Nano-silver/polystyrene hollow composite microspheres and preparation method thereof

A technology of polystyrene and composite microspheres, which is applied to the preparation of microspheres, microcapsule preparations, chemical instruments and methods, etc., can solve the problems of large specific surface area of ​​nano-silver, influence on antibacterial properties of materials, and large number of surface atoms. Good monodispersity, easy implementation, and simple polymerization process

Active Publication Date: 2014-11-19
ANHUI UNIVERSITY
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the large specific surface area of ​​nano silver, large number of surface atoms, high surface energy, and a large number of surface defects, the agglomeration betwe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-silver/polystyrene hollow composite microspheres and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0037] Example 1

[0038] The preparation of silica / polystyrene microspheres includes the following raw materials:

[0039] Styrene 8 parts

[0040] γ-methacryloxypropyl trimethoxysilane 0.6 part

[0041] Ethyl orthosilicate 5 parts

[0042] 0.6 parts of divinylbenzene

[0043] Hexadecane 0.8 parts

[0044] Azobisisobutyronitrile 0.15 parts

[0045] Methacrylic acid 1.6

[0046] Acrylonitrile 1 part

[0047] Sodium dodecyl diphenyl ether disulfonate 0.01 part

[0048] 95 parts of water

[0049] Ammonia water 1.5 parts (mass fraction 28%)

[0050] The specific preparation method is as follows:

[0051] Weigh styrene, hexadecane, γ-methacryloxypropyltrimethoxysilane, ethyl orthosilicate, divinylbenzene, methacrylic acid, and azobisisobutyronitrile as the oil phase. Dissolve sodium dodecyl sulfonate in water as the water phase. After the oil phase is stirred and mixed, slowly add it to the water phase, pre-emulsify it with magnetic stirring at room temperature for 30 minutes, and then use high-spe...

Example Embodiment

[0058] Example 2

[0059] The preparation of silica / polystyrene microspheres includes the following raw materials:

[0060] Styrene 8 parts

[0061] γ-methacryloxypropyl trimethoxysilane 0.8 parts

[0062] Ethyl orthosilicate 5 parts

[0063] 0.6 parts of divinylbenzene

[0064] Hexadecane 0.8 parts

[0065] Azobisisobutyronitrile 0.15 parts

[0066] Methacrylic acid 1.6

[0067] Acrylonitrile 1 part

[0068] Sodium dodecyl diphenyl ether disulfonate 0.01 part

[0069] 95 parts of water

[0070] Ammonia water 1.5 parts (mass fraction 28%)

[0071] The specific preparation method is as follows:

[0072] (Same as Example 1)

[0073] The raw materials and specific preparation methods for preparing nano silver / polystyrene hollow composite microspheres are as follows

[0074] (Same as Example 1)

Example Embodiment

[0075] Example 3

[0076] The preparation of silica / polystyrene microspheres includes the following raw materials:

[0077] Styrene 8 parts

[0078] γ-methacryloxypropyl trimethoxysilane 0.6 part

[0079] Ethyl orthosilicate 5 parts

[0080] 0.6 parts of divinylbenzene

[0081] Hexadecane 0.8 parts

[0082] Azobisisobutyronitrile 0.15 parts

[0083] Methacrylic acid 1.6

[0084] Acrylonitrile 0 parts

[0085] Sodium dodecyl diphenyl ether disulfonate 0.01 part

[0086] 95 parts of water

[0087] Ammonia water 1.5 parts (mass fraction 28%)

[0088] The specific preparation method is as follows:

[0089] (Same as Example 1)

[0090] The raw materials and specific preparation methods for preparing nano silver / polystyrene hollow composite microspheres are as follows

[0091] (Same as Example 1)

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses nano-silver/polystyrene hollow composite microspheres and a preparation method thereof. The preparation method comprises the following steps: by taking acrylic acid and acrylonitrile as functional monomers, preparing polystyrene microspheres of which the surfaces are jointly modified by carboxyl and nitrile groups by adopting a dual-in-situ miniemulsion polymerization process, preparing hollow polystyrene microspheres taking silicon dioxide as cores by utilizing the growing phase separation effect of polystyrene and tetraethyl orthosilicate, in-situ hydrolysis of tetraethyl orthosilicate and in-situ polymerization of styrene, then dropping silver nitrate, adsorbing silver ions by static electricity, and preparing the nano-silver/polystyrene hollow composite microspheres under the reduction action of hydrazine hydrate. The method provided by the invention has the advantages of simple process, mild conditions and easiness in control, the obtained microspheres are uniformly coated with nano-silver, and the coating rate is high.

Description

technical field [0001] The invention belongs to the field of inorganic / polymer composite materials, and in particular relates to nanometer silver / polystyrene hollow composite microspheres and a preparation method thereof. Background technique [0002] Antibacterial products are recognized as environmentally friendly and healthy products by countries all over the world. They are in great demand in domestic and foreign markets and are widely used in plastics, fibers, medical, construction, chemical and other fields; their use fundamentally eliminates the Cross-infection between people, people and things, things and things. At present, antibacterial materials are developing towards nano-antibacterial technology and inorganic / polymer nano-antibacterial materials. Nano-scale antibacterial materials refer to the preparation of nano-scale antibacterial agents through certain methods and technologies, and then compound them with antibacterial carriers to prepare materials with anti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F212/08C08F230/08C08F212/36C08F220/06C08F220/46C01B33/12B01J13/14B01J13/00
Inventor 杨建军吴庆云张建安吴明元王云云
Owner ANHUI UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap