A preparation method of a dual-functional environmental material for humidity adjustment and purification

A dual-function, environmental technology, applied in the field of environmental materials, can solve problems such as polluting the environment and wasting resources, and achieve the effects of large adsorption capacity, improved wet capacity, and good water absorption performance.

Active Publication Date: 2016-02-10
江苏华新高新技术创业有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Sericin has good hydrophilicity, but a large amount of high-concentration sericin wastewater has not been used in the past, which not only wastes resources but also pollutes the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: the preparation method of humidity-controlling and purifying dual-function environmental material of the present invention, it adopts following steps:

[0019] A) According to the number of parts by mass, take 100 parts of sericin solution with a concentration of 5-10% by weight, 1 part of β-cyclodextrin, add 0.1 part of transglutaminase solution with a concentration of 10% by weight, stir evenly, and Place at 20°C for 1 hour, then freeze-dry at minus 50°C, and pulverize evenly;

[0020] B) Take 0.2 parts of the product obtained in step A) in parts by mass, 5 parts of acrylic acid, 1 part of sodium methacrylate, 2 parts of sodium carboxymethylcellulose, 0.05 parts of potassium persulfate, 10 parts of water, at 40 °C , stirring and reacting for 0.5 hours;

[0021] C) Add 1 part of glutaraldehyde aqueous solution with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temperature of 55° C.;

[002...

Embodiment 2

[0023] Embodiment 2: the preparation method of humidity-controlling and purifying dual-function environmental material of the present invention, it adopts following steps:

[0024] A) According to the number of parts by mass, take 100 parts of sericin solution with a concentration of 5-10% by weight, 2 parts of β-cyclodextrin, add 1 part of transglutaminase solution with a concentration of 10% by weight, stir evenly, and Place at 20°C for 2 hours, then freeze-dry at minus 50°C, and pulverize evenly;

[0025] B) According to the number of parts by mass, take 0.6 parts of the product obtained in step A), 8 parts of acrylic acid, 1 part of sodium methacrylate, 3 parts of sodium carboxymethylcellulose, 0.1 part of potassium persulfate, 15 parts of water, at 45 ° C , stirring and reacting for 0.5 hours;

[0026] C) Add 3 parts of glutaraldehyde aqueous solution with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a tempe...

Embodiment 3

[0028] Embodiment 3: the preparation method of humidity-controlling and purifying dual-function environmental material of the present invention, it adopts following steps:

[0029] A) According to the number of parts by mass, take 100 parts of sericin solution with a concentration of 5-10% by weight, 3 parts of β-cyclodextrin, add 2 parts of transglutaminase solution with a concentration of 10% by weight, stir evenly, and Place at 30°C for 3 hours, then freeze-dry at minus 50°C and pulverize evenly;

[0030] B) According to the number of parts by mass, take 1 part of the product obtained in step A), 10 parts of acrylic acid, 2 parts of sodium methacrylate, 5 parts of sodium carboxymethylcellulose, 0.15 parts of potassium persulfate, 15 parts of water, at 50 ° C , stirring and reacting for 0.5 hours;

[0031] C) Add 5 parts of glutaraldehyde aqueous solution with a concentration of 5% by weight to the product of step B) in parts by mass, and stir and react for 1 hour at a temp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing a humidifying-purifying dual-function environmental material. The method comprises the following steps: (A) taking a sericin solution and beta-cyclodextrin in parts by mass, adding the components into a glutamine transaminase solution, uniformly stirring, standing for 1-3 hours under the condition of 20-30 DEG C, performing freeze drying under the condition of 50 DEG C below zero, and uniformly grinding; (2) taking the product obtained in the step (A), acrylic acid, sodium methacrylate, sodium carboxymethylcellulose, potassium peroxodisulfate and water, stirring and reacting for 0.5 hour at the temperature of 40-50 DEG C; (3) adding a glutaraldehyde aqueous solution into the product in the step (B) in parts by weight, stirring and reacting for 1 hour at the temperature of 55-75 DEG C; and (D) taking the products, activated carbon, a hydrophobic crystalline state silica molecular sieve, grinding and stirring uniformly, and obtaining the humidifying-purifying dual-function environmental material. The method has the beneficial effects that (1) the novel material is high in humidity response speed, high in moisture capacity and good in moisture absorption and desorption performance; (2) the material has the humidifying-purifying dual functions.

Description

technical field [0001] The invention relates to a preparation method of a dual-function environmental material for humidity adjustment and purification, and belongs to the technical field of environmental materials. Background technique [0002] Humidity-regulating materials are functional materials that can control water vapor adsorption according to changes in environmental humidity. When the humidity is high, the material can absorb water vapor in the environment; when the humidity is low, it can emit the water vapor absorbed by itself. Relative air humidity is an important parameter to measure the indoor environment. Appropriate humidity plays a very important role in human health and industrial and agricultural production. The annual average relative humidity in the humid areas of southern my country is 70% to 80%, sometimes as high as 95% to 100%, while the relative humidity in the dry period in the northern area is as low as 10%, so humidity adjustment is very necess...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L51/00C08K3/04C08K3/36C08J9/28C08F291/00C08F220/06C08F8/28
Inventor 冯道言
Owner 江苏华新高新技术创业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap