Mildew resistant treatment agent of wood
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
An anti-mildew treatment agent and wood technology, which is applied in the direction of impregnating wood, wood impregnation, wood processing equipment, etc., can solve the problems of wood not being used normally, environmental hazards for users, and easy mold and decay, etc. Convenience and easy-to-use effects
Inactive Publication Date: 2015-04-22
阜南佳利工艺品股份有限公司
View PDF4 Cites 11 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Wood is prone to mold and decay in a humid environment, causing the wood to be unable to be used normally. Now heavy metal salts are used for anti-mold treatment. Although it has a good anti-mold effect, heavy metals will leak out during use, which will cause harm to the environment and users. harm
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0010] An anti-mold treatment agent for wood, which is prepared by the following components by weight: 8 parts of sealwort, 12 parts of clove, 4 parts of woody fragrance, 4 parts of trillium, 9 parts of three-fork bitter, 3 parts of star anise, three Qiansan 1.8 parts, Tiannanxing 3 parts, bamboo leaves 8 parts, quicklime 12 parts, water 100 parts.
Embodiment 2
[0012] An anti-mold treatment agent for wood, which is prepared by the following components by weight: 7.5 parts of Polygonatum, 14 parts of Clove, 5 parts of Woody Fragrance, 3.5 parts of Trillium, 9 parts of Tridentia, 2.5 parts of Star Anise, 1.2 parts of Qiansan, 3 parts of Tiannanxing, 9 parts of bamboo leaves, 12 parts of quicklime, and 100 parts of water.
Embodiment 3
[0014] An anti-mold treatment agent for wood, which is prepared by the following components by weight: 7 parts of Polygonatum, 13 parts of Clove, 5 parts of Woody Fragrance, 5 parts of Trillium, 10 parts of Tridentia, 3 parts of Star Anise, Qiansan 1.5 parts, Tiannanxing 3 parts, bamboo leaves 8 parts, quicklime 14 parts, water 100 parts.
[0015] When using, mix Polygonatum, Clove, Woody Fragrance, Trillium, Sanchaku, Star Anise, Sanqiansan, Araceae, Bamboo Leaf, and water, soak at 65°C for 1 hour, then raise the temperature to 92°C, and continue soaking for 5 hours. To obtain the treatment solution, before use, add quicklime, stir evenly, add wood into it and soak. The present invention has a good inhibitory effect on black mold, red mold or penicillium and staphylococcus aureus.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to a mildew resistant treatment agent of wood. The mildew resistant treatment agent comprises 5-8 parts of Polygonatum sibiricum, 12-15 parts of Syzygium aromaticum, 3-5 parts of Radix Aucklandiae, 3-5 parts of Trillium tschonoskii, 8-12 parts of Evodia lepta, 2-4 parts of whitetomentose ainsliaes herb, 1-2 parts of Ormosia henryi Prain, 2-4 parts of Rhizoma Arisaematis, 8-10 parts of bamboo leaf, 12-15 parts of quicklime and 100 parts of water. The mildew resistant treatment agent of wood has the advantages of simple use method and convenient treatment, wood treated by the agent has a long mildew resistant time, can be used in air with the relative humidity of 45% at 25DEG C for 2 years without molds, and can be used under normal conditions for 4 years without molds.
Description
technical field [0001] The invention belongs to the field of wood processing, and in particular relates to an anti-mildew treatment agent for wood. Background technique [0002] Wood is the lignified tissue of plants capable of secondary growth, such as trees and shrubs. After the primary growth of these plants ends, the vascular cambium in the rhizome becomes active, developing bast outward and wood inward. Wood is a collective term for plant tissues that develop inwardly from the vascular cambium, including xylem and woody strands. Timber is a product of forestry and plays an important role in supporting human life. According to the different properties and characteristics of wood, people use them in different ways. Wood is prone to mold and decay in a humid environment, causing the wood to be unable to be used normally. Now heavy metal salts are used for anti-mold treatment. Although it has a good anti-mold effect, heavy metals will leak out during use, which will caus...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More 