Stainless steel water faucet shell welding technology

A faucet shell, welding process technology, applied in welding equipment, laser welding equipment, welding/welding/cutting items, etc., can solve the problems of easy damage to the faucet shell, large welding effect, insufficient bonding force, etc., to achieve excellence Good mechanical properties, good safety and hygiene performance, and small deformation of the workpiece

Active Publication Date: 2014-09-17
HUAQIAO UNIVERSITY
View PDF12 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this method does not disclose the detailed welding process, because argon arc welding often causes deformation, hardness reduction, sand holes, local annealing, cracking, pinholes, wear, scratches, undercuts, or bonding due to the large heat-affected zone. Insufficient force and internal stress damage, etc. The specific welding method has a great influence on the welding effect. In addition, this method still needs polishing after welding, which is easy to damage the faucet shell

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stainless steel water faucet shell welding technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.

[0034] The stainless steel faucet housing welding process of this implementation includes the following steps:

[0035] (1) Material selection: Austenitic stainless steel 1Cr18Ni8 plate with a thickness of 2mm-3mm is selected as the material, and the specific plate thickness can be selected according to actual needs.

[0036] (2) Parts preparation: The austenitic stainless steel 1Cr18Ni8 plate is made into the body and the bottom plate of the faucet shell respectively by means of pressure processing. During the processing, the unevenness and dislocation of the corresponding welding positions on the body and the bottom plate should be Control within 0.3mm. When the pressure processing method cannot achieve the required unevenness and misalignment, machining should be used to control the unevenness and misalignment of the corresponding welding po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a water faucet shell production technology, in particular to a stainless steel water faucet shell welding technology. The stainless steel water faucet shell welding technology comprises the following steps of material selection, part preparation, cleaning before welding, part clamping, part welding and post-welding checking. In the part clamping process, a welding clamp needs to be adjusted so that a welding position of a base plate can be embedded in a welding position of a body. A laser penetration fusion welding method is adopted for part welding. Due to the facts that the welding position of the base plate is embedded in the welding position of the body, and the body and the base plate are welded together through the laser penetration fusion welding method which is highly centralized in energy density, weld strength of weld joints is high, and the weld joints are compact and beautiful in appearance.

Description

technical field [0001] The invention relates to a production process for a faucet shell, in particular to a welding process for a stainless steel faucet shell. Background technique [0002] At present, the industry generally adopts the method of casting to produce the faucet shell, and the main material used is copper alloy or zinc alloy, and the cost is relatively high. The production process of the general faucet shell is: sand core forming-sand core inspection-casting alloy melting-chemical composition analysis-gravity casting-subsequent processing, etc. However, due to the overall soft and porous nature of the sand, the dimensional accuracy of the casting is low, and the surface is also rough and prone to defects, which makes the forming quality of the faucet poor. Simultaneously, each sandy mold can only be poured once, and the mold is damaged after obtaining the casting, and must be recast, which greatly increases the production cost and reduces the production efficie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K26/14B23K26/60
CPCB23K26/14B23K26/28B23K2103/04
Inventor 周广涛王立鹏陈强陈志伟陈聪彬刘骏梁国俐
Owner HUAQIAO UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap