A brick-like wall made of silicon-aluminum composite material and its preparation process

A silicon-aluminum composite material and a preparation process technology, applied in the field of building boards, can solve the problems of complicated procedures, long construction period, complicated operation, etc., and achieve the effects of good earthquake resistance, good waterproof performance and good effect.

Active Publication Date: 2016-01-20
王东彬
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the exterior wall, which leads to complicated procedures, complicated operations, and long construction periods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A brick-like wall made of silicon-aluminum composite material and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: preparation imitation green brick wall:

[0033] A preparation process of an imitation blue brick wall made of a silicon-aluminum composite material, comprising the following steps:

[0034] (1) Inject the imitation blue brick pigment into the polymer blended fireproof modified material, silicon-aluminum clinker, and stearic acid, then dry and mix for 20 minutes at 150°; at the same time, put the coal gangue in a high-temperature furnace After being drawn into a fibrous shape according to the standard, it is placed in the imitation green brick mold, and then the mixed material is filled into the imitation green brick mold, and integrated with the coal gangue fiber skeleton.

[0035] (2) Injection molding at a temperature of 150° to form a brick-like wall;

[0036] (3) After forming, open the mold and take out the imitation blue brick wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as ...

Embodiment 2

[0040] Embodiment 2: prepare imitation red brick wall body:

[0041] A preparation process for imitating red brick walls made of silicon-aluminum composite materials, comprising the following steps:

[0042] (1) Inject the imitation red brick pigment into the polymer blended fireproof modified material, silicon-aluminum clinker and stearic acid, then dry and mix for 20 minutes at 150°; at the same time, put the coal gangue in the high-temperature furnace After being drawn into a fibrous shape according to the standard, it is placed in the imitation red brick mold, and then the mixed material is filled into the imitation red brick mold, and integrated with the coal gangue fiber skeleton.

[0043] (2) Injection molding at a temperature of 150° to form a red brick wall;

[0044] (3) After forming, open the mold and take out the imitation red brick wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor ...

Embodiment 3

[0048] Embodiment 3: prepare imitation old brick wall;

[0049] A preparation process for an imitation brick wall made of silicon-aluminum composite material, comprising the following steps:

[0050] (1) Inject the old-fashioned brick pigment into the polymer blended fireproof modified material, silicon-aluminum clinker, and stearic acid, then dry it at 150°, stir and mix it for 20 minutes; at the same time, put the coal gangue in a high-temperature furnace After being drawn into a fiber shape according to the standard, it is placed in the imitation brick mold, and then the mixed material is filled into the imitation brick mold, and it is integrated with the gangue fiber skeleton.

[0051] (2) Injection molding at a temperature of 150° to form an imitation brick wall;

[0052] (3) After forming, open the mold and take out the old-fashioned brick wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a faux brick wall body made of a silicon-aluminum composite material and a preparation process of the faux brick wall body. The process comprises the following steps of (1) collectively injecting faux brick pigment and the silicon-aluminum composite material into a faux brick wall body forming mold; (2) molding the mixture into a faux brick wall body under the temperature condition of 150 DEG C; (3) opening the mold to take out the faux brick wall body after the molding is completed, and spraying an anti-ultraviolet material onto the surface of the faux brick wall body, wherein the silicon-aluminum composite material is formed by mixing gangue fibers, high molecular co-blended fireproof modified material, silicon-aluminum clinker and stearic acid. The faux brick wall body comprises a silicon-aluminum composite material basic layer, a faux brick layer and an anti-ultraviolet layer, which are sequentially arranged from inside to outside. The faux brick wall body is molded in one step on the production line and slightly subjected to the variation of the ambient temperature; the anti-ultraviolet material is sprayed by adopting a profession device, so that the effect for resisting the radiation of the ultraviolet is good, the service life is long, the structure is stable, the strength is high, and the anti-seismic effect is good.

Description

technical field [0001] The invention relates to the field of building boards, in particular to an imitation brick wall made of silicon-aluminum composite material and a preparation process thereof. Background technique [0002] With the continuous development of building decoration, people have higher and higher requirements for decoration, especially in the selection of materials, which not only require reasonable price, economical and practical, but also elegant appearance and environmental protection requirements. [0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the outer wall, which leads to complicated procedures, complicated operations, and long co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04C2/288B32B33/00B32B13/04B32B13/02C04B28/06C04B24/26C04B14/38
Inventor 程凤岐王东彬
Owner 王东彬