Preparation method and application of high-cohesiveness dealcoholized silicone rubber
A high-adhesive, silicone rubber technology, applied in the direction of adhesive types, chemical instruments and methods, non-polymer adhesive additives, etc., can solve the problems of poor bonding performance, reduced sealing performance, and easy Breathable and moisture-permeable and other issues, to achieve good market prospects, improve adhesion, and good shockproof performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] (1) Mix 60 parts of hydroxyl silicone oil with a viscosity of 20000mpa s, 20 parts of dimethyl silicone oil with a viscosity of 5000mpa s and 10 parts of silicone modified polyurethane (CH 3 ) 3 SiO[-NH-CO-] 8 OSi(CH 3 ) 3 After mixing evenly, add 20 parts of nano-calcium carbonate, stir evenly with a kneader and remove moisture in a vacuum for 1 hour to obtain a mixture;
[0034] (2) Grind the mixture obtained in (1) for 3-4 times with a three-roller machine and wake up for 4 hours, then add 4 parts of crosslinking agent methyltrimethoxysilane and 2 parts of curing accelerator tetramethyl titanate and curing catalyst stannous octoate 0.02 parts, then put it back into the kneader to continue stirring and vacuumize to remove moisture for 0.1h, then move to the press, press out and fill, and obtain a high-adhesive dealcoholized silicon rubber1.
[0035] The product is cured at room temperature for 24 hours, the hardness is 30 shore A, and the tensile strength is 2.8M...
Embodiment 2
[0037] (1) Mix 100 parts of hydroxy silicone oil with a viscosity of 2000mpa s, 50 parts of hydroxy silicone oil with a viscosity of 200000mpa s, 10 parts of dimethyl silicone oil with a viscosity of 500mpa s and 5 parts of silicone modified polyurethane (CH 3 CH 2 ) 3 SiO[-NH-CO-] 1000 OSi(CH 2 CH 3 ) 3 After mixing evenly, add 10 parts of nano-calcium carbonate, stir evenly with a kneader and remove moisture in a vacuum for 12 hours;
[0038] (2) Grind the mixture obtained in (1) for 3-4 times with a three-roller machine and wake it up for 48 hours, then add 8 parts of crosslinking agent methyltriethoxysilane, 8 parts of curing accelerator tetraethyl titanate part and 3.0 parts of stannous octoate as a curing catalyst, put it back into the kneader to continue stirring and vacuumize to remove moisture for 0.5 h, then move to the press, press out and fill, and obtain a high-adhesive dealcoholization type Silicone rubber2.
[0039] The product is cured at room temperatu...
Embodiment 3
[0041] (1) Mix 100 parts of hydroxy silicone oil with a viscosity of 20000mpa s, 50 parts of hydroxy silicone oil with a viscosity of 80000mpa s, 20 parts of dimethyl silicone oil with a viscosity of 500mpa s and 25 parts of silicone modified polyurethane (CH 3 CH 2 CH 2 ) 3 SiO[-NH-CO-] 100 OSi(CH2 CH 2 CH 3 ) 3 After mixing evenly, add 20 parts of precipitated white carbon black, stir evenly with a kneader and remove moisture in a vacuum for 7 hours;
[0042] (2) Grind the mixture obtained in (1) for 3-4 times with a three-roller machine and wake it up for 24 hours, then add 6 parts of crosslinking agent methyl tripropropoxysilane, curing accelerator tetrapropyl titanate 2 part and 1.0 part of curing catalyst dibutyltin dilaurate, put it back into the kneader to continue stirring and vacuumize to remove moisture for 2 hours, then move to the press, press out and fill, and obtain a highly cohesive release Alcohol type silicone rubber3.
[0043] The product is cured ...
PUM
Property | Measurement | Unit |
---|---|---|
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap