A glass frame and its preparation method and hot pressing method using the glass frame

A hot pressing method and glass edge technology, which are applied in glass manufacturing equipment, glass forming, glass remolding and other directions, can solve the problems of uneven thickness of frame boxes, glass waste, broken glass rods, etc. The effect of reducing glass cost and simple operation

Active Publication Date: 2015-11-04
江苏骏成电子科技股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the information display processing technology, the glass frame filling material used is a cylindrical glass rod (the length of the glass rod is 5um-7um), two pieces of glass with printed graphics are bonded together, and then hot pressing operation is carried out. During the hot pressing process, the frame is heated and extruded, which will cause the cylindrical glass rod to break, resulting in uneven thickness of the frame box, resulting in waste of glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A glass frame, comprising an upper glass substrate and a lower glass substrate, between the upper glass substrate and the lower glass substrate are uniformly mixed frame raw materials and silicon balls, the mass content of the frame raw materials is 98.5%, and the mass content of the silicon balls is 1.5% %.

[0021] The frame material above is SS950 manufactured by Shantou Sinengda Electronics Co., Ltd., and the silicon ball is Si-7.0 manufactured by Zhenjiang Aibang Electronics Co., Ltd.

[0022] The preparation method of the above-mentioned glass frame comprises the following steps:

[0023] 1) Thaw the frame raw materials at room temperature for 4 hours, and configure the frame raw materials and silicon balls according to the ratio;

[0024] 2) After configuration, manually stir for 4 minutes to obtain the mixed material;

[0025] 3) Put the obtained mixed material on the mixer and stir for 25 minutes to make it fully mixed to obtain the mixed mate...

Embodiment 2

[0034] A glass frame, comprising an upper glass substrate and a lower glass substrate, between the upper glass substrate and the lower glass substrate are uniformly mixed frame raw materials and silicon balls, the mass content of the frame raw materials is 99%, and the mass content of the silicon balls is 1 %.

[0035] The frame material above is SS950 manufactured by Shantou Sinengda Electronics Co., Ltd., and the silicon ball is Si-7.0 manufactured by Zhenjiang Aibang Electronics Co., Ltd.

[0036] The preparation method of the above-mentioned glass frame comprises the following steps:

[0037] 1) Thaw the frame raw materials at room temperature for 3 hours, and configure the frame raw materials and silicon balls according to the ratio;

[0038] 2) After configuration, manually stir for 3 minutes to obtain the mixed material;

[0039] 3) Put the obtained mixed material on the mixer and stir for 25 minutes to make it fully mixed to obtain the mixed material;...

Embodiment 3

[0048] A glass frame, comprising an upper glass substrate and a lower glass substrate, between the upper glass substrate and the lower glass substrate are uniformly mixed frame raw materials and silicon balls, the mass content of the frame raw materials is 98%, and the mass content of the silicon balls is 2 %.

[0049] The frame material above is SS950 manufactured by Shantou Sinengda Electronics Co., Ltd., and the silicon ball is Si-7.0 manufactured by Zhenjiang Aibang Electronics Co., Ltd.

[0050] The preparation method of the above-mentioned glass frame comprises the following steps:

[0051] 1) Thaw the frame raw materials at room temperature for 5 hours, and configure the frame raw materials and silicon balls according to the ratio;

[0052] 2) After configuration, manually stir for 5 minutes to obtain the mixed material;

[0053] 3) Put the obtained mixed material on the mixer and stir for 30 minutes to make it fully mixed to obtain the mixed mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass frame. The glass frame comprises an upper glass substrate and a lower glass substrate, a uniformly mixed mixture is arranged between the upper glass substrate and the lower glass substrate, and the mixture comprises 98-99mass% of a frame raw material and 1-2mass% of a silicon sphere. The glass frame has the advantages of simple operation, low cost, improvement of the adverse conditions of frames in the hot pressing process, and glass cost reduction.

Description

technical field [0001] The invention relates to the technical field of information display screens, in particular to a glass frame, a preparation method thereof, and a hot pressing method utilizing the glass frame. Background technique [0002] At present, in the information display processing technology, the glass frame filling material used is a cylindrical glass rod (the length of the glass rod is 5um-7um), two pieces of glass with printed graphics are bonded together, and then hot pressing operation is carried out. During the hot pressing process, the heat and extrusion of the frame will cause the cylindrical glass rod to break, resulting in uneven thickness of the frame box, resulting in waste of glass. Contents of the invention [0003] Purpose of the invention: The technical problem to be solved by the present invention is to provide a glass frame and its preparation method as well as a hot pressing method using the glass frame. [0004] Technical solut...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B23/24
Inventor 张小光蒋风华
Owner 江苏骏成电子科技股份有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com