Unlock instant, AI-driven research and patent intelligence for your innovation.

A ceramic-like wall made of silicon-aluminum composite material and its preparation process

A silicon-aluminum composite material and imitation ceramic wall technology, which is applied in the field of building panels, can solve problems such as complex operation, long construction period, and complicated procedures, and achieve good effects, good waterproof performance, and good earthquake resistance

Active Publication Date: 2015-08-19
王东彬
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the exterior wall, which leads to complicated procedures, complicated operations, and long construction periods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A ceramic-like wall made of silicon-aluminum composite material and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: Preparation of imitation exterior wall ceramic tile wall:

[0033] A preparation process for an imitation exterior wall tile wall made of a silicon-aluminum composite material, comprising the following steps:

[0034] (1) Inject the imitation exterior wall tile pigment into the polymer blended fireproof modified material, silicon-aluminum clinker, and stearic acid, then dry and mix for 20 minutes at 150°; at the same time, put the coal gangue in a high-temperature furnace After being drawn into a fiber shape according to the standard, it is placed in the imitation exterior wall tile mold, and then the mixed material is filled into the imitation exterior wall tile mold, and integrated with the gangue fiber skeleton.

[0035] (2) Injection molding at a temperature of 150° to form a wall imitating exterior wall tiles;

[0036] (3) After the molding is completed, open the mold and take out the imitation exterior wall tile wall. When the wall is used as an ext...

Embodiment 2

[0040] Embodiment 2: preparation imitation pottery mosaic brick wall:

[0041] A preparation process for a ceramic-like mosaic brick wall made of a silicon-aluminum composite material, comprising the following steps:

[0042] (1) Inject the imitation ceramic mosaic tile pigment into the polymer blended fireproof modified material, silicon-aluminum clinker, and stearic acid, then dry and mix for 20 minutes at 150°; at the same time, put the coal gangue in a high-temperature furnace After being drawn into a fibrous shape according to the standard, it is placed in a mosaic imitation ceramic mosaic mold, and then the mixed material is filled into the mosaic imitation ceramic mosaic mould, which is integrated with the gangue fiber skeleton.

[0043] (2) Injection molding at a temperature of 150° to form a wall of imitation ceramic mosaic bricks;

[0044] (3) After the molding is completed, open the mold and take out the imitation ceramic mosaic brick wall. When the wall is used as...

Embodiment 3

[0048] Embodiment 3: prepare imitation floor brick wall;

[0049] A preparation process for a ground-like brick wall made of a silicon-aluminum composite material, comprising the following steps:

[0050] (1) Inject the imitation floor tile pigment into the polymer blended fireproof modified material, silicon-aluminum clinker, and stearic acid, then dry and mix for 20 minutes at 150°; at the same time, put the coal gangue in a high-temperature furnace After being drawn into a fibrous shape according to the standard, it is placed in the imitation floor brick mold, and then the mixed material is filled into the imitation floor brick mold to integrate with the coal gangue fiber skeleton.

[0051] (2) Injection molding at a temperature of 150° to form a brick-like wall;

[0052] (3) After the molding is completed, open the mold and take out the imitation floor brick wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an imitated ceramic wall made of a silicon-aluminum composite material and a preparation process of the imitated ceramic wall. The preparation process comprises the steps of firstly, injecting imitated ceramic pigment and the silicon-aluminum composite material into an imitated ceramic wall forming mold together; carrying out injection molding at 150 DEG C to form the imitated ceramic wall; opening the mold to take out the imitated ceramic wall after injection molding and spraying an ultraviolet-resistant material on the surface of the imitated ceramic wall, wherein the silicon-aluminum composite material is formed by a mixture of coal gangue fiber, fireproofing and modified polymer blended material, silicon-aluminum clinker and stearic acid, the imitated ceramic wall comprises a silicon-aluminum composite material base layer, an imitated ceramic layer and an ultraviolet-resistant layer sequentially from inside to outside. The wall is molded one time in the production line and is hardly influenced by change of environment temperature; special equipment is adopted for spraying the ultraviolet-resistant material, good ultraviolet radiation resisting effect is achieved; and the imitated ceramic wall has long service life, stable structure, high strength and good anti-seismic effect.

Description

technical field [0001] The invention relates to the field of building boards, in particular to a ceramic imitation wall made of silicon-aluminum composite material and a preparation process thereof. Background technique [0002] With the continuous development of building decoration, people have higher and higher requirements for decoration, especially in the selection of materials, which not only require reasonable price, economical and practical, but also elegant appearance and environmental protection requirements. [0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the outer wall, which leads to complicated procedures, complicated operations, and long c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04C2/288C04B28/06C04B18/12C04B24/26
CPCY02W30/93Y02W30/91
Inventor 程凤岐王东彬
Owner 王东彬