Homogenization thermal-treatment method for ultra-large semi-continuous cast round ingot

A homogeneous heat treatment and super-large size technology, which is applied in the field of aluminum alloy processing, can solve the problems of inability to fully eliminate dendrite structure and low melting point eutectic structure, uneven forging structure, forging billet cracking, etc., and achieve the elimination of low melting point eutectic structure organization, elimination of dendrite organization, and the effect of ensuring comprehensive performance

Active Publication Date: 2015-07-29
广西南南铝加工有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The 2219 aluminum alloy round ingot adopts semi-continuous casting production process. Due to the high pouring speed and cooling rate, the ingot is prone to dendrite segregation, casting stress, and a large number of non-equilibrium eutectic structures distributed along the grain boundaries, which seriously affect the ingot quality. Plastic processing performance and final product performance
[0005] The existing homogenization heat treatment technology does not have a process for super-large-sized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Homogenization thermal-treatment method for ultra-large semi-continuous cast round ingot
  • Homogenization thermal-treatment method for ultra-large semi-continuous cast round ingot
  • Homogenization thermal-treatment method for ultra-large semi-continuous cast round ingot

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] In this embodiment, the homogenization heat treatment of the 2219 round ingot with a diameter of Φ1320 mm is achieved by the following scheme:

[0048] (1) Put the round ingot sample into the heating device and raise the temperature to 180°C with a heating rate of 14°C / h;

[0049] (2) Raise the temperature of the round ingot from 180°C to 520°C at a heating rate of 60°C / h, and keep it at 520°C for 80 hours;

[0050] (3) Cooling the temperature of the round ingot from 520°C to 360°C at a cooling rate of 58°C / h;

[0051] (4) The temperature of the round ingot is lowered from 360°C to 130°C at a cooling rate of 200°C / h.

[0052] (5) The round ingot was taken out from the heating apparatus, and it was air-cooled from 130° C. to room temperature.

Embodiment 2

[0054] In this embodiment, the homogenization heat treatment of the 2219 round ingot with a diameter of Φ1320 mm and a super large diameter is realized by the following scheme:

[0055] (1) Put the round ingot sample into the heating device to raise the temperature to 180°C, and the heating rate is 10°C / h;

[0056] (2) Heat the round ingot from 180°C to 535°C at a heating rate of 90°C / h, and keep it at 535°C for 30 hours;

[0057] (3) Cool the round ingot from 535°C to 360°C at a cooling rate of 50°C / h;

[0058] (4) Cool the round ingot from 360°C to 130°C at a cooling rate of 80°C / h.

[0059] (5) The round ingot was taken out from the heating apparatus, and it was air-cooled from 130° C. to room temperature.

Embodiment 3

[0061] In this embodiment, the homogenization heat treatment of the 2219 round ingot with a diameter of Φ1320 mm and a super large diameter is realized by the following scheme:

[0062] (1) Put the round ingot sample into the heating device to raise the temperature to 180°C, and the heating rate is 14°C / h;

[0063] (2) First, raise the temperature of the round ingot from 180°C to 300°C at a heating rate of 60°C / h, and keep it at 300°C for 30 hours; then raise the temperature of the round ingot from 300°C to 520°C at a heating rate of 60°C / h , kept at 520°C for 65h.

[0064] (3) Cool the round ingot from 520°C to 360°C at a cooling rate of 48°C / h;

[0065] (4) Cool the round ingot from 360°C to 130°C at a cooling rate of 120°C / h.

[0066] (5) The round ingot was taken out from the heating apparatus, and it was air-cooled from 130° C. to room temperature.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a homogenization thermal-treatment method for an ultra-large semi-continuous cast round ingot and relates to the technical field of aluminum alloy processing. The method comprises the following concrete steps: (1) heating the round ingot to the temperature of 180 DEG C at a temperature rising speed below 15 DEG C/h; (2) heating the round ingot to the temperature of 520 to 535 DEG C from the temperature of 180 DEG C at a temperature rising speed of 60-90 DEG C/h, and keeping the temperature for 30h to 80h at the temperature of 520 to 535 DEG C; (3) cooling the round ingot to the temperature of 360 DEG C from the temperature of 520 t0 535 DEG C at a temperature descending speed below 60DEG C/h; (4) cooling the round ingot to the temperature of 130 DEG C from the temperature of 360 DEG C at a temperature descending speed of 80 to 200 DEG C/h; (5) cooling the round ingot to room temperature from the temperature of 130 DEG C. According to the characteristics of the ultra-large semi-continuous cast round ingot, the method disclosed by the invention can be used for fully eliminating dendritic structures and low-melting-point eutectic structures, also enabling the elements such as zirconium, manganese and vanadium to be dispersed and distributed uniformly and guaranteeing the deformation processing structures in the later period and the final comprehensive performances of products.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy processing, in particular to a method for homogenizing heat treatment of a super-sized semi-continuous casting round ingot. Background technique [0002] Due to its high-temperature and low-temperature mechanical properties, high fracture toughness, stress corrosion resistance, processing performance, and good welding performance, 2219 aluminum alloy is a typical heat-treatable forged aluminum alloy. Products are used in aviation, aerospace and other fields in different forms and heat treatment states, especially their forgings can be used as materials for rocket storage tanks. With the continuous improvement of rocket thrust requirements and the increase of rocket diameter, there are higher requirements for the diameter, composition, structure and performance uniformity of 2219 forged billets. [0003] The 2219 aluminum alloy round ingot adopts semi-continuous casting production process. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22F1/057
CPCC22F1/057
Inventor 乐永康姚祥何克准蓝东华唐露华
Owner 广西南南铝加工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap