A stone imitation wall made of silicon-aluminum composite material and its preparation process
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A silicon-aluminum composite material and preparation technology, applied in covering/lining, building, building structure, etc., can solve the problems of complicated procedures, long construction period, complicated operation, etc., and achieve good earthquake resistance, good waterproof performance, and effective Good results
Active Publication Date: 2016-04-06
王东彬
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the exterior wall, which leads to complicated procedures, complicated operations, and long construction periods
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0032] Embodiment 1: preparation imitation marble body of wall:
[0033] A preparation process for a marble-like wall made of a silicon-aluminum composite material, comprising the following steps:
[0034] (1) Inject the imitation marble pigment into the polymer blended fireproof modified material, silicon-aluminum clinker and stearic acid, then dry it at 150°, stir and mix it for 20 minutes; After the standard is drawn into a fiber shape, it is placed in a marble-like mold, and then the mixed material is filled into the marble-like mold to integrate with the gangue fiber skeleton.
[0035] (2) Injection molding at a temperature of 150° to form a marble-like wall;
[0036] (3) After molding, open the mold and take out the imitation marble wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor partition wall, it is not necessary to spray this material.
[0037] Among them, the silicon-aluminum compo...
Embodiment 2
[0040] Embodiment 2: preparation imitation granite body of wall;
[0041] A preparation process of a granite-like wall made of a silicon-aluminum composite material, comprising the following steps:
[0042] (1) Inject the imitation granite pigment into the polymer blended fireproof modified material, silicon-aluminum clinker, stearic acid, then dry at 150°, stir and mix for 20 minutes; The standard is drawn into a fiber shape and placed in a granite-like mold, and then the mixed material is filled into the granite-like mold to integrate with the gangue fiber skeleton.
[0043] (2) Injection molding at a temperature of 150° to form a granite-like wall;
[0044] (3) After molding, open the mold and take out the imitation granite wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor partition wall, this material does not need to be sprayed.
[0045]Among them, the silicon-aluminum composite material ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
length
aaaaa
aaaaa
aspect ratio
aaaaa
aaaaa
Login to View More
Abstract
The invention relates to a faux stone wall made of silicon and aluminum composited materials and a production method thereof. The production method of the faux stone wall made of the silicon and aluminum composited materials comprises steps of (1), pouring faux stone pigment and the silicon and aluminum composited materials to a forming mold of the faux stone wall; (2) forming into the faux stone wall through injection molding under the condition with the temperature to be in 150 DEG C; (3) opening the mold and taking out the faux stone wall after the forming is finished and spraying ultraviolet resistant materials on the surface of the faux stone wall. The silicon and aluminum composited materials is formed by coal gangue fibers, macromolecule blending fireproof modified materials, silicon and aluminum clinker and stearic acid through mixing. The faux stone wall comprises a silicon and aluminum composited material base layer, a faux stone layer and an ultraviolet resistant layer, wherein the aluminum composited material base layer, the faux stone layer and the ultraviolet resistant layer are sequentially arranged from interior to exterior. The faux stone wall has the advantages of being small in environmental temperature variation change due to the fact the wall is formed in production lines in one time; being good in ultraviolet radiation resistant effect due to the fact that the ultraviolet resistant materials are sprayed through a special device; being long in service life, stable in structure, high in intensity and good in quake proof effect.
Description
technical field [0001] The invention relates to the field of building boards, in particular to a stone imitation wall made of a silicon-aluminum composite material and a preparation process thereof. Background technique [0002] With the continuous development of building decoration, people have higher and higher requirements for decoration, especially in the selection of materials, which not only require reasonable price, economical and practical, but also elegant appearance and environmental protection requirements. [0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the outer wall, which leads to complicated procedures, complicated operations, and long c...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More