Unlock instant, AI-driven research and patent intelligence for your innovation.

A wood-like wall made of silicon-aluminum composite material and its preparation process

A silicon-aluminum composite material and technology of preparation process, applied in covering/lining, construction, building structure, etc., can solve the problems of long construction period, complicated operation, complicated procedures, etc., and achieve good waterproof performance, good effect, and seismic effect. Good results

Active Publication Date: 2016-01-20
王东彬
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the exterior wall, which leads to complicated procedures, complicated operations, and long construction periods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A wood-like wall made of silicon-aluminum composite material and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Embodiment 1: preparation imitation ebony wall:

[0033] A preparation process for an imitation ebony wall made of a silicon-aluminum composite material, comprising the following steps:

[0034] (1) Inject the imitation ebony pigment into the polymer blended fireproof modified material, silicon-aluminum clinker and stearic acid, and then dry it at 150° and mix it for 20 minutes; After being drawn into a fiber shape according to the standard, it is placed in an imitation ebony mould, and then the mixed material is filled into the imitation ebony mould, which is integrated with the gangue fiber skeleton.

[0035] (2) Injection molding at a temperature of 150° to form an imitation ebony wall;

[0036] (3) After molding, open the mold and take out the imitation ebony wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor partition wall, it is not necessary to spray this material.

[0037] Among ...

Embodiment 2

[0040] Embodiment 2: preparation imitation ash wall:

[0041] A kind of preparation technology of the imitation ash wall made of silicon-aluminum composite material, comprises the following steps:

[0042] (1) Inject the imitation ash pigment into the polymer blended fire-proof modified material, silicon-aluminum clinker, and stearic acid, and then dry it at 150° and mix it for 20 minutes; at the same time, put the coal gangue in the high-temperature furnace After being drawn into a fibrous form according to the standard, it is placed in the imitation ash mold, and then the mixed material is filled into the imitation ash mold, and integrated with the coal gangue fiber skeleton.

[0043] (2) Injection molding at a temperature of 150°C to form an imitation ash wall;

[0044] (3) After forming, open the mold and take out the imitation ash wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor partition...

Embodiment 3

[0048] Embodiment 3: prepare imitation pine wall;

[0049] A preparation process for imitation pine wall made of silicon-aluminum composite material, comprising the following steps:

[0050] (1) Inject the imitation pine wood pigment into the polymer blended fireproof modified material, silicon-aluminum clinker and stearic acid, then dry and mix for 20 minutes at 150°; After the standard is drawn into a fibrous shape, it is placed in a pine-like mold, and then the mixed material is filled into the pine-like mold to integrate with the gangue fiber skeleton.

[0051] (2) Injection molding at a temperature of 150° to form a pine-like wall;

[0052] (3) After molding, open the mold and take out the imitation pine wall. When the wall is used as an external wall, the surface is sprayed with anti-ultraviolet material. When it is used as an indoor partition wall, it does not need to be sprayed with this material.

[0053] Among them, the silicon-aluminum composite material in Exampl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a faux wood grain wall made of silicon and aluminum composited materials and a production method thereof. The production method of the faux wood grain wall made of the silicon and aluminum composited materials comprises steps of (1), pouring faux wood pigment and the silicon and aluminum composited materials to a forming mold of the faux wood grain wall; (2) forming into the faux wood grain wall through injection molding under the condition with the temperature to be in 150 DEG C; (3) opening the mold and taking out the faux wood grain wall after the forming is finished and spraying ultraviolet resistant materials on the surface of the faux wood grain wall. The silicon and aluminum composited materials is formed by coal gangue fibers, macromolecule blending fireproof modified materials, silicon and aluminum clinker and stearic acid through mixing. The faux wood grain wall comprises a silicon and aluminum composited material base layer, a faux wood grain layer and an ultraviolet resistant layer, wherein the aluminum composited material base layer, the faux wood grain layer and the ultraviolet resistant layer are sequentially arranged from interior to exterior. The faux wood grain wall has the advantages of being small in environmental temperature variation change due to the fact the wall is formed in production lines in one time; being good in ultraviolet radiation resistant effect due to the fact that the ultraviolet resistant materials are sprayed through a special device; being long in service life, stable in structure, high in intensity and good in quake proof effect.

Description

technical field [0001] The invention relates to the field of building boards, in particular to a wood-grain imitation wall made of a silicon-aluminum composite material and a preparation process thereof. Background technique [0002] With the continuous development of building decoration, people have higher and higher requirements for decoration, especially in the selection of materials, which not only require reasonable price, economical and practical, but also elegant appearance and environmental protection requirements. [0003] In the field of construction, block building materials are generally used for masonry in the production of exterior walls, and then thermal insulation, plastering, puttying, painting or exterior wall bricks, or keels and curtain walls are added to the outside of the exterior walls. The operation of the type of work can finally complete the complete construction of the outer wall, which leads to complicated procedures, complicated operations, and l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/075C04B28/00C04B24/26
Inventor 程凤岐王东彬柳意安胡梁
Owner 王东彬