A kind of stainless steel material and its manufacturing method
A technology of steel grade and charge, which is applied in the field of stainless steel materials and its manufacturing, can solve the problems that the proportion of nitrogen added in stainless steel does not meet the design requirements, and the difficulty of smelting nitrogen-containing stainless steel.
Active Publication Date: 2016-06-08
CENT IRON & STEEL RES INST +1
View PDF8 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0022] The second technical problem to be solved by the present invention is to provide a method for smelting stainless steel in a pressurized induction furnace in view of the defects in the prior art that the smelting of nitrogen-containing stainless steel is difficult and the proportion of nitrogen added in stainless steel cannot meet the design requirements
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0141] The stainless steel material is a Cr-Mn-N austenitic stainless steel in which nitrogen is substituted for nickel, and the stainless steel material comprises the following components in weight percentage:
[0142] Cr: 18%; Mn: 14%; N: 0.4%; C: 0.1%.
Embodiment 2
[0144] The stainless steel material is a Cr-Mn-N austenitic stainless steel in which nitrogen is substituted for nickel, and the stainless steel material comprises the following components in weight percentage:
[0145] Cr: 22%; Mn: 17%; N: 0.75%; C: 0.12%.
Embodiment 3
[0147] The stainless steel material is a Cr-Mn-N austenitic stainless steel in which nitrogen is substituted for nickel, and the stainless steel material comprises the following components in weight percentage:
[0148] Cr: 18%; Mn: 14%; N: 0.4%; C: 0.1%; S: 0.02%; P: 0.025%; Si: 0.8%; Cu: 0.2%; Al: 0.01%; and Fe.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
| Property | Measurement | Unit |
|---|---|---|
| flexural strength | aaaaa | aaaaa |
| directional tensile yield strength | aaaaa | aaaaa |
| strength | aaaaa | aaaaa |
Login to view more
Abstract
Disclosed is a stainless steel material and a manufacturing method therefor. The stainless steel material is a Cr-Mn-N austenitic stainless steel where nickel is replaced by nitrogen. The manufacturing method comprises: a smelting method, a blank stamping method and a machining method. The smelting method mainly consists in the smelting of high nitrogen steel by means of two methods of a solid nitrogen-containing material and gaseous nitrogen for alloying and increasing a nitrogen content. The blank stamping method mainly consists in repeated cycles of blank stamping, thermal treatment, solid solution treatment; the control of heat-preserving temperature and duration, and the selection of moulds mainly takes the hardness and impact toughness values into consideration. The machining mainly comprises the control of the suitable processing parameters for milling and turning operations. The smelting method for the stainless steel material is suitable for the batchwise smelting of high nitrogen steel having a nitrogen content of 0.4 wt%-0.75 wt%; the blank stamping method inhibits the cold-work hardening phenomenon during the processing of high nitrogen steels, and facilitates the stamping of the blank; and the machining method overcomes the problem of high processing difficulty due to the great hardness of high nitrogen steel.
Description
technical field [0001] The invention relates to stainless steel and its smelting and processing methods, more specifically, to a stainless steel material and its manufacturing method. Background technique [0002] 1. Significance of using high nitrogen steel [0003] Stainless steel is a steel that is not easy to rust. The stainless steel and corrosion resistance of stainless steel are due to the chromium-rich oxide film (passive film) on its surface. Because stainless steel has a series of characteristics such as excellent corrosion resistance, formability, compatibility, and strength and toughness in a wide temperature range, it has been widely used in heavy industry, light industry, daily necessities industry, and architectural decoration industries for its excellent characteristics. Applications are not only functional materials, but also modern structural materials. Stainless steel has the advantages of long life cycle and low cost. It can be 100% recycled and reused....
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/38C21C5/52C21D8/00B21D22/02B23P15/00B23C3/00
CPCC21C7/0685C21D6/002C21D8/00C22C38/001C22C38/02C22C38/06C22C38/20C22C38/32C22C38/38
Inventor 郎宇平李北邢长军鲍贤勇孙绍华翁建寅姚春发唐海元陈海涛曹呈祥吴林宁小智屈华鹏
Owner CENT IRON & STEEL RES INST
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap