Hydrophilic magnetic mesoporous microsphere and production method and application thereof

A magnetic and mesoporous technology, used in the preparation of microspheres, the preparation of peptides, magnetic materials, etc., to achieve good use value and application prospects, good magnetic field sensitivity, and strong specificity.

Inactive Publication Date: 2013-08-28
FUZHOU UNIV
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Hydrophilic magnetic mesoporous composites have not been reported as adsorbents for glycosylated peptides

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophilic magnetic mesoporous microsphere and production method and application thereof
  • Hydrophilic magnetic mesoporous microsphere and production method and application thereof
  • Hydrophilic magnetic mesoporous microsphere and production method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Example 1 Synthesis of hydrophilic magnetic mesoporous microspheres

[0031] Hydrothermal synthesis of magnetic microspheres: using 6.8 grams of FeCl 3 ·6H 2 O, add 12.0 g of sodium acetate as a dispersant, mix well in 200 mL of ethylene glycol solution, add 2.0 g of trisodium citrate dihydrate, and then transfer the solution into a closed heating vessel, and perform solvothermal reaction at 200°C , The heating time is 7 h, and the ferroferromagnetic microspheres are obtained. After the product was washed, it was vacuum dried at 60°C for 12 h.

[0032] Preparation of chloropropyl modified magnetic mesoporous microspheres: take 300 mg Fe 3 O 4 The magnetic microspheres were ultrasonically dispersed in 580 mL secondary water, and 1.0 g CTAB and 24 mg NaOH were added. In a 60°C water bath, the ethanol solution of the silane precursor (8 mL, 4 mL and 8 mL of tetraethoxysilane, chloropropyltriethoxysilane and ethanol respectively) was added dropwise with mechanical stirring. C...

Embodiment 2

[0037] Example 2 Performance Test

[0038] figure 1 In the scanning electron micrograph of the hydrophilic magnetic mesoporous microspheres synthesized in Example 1, it can be seen that the particle size of the ferroferric oxide nanoparticles is about 200 nm, and the dispersion is good.

[0039] figure 2 It is a transmission electron micrograph of the hydrophilic magnetic mesoporous microspheres obtained in Example 1. It can be seen that it has an obvious core-shell structure and the shell has a vertical ordered mesoporous structure, indicating that the magnetic nanoparticles have undergone sol-gel reaction. Successfully coated with mesoporous SiO 2 shell.

[0040] image 3 The magnetic mesoporous microspheres containing CTAB (a), chloropropyl-modified magnetic mesoporous microspheres (b), azide magnetic mesoporous microspheres (c) and hydrophilic magnetic mesoporous microspheres synthesized in Example 1 Infrared spectrum of microsphere (d). In (a) there is an obvious vibration a...

Embodiment 3

[0042] Example 3 Hydrophilic magnetic mesoporous microspheres are used for the enrichment of glycosylated peptides

[0043] Take 20 μL of the peptide mixture of 2 μg / μL horseradish peroxidase (HRP) trypsin digestion and prepare 1 mL of 40 ng / μL HRP solution (80% acetonitrile and 0.2% (v / v) ) An aqueous solution of acetic acid), add 0.1 mg of hydrophilic magnetic mesoporous microspheres, and shake at room temperature for 30 minutes; separate the supernatant and the microspheres enriched with glycosylated peptides under the action of a magnetic field. Wash the material with 80% acetonitrile aqueous solution (containing 0.2% (v / v) acetic acid), and then use 40 μL 20% acetonitrile aqueous solution (containing 0.2% (v / v) acetic acid) to elute the enriched glycosylated peptides. Take 10 μL of eluate and use ESI-Q-TOF mass spectrometry to detect. As shown in Figure 5, the number of glycosylated peptides detected after enrichment increased from 4 to 10 (corresponding to 5 and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of organic-inorganic composite materials and analysis, particularly relates to a hydrophilic magnetic mesoporous microsphere and a production method and application thereof. The production method includes (1) taking a surfactant as a structure-directing agent through sol-gel reaction, and coating a layer of functionalized silica / surfactant composite materials with ordered mesostructure on surfaces of magnetic layer inorganic nanoparticles; (2) removing the surfactant through solvent extraction, and acquiring surface-functionalized magnetic mesoporous microspheres; (3) acting with sodium azide to acquire azide magnetic mesoporous microspheres; and (4) utilizing click chemistry reaction to allow alkynyl saccharides to act with the azide magnetic mesoporous microspheres, and acquiring hydrophilic magnetic mesoporous microspheres. The hydrophilic magnetic mesoporous microspheres have the advantages of good magnetic induction, strong specificity and the like, and have good using value and application prospect in the field of proteomics and the like.

Description

technical field [0001] The invention belongs to the technical field of organic-inorganic composite materials and analysis, and in particular relates to a hydrophilic magnetic mesoporous microsphere and its preparation method and application. Background technique [0002] Post-translational protein modification is a hot topic in proteomics research. Glycosylation modification is the most common protein post-translational modification, which plays a key role in biological development, cell division, inflammatory response and important diseases. Due to its relatively low abundance (2-4%), and there may be sugar chains of various structures at each glycosylation site, it is difficult to study. Therefore, enriching glycosylated peptides has become a crucial step in glycosylation research. [0003] The existing enrichment methods for glycosylated peptides mainly include the following: lectin affinity chromatography, hydrophilic chromatography, hydrazine reaction method and boric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01F1/00H01F1/42B01J13/02C07K1/14
Inventor 林子俺郑江南张兰杨黄浩陈国南
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com