A kind of dry grinding wheel and its manufacturing method

A manufacturing method and grinding wheel technology, applied in the direction of abrasive materials, grinding devices, manufacturing tools, etc., can solve the problems of poor recycling, low user satisfaction, waste of trimming wheel resources, etc., and achieve a good glaze effect , Reduce energy consumption, long service life

Inactive Publication Date: 2016-05-04
FOSHAN DINGSHUN TECH CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The grinding wheel in the prior art has the following disadvantages: its production cost is relatively high, and it uses colored precious metal powder, and the glaze powder ground out cannot be recycled well due to the presence of metal powder. The bonding agent of the trimming wheel is also relatively wasteful of resources, which makes the user satisfaction not high
The sintering temperature of the outer grinding wheel is 630-710°C, and the hot pressing temperature of the inner grinding wheel is 175-185°C, which has the disadvantage of high energy consumption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of dry grinding wheel and its manufacturing method
  • A kind of dry grinding wheel and its manufacturing method
  • A kind of dry grinding wheel and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] refer to Figure 1-Figure 3 , the dry grinding wheel described in this embodiment includes a base plate 1 and a grinding head 2 arranged on the base plate 1, and the grinding head is made of the following raw materials in parts by weight:

[0026] 200 parts of diamond, 130 parts of silicon carbide, 100 parts of polyvinyl chloride resin powder, 10 parts of coupling agent, 200 parts of silicon carbide micropowder, 20 parts of anti-wear agent, and 100 parts of polyvinyl alcohol rubber powder.

[0027] The particle size of the silicon carbide micropowder is 1500 mesh. The wear-resistant agent is cryolite. The substrate is an aluminum substrate.

[0028] The invention discloses a method for making a dry grinding wheel. The raw materials are weighed according to the formula of the above-mentioned grinding head, then a uniformly mixed material is obtained through a mixing process, and finally a dry grinding wheel is obtained through a forming process.

[0029] The mixing pr...

Embodiment 2

[0035] Features of this embodiment: 130 parts of diamond, 100 parts of silicon carbide, 60 parts of polyvinyl chloride resin powder, 5 parts of coupling agent, 200 parts of silicon carbide micropowder, 10 parts of anti-wear agent, 60 parts of polyvinyl alcohol rubber powder.

[0036] Others are the same as in Example 1.

Embodiment 3

[0038] Features of this embodiment: 150 parts of diamond, 120 parts of silicon carbide, 80 parts of polyvinyl chloride resin powder, 8 parts of coupling agent, 200 parts of silicon carbide micropowder, 15 parts of anti-wear agent, 80 parts of polyvinyl alcohol rubber powder.

[0039] Others are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dry grinding wheel. The dry grinding wheel comprises a substrate and a grinding head arranged on the substrate. The grinding head is prepared from, by weight, 130 parts to 200 parts of diamond, 100 parts to 130 parts of silicon carbide, 60 parts to 100 parts of polyvinyl chloride resin powder, 5 parts to 10 parts of coupling agents, 200 parts of silicon carbide micro powder, 10 parts to 20 parts of anti-abrasion agents, and 60 parts to 100 parts of polyvinyl alcohol gelatine powder. The invention discloses a manufacturing method of the dry grinding wheel. The raw materials are weighed according to the formula of the grinding head, then, an evenly mixed mixture is obtained through the mixing technology, and finally the dry grinding wheel is obtained through the forming technology. The dry grinding wheel has the advantages that the materials are easy to obtain, grinding sharpness and hardness performance of a grinding wheel matrix are good, and the service life is long. The manufacturing method has the advantages of being low in sintering temperature, low in manufacturing cost and capable of achieving energy conservation and environmental protection.

Description

technical field [0001] The invention relates to a grinding wheel and a manufacturing method thereof, in particular to a dry grinding wheel and a manufacturing method thereof, which are suitable for glazed dry-type edging machines. Background technique [0002] At present, when the common dry grinding wheel grinds glazed tiles, two types of dry metal bonded grinding wheel and polyimide resin bonded dry trimming wheel are used in combination. In addition, the Chinese patent application number is The invention patent of "200610035898.1" discloses a grinding wheel and its manufacturing method. The formula weight ratio of the inner grinding wheel is: diamond 90-110g, green silicon carbide 45-55g, coupling agent 45-55g, modified phenolic resin powder 90-110g, filler: green silicon carbide powder 90-110g, alloy powder 162-196g, ZnO18-22g, cr 2 o 3 32-48g. The manufacturing method is to press a ring of resin bonded diamond working layer on the inner layer of the metal bonded diam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D18/00B24D3/28B29C69/00
Inventor 冯竞浩周宝泉
Owner FOSHAN DINGSHUN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com