A kind of embedded nylon pet glasses plate and preparation method thereof

An embedded and glasses technology, applied in glasses/goggles, chemical instruments and methods, flat products, etc., can solve the problems of mechanical strength, stiffness, low hardness, no bright spots, unfavorable to human health, etc., and achieve the effect of high hardness

Inactive Publication Date: 2016-07-27
黄永忠
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. During the processing of cellulose acetate sheet, a pungent acid smell will be volatilized, and cellulose acetate sheet is a non-degradable material, which is not friendly to the environment; when using polycarbonate resin particles, color essence is sometimes used for aesthetics Dyeing polycarbonate resin particles, or using paint to paint the formed frame, the color essence and paint used will directly contact the skin of the human body when wearing glasses, and long-term use is not conducive to human health
[0004] 2. The mechanical strength, rigidity and hardness of the above-mentioned acetate fiber material and polycarbonate material are relatively low, and the sliding performance and wear resistance are poor
[0005] 3. The appearance of traditional glasses plate only through dyeing or drawing patterns has no bright spots, and the pattern is single, which cannot meet the current requirements for the diversity and individualization of glasses patterns.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of embedded nylon pet glasses plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] An embedded spectacle plate, the embedded spectacle plate comprises a transparent layer, an embedding layer, a background layer and a base layer from the outside to the inside, the transparent layer is made of nylon, the background layer and the base layer are The materials are all PET, and the connection surface between any two adjacent layers of the embedded glasses plate is the joint surface. The PET is a degradable material and is more friendly to the environment. The use of nylon material can ensure good flexibility of the embedded spectacle plate.

[0035] The PET mentioned in the present invention is the abbreviation of polyethylene terephthalate. PET has the advantages of high mechanical strength, rigidity and hardness, and has good performance in sliding performance and wear resistance, electrical insulation, creep resistance, wear resistance and chemical stability.

[0036] The background layer is an opaque material, and the color of the background layer is ...

Embodiment 2

[0041] A kind of embedded spectacle plate described in embodiment one, wherein frame material 5.5mm, temple material 3.75mm, the thickness of described transparent layer is 1mm, the thickness of described embedding layer is 0.35mm, the thickness of described background layer The thickness is 0.8mm, and the remaining thickness is supplemented by the base layer, and the thickness of the base layer is 3.35mm or 1.6mm.

Embodiment 3

[0043] A kind of embedded spectacle plate described in embodiment one, wherein frame material 6.5mm, temple material 4.5mm, the thickness of described transparent layer is 1.2mm, the thickness of described embedding layer is 0.5mm, and described background layer The thickness of the base layer is 0.8mm, and the remaining thickness is supplemented by the base layer, and the thickness of the base layer is 4mm or 2mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an embedded type nylon PET (Polyethylene Terephthalate) glasses sheet material which has good safety, large mechanical strength and various patterns, and can be individually customized, and a preparation method thereof. The embedded type glasses sheet material sequentially comprises a transparent layer, an embedding layer, a background layer and a base layer in sequence from outside to inside, wherein the transparent layer is made of nylon; and the background layer and the base layer are made of PET. The embedded type nylon PET glasses sheet material has the beneficial effects that the glasses sheet material adopts an embedded type interlayer decorative design and the embedding layer can use various decorative materials, so that the patterns of glasses are greatly enriched; and the patterns of the sheet materials are more stereoscopic and the individualized requirements of people can be met.

Description

technical field [0001] The invention belongs to the field of spectacle plates and their preparation, and in particular relates to an embedded nylon PET spectacle plate and a preparation method thereof. Background technique [0002] Traditional spectacle frames can generally be divided into two types, one is cut from acetate sheets; the other is directly stamped from polycarbonate resin particles. However, these two materials have the following drawbacks: [0003] 1. During the processing of cellulose acetate sheet, a pungent acid smell will be volatilized, and cellulose acetate sheet is a non-degradable material, which is not friendly to the environment; when using polycarbonate resin particles, color essence is sometimes used for aesthetics Dyeing polycarbonate resin particles, or using paint to paint the formed frame, the color essence and paint used will directly contact the skin of the human body when wearing glasses, and long-term use is not conducive to human health. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02C5/00B32B27/36B29D7/00
CPCB32B27/06B32B27/08B32B27/34B32B27/36B32B2307/206B32B2307/536B32B2307/548B32B2307/554B32B2307/714G02C5/008
Inventor 李华强
Owner 黄永忠
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products