Copper coordination polymer having ion exchange and solvent exchange functions and application of copper coordination polymer

A technology of coordination polymers and copper complexes, applied in the field of copper coordination polymers and preparation, Cu-anthracycline bistriazole two-dimensional copper coordination polymers, can solve the problems of rare two-dimensional structure, and achieve the reaction The operation is simple and easy, the reaction yield is high, and the method is simple and effective

Inactive Publication Date: 2015-04-08
TIANJIN NORMAL UNIVERSITY
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is a great challenge to design and synthesize triazole-copper metal coordination polymers containing nanopores and ion exchange functions. So far, there are relatively few reports in the literature, and two-dimensional structures are even rarer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copper coordination polymer having ion exchange and solvent exchange functions and application of copper coordination polymer
  • Copper coordination polymer having ion exchange and solvent exchange functions and application of copper coordination polymer
  • Copper coordination polymer having ion exchange and solvent exchange functions and application of copper coordination polymer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Preparation of 1-[9-(1H-1,2,4-triazol-1-yl)anthracen-10-yl]-1H-1,2,4-triazole (tatrz)

[0031] The molar ratio of 9,10-dibromoanthracene: triazole: potassium carbonate: copper oxide is 2:10:30:1;

[0032] CuO (0.0398 mg, 0.5 mmol), potassium carbonate (2.0731 g, 15 mmol), triazole (0.345 mg, 5 mmol), and 9,10-Dibromoanthracene (0.3360 g, 1 mmol), 20 mL DMF. Start stirring at 100 o C, reacted for 24 hours. After the reaction, the reaction solution was lowered to room temperature, filtered, and 100 mL of water was added to the filtrate, a large amount of precipitate was precipitated, filtered with suction, and the filter cake was collected, with a yield of 60%.

Embodiment 2

[0034] Complex 1 preparation of

[0035] Cu(NO 3 ) 2 and 1-[9-(1H-1,2,4-triazol-1-yl)anthracen-10-yl]-1H-1,2,4-triazole (tatrz) in a molar ratio of 1: 1;

[0036] tatrz (0.0625 g, 0.2 mmol) and Cu(NO 3 ) 2 (0.0483 g, 0.2 mmol) in H 2 O (6 mL) and CH 3 OH (4 mL) in a mixed solvent at room temperature for half an hour and then filtered, and the filtrate was volatilized at room temperature for two weeks to obtain green rod-shaped crystals suitable for X-ray single crystal diffraction analysis. Yield: 69%. Elemental analysis (%) C 37 h 38 CuN 14 o 12 : C 47.56, H 4.10, N 20.99; Found: C 47.68, H 4.08, N 20.88.

Embodiment 3

[0038] Ion exchange properties of complexes

[0039] in the complex 1 (0.4672 g, 0.5 mmol) and NaClO 4 (0.7023 g, 5 mmol) in a mixed solvent of water and methanol (10 mL, v:v = 5:5) was stirred for 6 hours, and green rod-shaped crystals suitable for X-ray single crystal diffraction analysis were obtained 1a , Yield: 25%. Elemental Analysis (%) C 40 h 44 Cl 2 CuN 12 o 14 : C 45.70, H 4.22, N 15.99; Found: C 45.58, H 4.02, N 15.78.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a copper coordination polymer as well as a preparation method and application of the copper coordination polymer. The copper coordination polymer is a nano-hole-containing Cu (II)-anthracenecyclo bistriazole two-dimensional coordination polymer having ion exchange and solvent exchange functions and is a complex having the following chemical formula, namely, {[Cu(tatrz)2(NO3)2].(CH3OH).4H2O} (1), wherein tatrz is 1-[9-(1H-1,2,4-triazole-1-yl) anthracene-10-yl]-1H-1,2,4-triazole. When NaClO4 is added into aqueous and methanol solutions of the complex, ClO4<-> can replace NO3<-> which is involved in the coordination to obtain the complex {[Cu(tatrz)2(H2O)2](ClO4)2.4CH3OH} (1a). When the complex (1) is immersed in methanol, water molecules in the complex are partially replaced by methanol molecules to obtain the complex {[Cu (tatrz)2 (NO3)2].4.4CH3OH.0.6H2O} (1c). The complex as an ion exchange and solvent exchange agent has great application value in the field of material science.

Description

[0001] The present invention has been funded by the National Natural Science Foundation of China (21471113), the Tianjin Municipal Education Commission project (20140506), the Tianjin Normal University academic innovation promotion project for young and middle-aged teachers, and the Tianjin Higher Education Innovation Team Training Program (TD12-5038). technical field [0002] The present invention relates to a transition metal coordination polymer, especially a copper coordination polymer and its preparation method and application. The copper coordination polymer is Cu(II)-anthracycline bistriazole di Copper-dimensional coordination polymer with ion exchange and solvent exchange functions. Background technique [0003] In recent years, the construction of materials with new open pore structures and capable of ion exchange and solvent adsorption is the most challenging subject. Not only because of their novel topology, but also because they often exhibit specific optical, el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07F1/08B01J45/00
CPCB01J45/00C07F1/08
Inventor 王英
Owner TIANJIN NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap