A kind of hemp-dai cloth fabric and its production process

A fabric and hemp technology, which is applied in the field of hemp jacquard Dai cloth fabric and its production technology, can solve the problems of easy ejection of the yarn body at the fiber end, high bending and torsional rigidity of hemp fibers, and high unevenness in length. , to achieve the effect of improving the phenomenon of not falling off, improving wearing comfort and good visual effect

Active Publication Date: 2015-10-07
SHANGHAI JUNTEX TEXTILE +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, the bending and torsional rigidity of hemp fiber is large, the fiber is not easy to cohere, the length unevenness is high, the fiber end is easy to pop out of the yarn body, the hairiness is much, hard and long
Therefore, pure hemp yarn is hard, brittle and straight, and has defects such as low single strength and many knots, which makes it difficult for knitting and weaving to bend and form loops.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Warp: The weight ratio of hemp and bright rayon is 30:70, the count of the warp is 60s, the twist coefficient is 450, and the warp density is 450 pieces / 10cm; the single-ply yarn is obtained through the existing compact spinning technology Wire.

[0027] Weft: the weight ratio of Porel fiber to polyester is 20:80, the denier of the weft is 120D, the twist coefficient is 370, and the density of weft is 230 / 440 per centimeter; the color of weft is two kinds;

[0028] Using Japanese Toyota JA710 air-jet loom and French Stäubli LX320 for weaving, the jacquard pattern is transmitted to the machine computer, and the fabric structure diagram is made by the photo rotation method. When weaving jacquard, the pattern is 2.6m in one cycle;

[0029] The parameter setting of Japan Toyota JA710 air jet loom is: the main nozzle pressure is 3-3.5kg / cm 2 , auxiliary injection pressure 4-4.5kg / cm 2 , the vehicle speed is 450 rpm, the weft insertion time is designed to be 90°, the back b...

Embodiment 2

[0037] Warp: the weight ratio of hemp and bright rayon in the warp is 35:65, the count of the warp is 50s, the twist coefficient is 460, and the warp density is 420 / 10cm; the warp is obtained through the existing compact spinning technology Obtain a single yarn.

[0038] Weft: the weight ratio of Porel fiber to polyester is 35:65, the denier of the weft is 100D, and the twist coefficient is 390; the weft density is 280 per centimeter; the weft adopts the blending of 2 single strands of Porel fiber and polyester The yarns are plied together.

[0039] Using Japanese Toyota JA710 air-jet loom and French Stäubli LX320 for weaving, the jacquard pattern is transmitted to the machine computer, and the fabric structure diagram is made by the photo rotation method. When weaving jacquard, the pattern is 2.6m in one cycle;

[0040] The parameter setting of Japan Toyota JA710 air jet loom is: the main nozzle pressure is 3-3.5kg / cm 2 , auxiliary injection pressure 4-4.5kg / cm 2 , the veh...

Embodiment 3

[0048] Warp: the weight ratio of hemp and bright rayon is 40:60, the count of the warp is 55s, the twist coefficient is 470, and the warp density is 450 / 10cm; the single-ply yarn is obtained through the existing compact spinning technology Wire.

[0049] Weft: the weight ratio of Porel fiber to polyester is 30:70, the denier of the weft is 200D, and the twist coefficient is 390; the weft density is 230 / 400 / 600 / 800 per centimeter, and the weft is 6 colors; The weft is made of 3 single-strand Porel fiber and polyester blended yarns.

[0050] Using Japanese Toyota JA710 air-jet loom and French Stäubli LX320 for weaving, the jacquard pattern is transmitted to the machine computer, and the fabric structure diagram is made by the photo rotation method. When weaving jacquard, the pattern is 2.6m in one cycle;

[0051] The parameter setting of Japan Toyota JA710 air jet loom is: the main nozzle pressure is 3-3.5kg / cm 2 , auxiliary injection pressure 4-4.5kg / cm 2 , the vehicle speed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a China-hemp Dai fabric which is formed by interweaving warps and wefts through a jacguard; the warps are blended yarns of China-hemp and lustrous rayons; the weight ratio of the China-hemp to lustrous rayons in the warps is 30-50:50-70; the count of the warps are 60-45s and the twist coefficient of the warps is 450-490; the wefts are blended yarns of Porel fibers and Dacron; the weight ratio of the Porel fibers to Dacron in the wefts is 20-35:65-80, the denier of the wefts is 100-200D and the twist coefficient is 370-390. The China-hemp Dai fabric is bright-colored and soft in hand feeling and has the self-temperature and humidity adjusting, controlling and balancing function and the strength and performance of the China-hemp Dai fabric also meet the industrial production demands.

Description

technical field [0001] The invention relates to a textile fabric, in particular to a Dai cloth fabric of hemp jacquard and a production process thereof. Background technique [0002] Now many national costume fabrics on the market, especially the national costume fabrics of the Dai people are basically jacquard fabrics with gorgeous colors and complex patterns. Mainly polyester fabric. Fabrics other than polyester are only handmade and cannot be mass-produced. The disadvantages of the existing Dai clothing fabrics are non-absorbent, airtight, and poor comfort under local natural conditions, and because there are certain problems in the jacquard part of the Dai cloth, it causes serious itching when worn. [0003] The "hemp fibers" in daily life are mainly daily necessities such as "hemp ropes" and "sacks", which give people the impression that they are rough and stiff in appearance, dull in color, wear-resistant, and uncomfortable to skin. With the development of science a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D03D13/00D03D21/00D03D15/20D03D15/217D03D15/283D03D15/47D03D15/50
Inventor 朱威郭刚李彦吕香红李永航高志强
Owner SHANGHAI JUNTEX TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap