A kind of styrene-acrylic emulsion for making artificial stone, preparation method and artificial stone made thereof

A technology of artificial stone and emulsion, which is applied in the field of new materials and polymer chemistry, can solve the problems of large shrinkage, poor heat resistance, and low flame retardancy, and achieve the effects of small shrinkage, high weather resistance, and easy processing and shaping

Active Publication Date: 2014-10-08
广东海顺新材料科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the problems of a large amount of harmful VOC (volatile organic compounds) in artificial stone, and the product has a large shrinkage rate, low flame retardancy, and poor heat resistance, the present invention provides a styrene-acrylate emulsion for artificial stone. At the same time, the preparation method of the emulsion and the artificial stone produced by the emulsion are provided. The artificial stone has excellent chemical corrosion resistance, pollution resistance, heat resistance, water resistance and good hardness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of styrene-acrylic emulsion for making artificial stone, preparation method and artificial stone made thereof
  • A kind of styrene-acrylic emulsion for making artificial stone, preparation method and artificial stone made thereof
  • A kind of styrene-acrylic emulsion for making artificial stone, preparation method and artificial stone made thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Prepare the styrene-acrylate emulsion for the manufacture of artificial stone with the following formula:

[0051] Mixed monomer 52%

[0052] Emulsifier 0.5%

[0053] Initiator 0.09%

[0054] Oxidizing agent 0.05%

[0055] Reducing agent 0.05%

[0056] water balance

[0057] The mixed monomer is made up of 90 parts of styrene, 20 parts of ethyl acrylate, 40 parts of butyl acrylate, 100 parts of isooctyl acrylate, 1 part of acrylic acid, and 2 parts of acrylamide; the emulsifier is a mass ratio of 1: 1 sodium lauryl sulfate and dodecylbenzenesulfonic acid; the initiator is ammonium persulfate and sodium persulfate with a mass ratio of 1:0.5; the oxidizing agent is butyl hydroperoxide, and the reducing agent is a mass ratio of 1 : 1 sodium sulfite and sodium dithionite.

[0058] Specific steps are as follows:

[0059] ⑴ Mix the emulsifier, one-third of the water and the mixed monomer evenly according to the formula to obtain a uniform mixed solution I;

[0060] (2...

Embodiment 2

[0083] Prepare the styrene-acrylate emulsion for the manufacture of artificial stone with the following formula:

[0084] Mixed monomer 53%

[0085] Emulsifier 0.5%

[0086] Initiator 0.1%

[0087] Oxidizing agent 0.1%

[0088] Reducing agent 0.1%

[0089] water balance

[0090] The mixed monomer is composed of 95 parts of styrene, 25 parts of ethyl acrylate, 35 parts of butyl acrylate, 97 parts of isooctyl acrylate, and 1 part of acrylic acid; the emulsifier is dodecylbenzenesulfonic acid, and the initiator It is sodium persulfate, the oxidizing agent is tert-butyl hydroperoxide, and the reducing agent is sodium sulfite.

[0091] Specific steps are as follows:

[0092] ⑴ Mix the emulsifier, one-third of the water and the mixed monomer evenly according to the formula to obtain a uniform mixed solution I;

[0093] (2) Heat up the remaining two-thirds of the water to 80°C, add an initiator equivalent to 4% of the mass of the mixed solution I, keep it warm for 30 minutes, ...

Embodiment 3

[0115] Prepare the styrene-acrylate emulsion for the manufacture of artificial stone with the following formula:

[0116] Mixed monomer 54%

[0117] Emulsifier 0.6%

[0118] Initiator 0.12%

[0119] Oxidizing agent 0.1%

[0120] Reducing agent 0.1%

[0121] water balance

[0122] The mixed monomer is composed of 100 parts of styrene, 30 parts of ethyl acrylate, 30 parts of butyl acrylate and 95 parts of isooctyl acrylate; the emulsifier is dodecylbenzenesulfonic acid, and the initiator is sodium persulfate , the oxidizing agent is tert-butyl hydroperoxide, and the reducing agent is sodium sulfite. The emulsifier is dodecylbenzenesulfonic acid, the initiator is ammonium persulfate, the oxidizing agent is tert-butyl hydroperoxide, and the reducing agent is sodium dithionite.

[0123] Specific steps are as follows:

[0124] ⑴ Mix the emulsifier, one-third of the water and the mixed monomer evenly according to the formula to obtain a uniform mixed solution I;

[0125](2) H...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

In order to solve the problems of a large amount of harmful VOC in artificial stone, and the product has a large shrinkage rate, low flame retardancy, poor corrosion resistance, and low hardness, the present invention provides a styrene-acrylate emulsion for artificial stone. At the same time, The preparation method of the emulsion and the artificial stone produced by the emulsion are provided. The artificial stone has excellent chemical corrosion resistance, pollution resistance, heat resistance, water resistance and good hardness.

Description

technical field [0001] The invention relates to a styrene acrylate emulsion used for manufacturing artificial stones, a preparation method thereof and the prepared water-based artificial stone, belonging to the fields of polymer chemistry and new materials. Background technique [0002] Artificial stone is a new product that first appeared in the United States in the 1930s. There are many ways to manufacture artificial stone, and the main raw materials are adhesives and fillers. Adhesive is the most important factor to determine the quality of artificial stone. From the perspective of adhesives, artificial boulders can be divided into two categories: inorganic artificial stones and organic polymer artificial stones. [0003] Among them, organic artificial stone has been sought after by people because of its superior performance. The current artificial stone research work is progressing rapidly. Some problems it faces, such as the aging problem of organic polymer artifici...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F212/08C08F220/18C08F2/26C08F4/40C04B26/06
Inventor 付少辉易承志
Owner 广东海顺新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com