiment and their weight percentages are:

[0039] 55 parts by weight of polypropylene resin;

[0040] 20 parts by weight of filler;

[0041] Compatibilizer 3 parts by weight

[0042] 10 parts by weight of toughening agent;

[0043] 3 parts by weight of anti-scratch agent;

[0044] 3 parts by weight of odor adsorbent;

[0045] 5 parts by weight of antistatic agent;

[0046] Antioxidant 0.3 parts by weight; and

[0047] Lubricant 0.7 parts by weight.

[0048] Among them, the polypropylene is low-odor high-crystalline polypropylene, the filler is 2000 mesh talc, the compatibilizer is low-odor maleic anhydride grafted polypropylene, the toughening agent is POE, and the scratch-resistant agent is active polysiloxane. The odor adsorbent is a composition of zeolite, molecular sieve and nano-silica, and its mass ratio is 1:1:1, the antistatic agent is a ...

Example Embodiment

[0050] Example 2

[0051] The components of the polypropylene material for automobile interior decoration of the present embodiment and their weight percentages are:

[0052] 50 parts by weight of polypropylene resin;

[0053] 20 parts by weight of filler;

[0054] Compatibilizer 3 parts by weight

[0055] 10 parts by weight of toughening agent;

[0056] 3 parts by weight of anti-scratch agent;

[0057] 3 parts by weight of odor adsorbent;

[0058] 10 parts by weight of antistatic agent;

[0059] Antioxidant 0.3 parts by weight; and

[0060] Lubricant 0.7 parts by weight.

[0061] Among them, the polypropylene is low-odor high-crystalline polypropylene, the filler is 2000 mesh talc, the compatibilizer is low-odor maleic anhydride grafted polypropylene, the toughening agent is POE, and the scratch-resistant agent is active polysiloxane. The odor adsorbent is a composition of zeolite, molecular sieve and nano-silica, and its mass ratio is 1:1:1, the antistatic agent is a...

Example Embodiment

[0063] Example 3

[0064] The components of the polypropylene material for automobile interior decoration of the present embodiment and their weight percentages are:

[0065] 45 parts by weight of polypropylene resin;

[0066] 20 parts by weight of filler;

[0067] Compatibilizer 3 parts by weight

[0068] 10 parts by weight of toughening agent;

[0069] 3 parts by weight of anti-scratch agent;

[0070] 3 parts by weight of odor adsorbent;

[0071] 15 parts by weight of antistatic agent;

[0072] Antioxidant 0.3 parts by weight; and

[0073] Lubricant 0.7 parts by weight.

[0074]Among them, the polypropylene is low-odor high-crystalline polypropylene, the filler is 2000 mesh talc, the compatibilizer is low-odor maleic anhydride grafted polypropylene, the toughening agent is POE, and the scratch-resistant agent is active polysiloxane. The odor adsorbent is a composition of zeolite, molecular sieve and nano-silica, and its mass ratio is 1:1:1, the antistatic agent is a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a polypropylene composite material for an automobile internal ornament, a preparation method thereof and an automobile internal ornament. The polypropylene composite material for the automobile internal ornament comprises 40-60 parts by weight of polypropylene resin, 0-30 parts by weight of filler, 1-5 parts by weight of compatibilizer, 5-15 parts by weight of toughening agent, 1-5 parts by weight of scratch-resistant agent, 1-5 parts by weight of odor adsorption agent, 5-15 parts by weight of anti-static agent, 0.1-0.5 part by weight of antioxidant and 0.3-1 part by weight of lubricating agent. Therefore, the polypropylene composite material which has the characteristics of low odor, scratch-resistant surface, low surface resistivity and excellent mechanical properties and is used for the automobile internal ornament can be obtained.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polypropylene composite material used for automobile interior decoration, a preparation method thereof and an interior decoration part. Background technique [0002] Polypropylene (PP) is one of the five general-purpose plastics. Due to its low specific gravity, good performance, easy processing and low price, it is widely used in automotive interior and exterior parts. However, due to the low hardness of polypropylene raw materials, it is easy to be scratched during use as an automotive interior part, and the surface of the part is white, which affects the appearance. With the continuous enhancement of environmental protection and health awareness, the requirements for air quality in the car Also keep improving. Therefore, the development and use of polypropylene materials that meet the requirements of low odor, scratch resistance and antistatic at the same time has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/16C08L23/08C08L83/04C08K13/02C08K3/34C08K3/36C08K5/098
Inventor 安林林吕建国姜振春
Owner GREAT WALL MOTOR CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap