High initial adhesion self-adhering waterproof roll and preparation method

A technology of self-adhesive waterproof membrane and high initial viscosity, which is applied in the direction of polymer adhesive additives, non-polymer adhesive additives, adhesives, etc. Under the modified asphalt material, affect the waterproof effect and other problems, to achieve good self-healing and puncture resistance performance, good bonding and sealing performance, and prevent the effect of plant root puncture

Inactive Publication Date: 2015-01-07
包头市草原驼峰防水材料有限公司
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the base is uneven, there is floating dust on the surface, the base is wet or the temperature is low, the self-adhesive waterproof membrane will not be firmly bonded to the base, and it is easy to form a hollowing phenomenon, and a film will be formed on the interface of the base. It cannot be perfectly bonded to the base layer, that is, after the construction, the coiled material is peeled off from the base layer, and the interface is separated, and the modified asphalt material cannot be left on the base layer, which will affect the waterproof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High initial adhesion self-adhering waterproof roll and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A self-adhesive waterproof membrane with high initial viscosity, in terms of mass percentage: 35% of petroleum asphalt, 5% of softener, 5% to 25% of modifier, 2% of adhesive, 0.1% of interface agent, 0.1% of anti-aging agent, filling The softening agent is 5%, the petroleum asphalt is grade A naphthenic petroleum pitch, the penetration is 70-200, based on 0.1mm, and the softening agent is selected from maleic acid, octyl acrylate, second-line machine oil, A mixture of one or more of three-line engine oil, furfural oil, naphthenic oil, aromatic oil, and co-solvents containing low-molecular-weight aromatics, and the modifier is selected from the group consisting of styrene-butadiene block copolymers, Hydrogenated styrene-butadiene block copolymer, styrene-isoprene-styrene block copolymer, styrene-butadiene rubber, neoprene, polyethylene, polypropylene, thermoplastic elastomer POE, desulfurized recycled rubber powder , butyl reclaimed rubber, and a mixture of one or more o...

Embodiment 2

[0016]A high initial tack self-adhesive waterproofing membrane, characterized in that it contains the following components, by mass percentage: 55% petroleum asphalt, 25% softener, 25% modifier, 8% adhesive, 2% interface agent, anti-aging agent 3%, 20% filler, the petroleum asphalt is naphthenic petroleum asphalt grade A, the penetration is 70-200, based on 0.1mm, the softener is selected from maleic acid, octyl acrylate, A mixture of one or more of the second-line reduced engine oil, the third-line reduced engine oil, furfural oil, naphthenic oil, aromatic oil, and co-solvent containing low-molecular-weight aromatics, and the modifier is selected from the group consisting of styrene-butadiene embedded Segment copolymer, hydrogenated styrene-butadiene block copolymer, styrene-isoprene-styrene block copolymer, styrene-butadiene rubber, neoprene, polyethylene, polypropylene, thermoplastic elastomer POE, One or more mixtures of desulfurized regenerated rubber powder, butyl reclai...

Embodiment 3

[0022] A high initial tack self-adhesive waterproof membrane, characterized in that it contains the following ingredients, in mass percentage: 40% petroleum asphalt, 20% softener, 20% modifier, 6% adhesive, 1% interface agent, anti-aging agent 2%, filler 20%, the petroleum asphalt is grade A naphthenic petroleum asphalt, the penetration is 70-200, based on 0.1mm, the softener is selected from maleic acid, octyl acrylate, A mixture of one or more of the second-line reduced engine oil, the third-line reduced engine oil, furfural oil, naphthenic oil, aromatic oil, and co-solvent containing low-molecular-weight aromatics, and the modifier is selected from the group consisting of styrene-butadiene embedded Segment copolymer, hydrogenated styrene-butadiene block copolymer, styrene-isoprene-styrene block copolymer, styrene-butadiene rubber, neoprene, polyethylene, polypropylene, thermoplastic elastomer POE, One or more mixtures of desulfurized regenerated rubber powder, butyl reclaim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high initial adhesion self-adhering waterproof roll which is characterized by comprising the following components in percentage by mass: 35-55% of petroleum asphalt, 5-25% of a softening agent, 5-25% of a modifier, 2-8% of an adhesive, 0.1-2% of a surfactant, 0.1-3% of an anti-aging agent and 5-20% of a filling agent.

Description

technical field [0001] The invention relates to a self-adhesive waterproof coiled material with high initial viscosity and a preparation method. Background technique [0002] With the development of the economy and the progress of the times, the requirements for building materials are getting higher and higher. Polymer waterproof membranes are recognized as waterproof materials with excellent performance and are widely used in waterproof and moisture-proof in industrial and civil construction fields. There are many disadvantages in the construction of self-adhesive waterproof membranes, which are as follows: (1) cumbersome welding construction; (2) poor anti-leakage effect, serious water leakage; (3) poor resistance to damage, prone to puncture or The tearing phenomenon requires manpower and material resources to repair, which shortens the service life of the waterproof membrane and causes a waste of resources and funds. In addition, the general polymer self-adhesive waterp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/00C09J195/00C09J11/04C09J11/06C09J11/08C08G18/75C08G18/73C08G18/66C08G18/42C08G18/32
Inventor 陈桂兰陈爱国陈仁训刘桂春陈海波
Owner 包头市草原驼峰防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com