Impervious tunnel fireproof paint

A fireproof coating and impermeability technology, applied in the field of chemical coatings, can solve the problems of short fire protection time, long-term coating peeling, complicated construction, etc., and achieve the effect of easy construction operation, making up for easy water seepage, and good fire performance.

Inactive Publication Date: 2014-03-19
上海世范乐建新材料有限公司
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the construction industry and other related industries, various types of fire-resistant coatings have emerged. Although they can achieve fire protection, the products have disadvantages such as complex construction, long-term coating peeling, and short fire protection time, which are related to people's life safety and fire safety. If you can't be a little sloppy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] An anti-seepage type tunnel fireproof coating is prepared by mixing the following raw materials according to the weight ratio: 80-88 parts of refractory cement, 30-34 parts of white special blue cement, 20-30 parts of styrene-acrylic emulsion, 30-35 parts of bisphenol ring Oxidized resin emulsion, 6-8 parts of aluminum hydroxide, 10-11 parts of magnesium hydroxide, 10-14 parts of starch, 6-8 parts of ammonium dichromate, 6-8 parts of light calcium carbonate, 10-16 parts of ethyl alcohol Base cellulose, 5-9 parts of glass fiber, 14-18 parts of fly ash hollow floating beads, 3-5 parts of diatomaceous earth, 6-8 parts of vermiculite, 6-8 parts of mica, 6-8 parts of tripolyphosphoric acid Aluminum, 8-10 parts clay, 5-7 parts pentaerythritol.

Embodiment 2

[0012] An anti-seepage type tunnel fireproof coating is prepared by mixing the following raw materials according to the weight ratio: 80-88 parts of refractory cement, 30-34 parts of white special blue cement, 20-30 parts of styrene-acrylic emulsion, 30-35 parts of bisphenol ring Oxidized resin emulsion, 6-8 parts of aluminum hydroxide, 10-11 parts of magnesium hydroxide, 10-14 parts of starch, 6-8 parts of ammonium dichromate, 6-8 parts of light calcium carbonate, 10-16 parts of ethyl alcohol Base cellulose, 5-9 parts of glass fiber, 14-18 parts of fly ash hollow floating beads, 3-5 parts of diatomaceous earth, 6-8 parts of vermiculite, 6-8 parts of mica, 6-8 parts of tripolyphosphoric acid Aluminum, 8-10 parts clay, 5-7 parts pentaerythritol and 4-8 parts ammonium borate.

Embodiment 3

[0014] The formulations of the above examples are all prepared and constructed according to the following methods: (1) Ingredients, mix the paint and water at a ratio of about 0.7, first add a small amount of water while stirring while adding the paint, and add water in an appropriate amount, and generally stir for 20 minutes to form a thick paste Slurry (2) construction, use a sprayer to spray from the waist of the tunnel from bottom to top, each spraying is 3-7mm thick, and the construction interval is based on the fact that the last paint is basically dry, and so on, until the design thickness is sprayed, After the last spraying, if it needs to be smoothed, use the method of wiping and smoothing.

[0015] The finished products prepared in the above examples can all reach the following technical indicators after testing: 1. Sieve rate ≤ 1.0%; 2. Dry density ≤ 580kg / m 3 ;3. Water resistance: h≥24, the coating will not crack, peel off or fall off; 4. Alkali resistance: h≥24, t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Dry densityaaaaaaaaaa
Bond strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Login to View More

Abstract

A disclosed impervious tunnel fireproof paint is prepared by stirring the following raw materials in parts by weight: 80-88 parts of refractory cement, 30-34 parts of portland cement, 20-30 parts of styrene acrylic emulsion, 30-35 parts of bisphenol epoxy resin emulsion, 6-8 parts of aluminium hydroxide, 10-11 parts of magnesium hydroxide, 10-14 parts of starch, 6-8 parts of ammonium bichromate, 6-8 parts of light calcium carbonate, 10-16 parts of ethyl cellulose, 5-9 parts of glass fibre, 14-18 parts of coal flying ash cenosphere, 3-5 parts of diatomite, 6-8 parts of vermiculite, 6-8 parts of mica, 6-8 parts of aluminum tripolyphosphate, 8-10 parts of potter's clay and 5-7 parts of pentaerythritol. The product provided by the invention not only is good in fireproof performance, but also has water seepage resistant performance, and thus makes up the disadvantage that the conventional fireproof paints are easily subjected to water seepage; and the fireproof paint is strong in caking property, easy to construct and operate and excellent in comprehensive performance, and is suitable for the fields such as traffic tunnels, people's air defence buildings, underground buildings and the like.

Description

technical field [0001] The invention relates to an anti-seepage type tunnel fireproof coating, which belongs to the technical field of chemical coatings. technical background [0002] In architecture, the cross-sectional area exceeds 30m 2 The underground artificially constructed passage is defined as a tunnel. Tunnels not only undertake the task of transportation, but also function as channels for optical cables, cables, and even oil and water pipelines. Although the reinforced concrete components used as the main building in the tunnel are non-combustible materials, the tunnel fire has the characteristics of a rapid rise in ambient temperature after combustion, a long duration, a large fire range, and difficulties in fire fighting and entry. In a short period of time after the fire broke out, the local temperature of the fire site in the tunnel will rise rapidly to 1000°C. As the temperature continues to rise, the bound water in the concrete will turn into steam and expa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B24/28
Inventor 石小强
Owner 上海世范乐建新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com