A kind of preparation method of colored polymer dispersed liquid crystal film

A technology of dispersed liquid crystal and polymer, applied in optics, instruments, nonlinear optics, etc., can solve the problems of colorful and unable to produce color, and achieve the effect of eliminating visual differences, slowing down visual haze, and gorgeous decorative effects.

Active Publication Date: 2017-05-24
江苏同辉新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method can only prepare monochromatic liquid crystal films, and cannot produce colorful and gorgeous decorative effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of colored polymer dispersed liquid crystal film
  • A kind of preparation method of colored polymer dispersed liquid crystal film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A preparation method of a colored polymer dispersed liquid crystal film, using anthraquinone dyes and azo dyes, the operation steps are as follows:

[0019] A. Mix anthraquinone dyes or azo dyes into liquid crystal raw materials, heat and stir evenly to color the liquid crystal raw materials to form colored liquid crystals; the anthraquinone dyes are 1,5-bis(phenylthio)anthraquinone dyes or 1,5-di(p-alkyl or alkoxy)anilinoanthraquinone dye or 1-(p-alkyl or alkoxy)anilinoanthraquinone dye or 1,5-diamino-4,8- Dihydroxy-2(p-alkoxybenzene)anthraquinone dye or 1,5-diamino-4,8-dihydroxy-3(p-alkoxybenzene)anthraquinone dye or 1,5-diamino- At least one dye or at least three dyes in 4,8-dihydroxy-3,7-bis(p-alkoxybenzene)anthraquinone dyes; azo dyes are p-dimethylaminoazobenzene dyes or bis Azo blue dye (Japanese dye, its product model is G168) or trisazo yellow dye (Japanese dye, its product model is G232); the weight percentage of the dye to the liquid crystal raw material is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing color polymer dispersed liquid crystal films. The method includes: mixing anthraquinone dye or azo dye into a liquid crystal raw material, and heating with stirring uniformly to enable the liquid crystal raw material to be colored to form color liquid crystals; mixing the color liquid crystals with a polymer monomer uniformly to form a liquid crystal mixture isotropous at a room temperature; mixing the liquid crystal mixture with glass beads, clamping the liquid crystal mixture mixed with the glass beads between two indium tin oxid conductive thin films and rolling to form a liquid crystal thin film; heating to cure the liquid crystal thin film or curing via ultraviolet light to obtain the color polymer dispersed liquid crystal film. The prepared color polymer dispersed liquid crystal film has the advantages that transparence and concealing are achieved and color variation is added.

Description

technical field [0001] The invention relates to a method for preparing a colored polymer-dispersed liquid crystal film. In the invention, anthraquinone dyes or azo dyes are mixed into liquid crystal raw materials, and then mixed evenly with polymer monomers to prepare a colored polymer-dispersed liquid crystal film. liquid crystal film. Background technique [0002] Chinese patent 200810005682.X discloses a method for manufacturing a liquid crystal film. The method for manufacturing a liquid crystal film includes a process of coating a liquid crystal polymer solution on an alignment substrate film and making the alignment substrate coated with the liquid crystal polymer solution In the drying process of film drying, in the drying process, the gas for drying the liquid crystal polymer solution is dehumidified and introduced into a drying furnace. Water is sufficiently prevented from being absorbed into the liquid crystal polymer solution, so that precipitation of the liquid ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02F1/1334
Inventor 刘俊玲王磊罗建伟张维平赵勤
Owner 江苏同辉新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com