Robot sprayed automobile intermediate coating

A primer and robot technology, used in coatings, conductive coatings, polyurea/polyurethane coatings, etc., can solve the problems of high energy consumption, high price, and high baking temperature, and achieve improved sedimentation resistance and improved resistance. Prickly heat performance, good effect of long-distance pipeline transportation

Inactive Publication Date: 2015-01-21
ZHENGZHOU YUTONG BUS CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the baking temperature of the intermediate coating is high, the energy consumption is large, and the conductive agent is made of special materials, which is expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Robot sprayed automobile intermediate coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In this embodiment, the robot sprays the automobile surfacer, which is composed of main paint, curing agent and thinner, and the main paint is composed of the following components in parts by weight: 26 parts of acrylic resin 802, 8 parts of polyester resin 803, titanium dioxide 25 parts, 12 parts of superfine talc powder, 0.5 parts of fumed silica, 0.5 parts of BYK110, 8 parts of zinc phosphate, 2 parts of ES80, 20 parts of mixed solvents of lipids and benzene, including: 12 parts of butyl acetate, xylene 5 parts, 3 parts of PMA; 55 parts of N75 in the curing agent, 45 parts of butyl acetate; a total of 100 parts of diluent, including: 20 parts of butyl acetate, 40 parts of xylene, 30 parts of PMA, and 10 parts of DBE.

[0022] The preparation method of robot spraying automobile surfacer in the present embodiment comprises the following steps:

[0023] (1) Main paint: Accurately take each component according to the parts by weight, add 26 parts of acrylic resin 802, 8 ...

Embodiment 2

[0028] In this embodiment, the robot sprays the automobile surfacer, which is composed of main paint, curing agent and thinner, and the main paint is composed of the following components in parts by weight: 20 parts of acrylic resin 802, 8 parts of polyester resin 803, titanium dioxide 25 parts, 18 parts of superfine talc powder, 0.5 parts of fumed silica, 0.5 parts of BYK110, 8 parts of zinc phosphate, 2 parts of ES80, 20 parts of mixed solvents of lipids and benzene, including: 12 parts of butyl acetate, xylene 5 parts, 3 parts of PMA; 55 parts of N75 in the curing agent, 45 parts of butyl acetate; a total of 100 parts of diluent, including: 20 parts of butyl acetate, 40 parts of xylene, 30 parts of PMA, and 10 parts of DBE.

[0029] When used, the volume ratio of main paint to curing agent and thinner is 40:10:15.

[0030] In this embodiment, the preparation method of robot spraying automobile surfacer is the same as that in Embodiment 1.

Embodiment 3

[0032] In this embodiment, the robot sprays the automobile surfacer, which is composed of main paint, curing agent and thinner, and the main paint is composed of the following components in parts by weight: 26 parts of acrylic resin 802, 8 parts of polyester resin 803, titanium dioxide 25 parts, 12 parts of superfine talcum powder, 0.5 parts of fumed silica, .5 parts of BYK1100, 8 parts of zinc phosphate, 20 parts of mixed solvents of lipids and benzene, including: 12 parts of butyl acetate, 5 parts of xylene, 3 parts of PMA; 55 parts of N75 in curing agent, 45 parts of butyl acetate; 100 parts of diluent in total, including: 20 parts of butyl acetate, 40 parts of xylene, 30 parts of PMA, and 10 parts of DBE.

[0033] When used, the volume ratio of main paint to curing agent and thinner is 40:10:15.

[0034] In this embodiment, the preparation method of robot spraying automobile surfacer is the same as that in Embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a robot sprayed automobile intermediate coating, and belongs to the technical field of automobile coatings. The automobile intermediate coating includes a main paint, a curing agent and a diluent, and the main paint comprises, by weight, 20-30 parts of acrylic resin, 5-10 parts of polyester resin, 20-30 parts of titanium dioxide, 5-20 parts of ultrafine talcum powder, 0.5-1.5 parts of fumed silica, 0.5-1.5 parts of a wetting dispersant, 3-10 parts of a conductive agent, 0-5 parts of a conductive assistant and 15-20 parts of a solvent. The settlement resistance of the coating is improved by selecting lightweight color fillers and adjusting the binder ratio of the intermediate coating in order to realize good long-distance pipeline conveying. In addition, the conductive agent and the conductive assistant are compounded according to a certain ratio to adjust the conductivity of the intermediate coating to 15-40Momega in order to adapt to the robot spraying and the cost of the intermediate coating.

Description

technical field [0001] The invention relates to a robot spraying automobile surfacer, which belongs to the technical field of automobile coatings. Background technique [0002] Automobile surfacer is a coating used between the automobile primer and the topcoat. Automobile secondary primer requires not only to be firmly attached to the surface of the primer, but also to be combined with the topcoat on it, which plays an important role in linking the preceding and the following. In addition to the requirements of good adhesion and bonding with the upper and lower coatings, the automotive secondary primer also requires good mechanical properties, which can provide protection properties suitable for the top coat, as well as suitable electrical conductivity and good settlement resistance, so that It is suitable for long-distance pipeline transportation, which is convenient for pipeline cleaning. [0003] At present, the automotive surfacer on the market is mainly used for manua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/06C09D7/12
CPCC08L2205/02C09D5/24C09D7/20C09D7/61C09D7/63C09D7/65C09D175/04C08L75/06C08K13/02C08K2003/2241C08K3/34C08K3/36C08K2003/328
Inventor 童志中魏永超邱民举梁保光刘凤山杨广伟徐平起陈耀龙刘合文王一昂刘朋巫青锋肖承龙刘鹏
Owner ZHENGZHOU YUTONG BUS CO LTD