Aluminum foil surface intaglio printing ink and preparation technology thereof

A gravure printing and ink technology, applied in the field of printing ink, can solve the problems of white leakage on the surface of aluminum foil, affecting the appearance of aluminum foil packaging products, etc., and achieve the effects of fast drying speed, good water and oil resistance, and good water resistance.

Active Publication Date: 2014-11-19
SUZHOU SIDIKE NEW MATERIALS SCI & TECH
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, there will be white leakage on the surface of the aluminum foil, which will affect the appearance of the aluminum foil packaging product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum foil surface intaglio printing ink and preparation technology thereof
  • Aluminum foil surface intaglio printing ink and preparation technology thereof
  • Aluminum foil surface intaglio printing ink and preparation technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be further described in detail below with reference to the embodiments, so that those skilled in the art can implement it according to the text of the description.

[0021] The present invention provides an aluminum foil gravure printing ink, wherein the ink is made of the following percentages of raw materials: polyurethane resin 30-35%; polyester resin 10-15%; carbon black 8-12%; solvent 30 ~37%; additives 2~3%; fillers 10~20%. Among them, the polyester resin is selected from one or more of nitrocellulose, cellulose acetate, cellulose acetate propionate and cellulose acetate butyrate; the carbon black is an insulating carbon black; the solvent is toluene, methyl ethyl ketone, iso One or more of propanol, n-butanol, butyl acetate, ethyl acetate, cyclohexanone and butyl ester.

[0022] The additives in this case include defoaming agent, leveling agent, dispersant, wax powder, antistatic agent, matting powder; among them, the defoaming agent is one...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminum foil surface intaglio printing ink. The aluminum foil surface intaglio printing ink is prepared by using 30-35% of polyurethane resin, 10-15% of polyester resin, 8-12% of carbon black, 30-37% of a solvent, 2-3% of an assistant and 10-20% of a filler. The ink provided by the invention has a very good bonding performance with aluminum foil, overcomes the bare phenomenon due to oil stains on the surface of the aluminum foil, and has the characteristics of fast drying speed and good water resistance.

Description

Technical field [0001] The invention relates to the technical field of printing inks, in particular to an ink printed on the surface of an aluminum foil by a gravure coating method. Background technique [0002] In recent years, aluminum foil has been widely used in many fields such as food, medicine, aerospace, etc. due to its light weight, good sealing, good covering, and environmental protection. Since 2006, China's aluminum foil production capacity and output have continued to rank first in the world. The demand for aluminum foil market is growing rapidly. In 2008, China's aluminum foil output was 1.57 million tons, accounting for 44% of the global total. At present, China's annual consumption of aluminum foil has become the world's second largest aluminum foil consumer after the United States. [0003] The food industry and the pharmaceutical industry are important markets for aluminum foil packaging. Their requirements for printing inks are water-based, non-toxic, have go...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/104
Inventor 金闯禾文静
Owner SUZHOU SIDIKE NEW MATERIALS SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap