A coating for auxiliary electrodes of silicon-fixed sensors and its preparation method

A technology for auxiliary electrodes and sensors, applied in the direction of alkali metal silicate coatings, coatings, etc., can solve the problems that the stability of auxiliary electrodes cannot be guaranteed, so as to improve the working efficiency of blast furnaces, improve stability, and excellent high-temperature adhesion performance Effect

Active Publication Date: 2017-02-22
WUHAN UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current research focuses on the selection of the auxiliary electrode itself, while ignoring the problem of various additives for the auxi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0034] Example 1

[0035] A paint used for an auxiliary electrode of a fixed silicon sensor and a preparation method thereof. The composition and content of the paint used to fix the auxiliary electrode of the silicon sensor in this embodiment are:

[0036] Ethanol 35~40wt%;

[0037] Triethanolamine 0.5~0.7wt%;

[0038] Butyl benzyl phthalate 0.5~0.7wt%;

[0039] Water glass 4~6wt%;

[0040] Polyvinyl butyral 0.5~0.7wt%;

[0041] Silica 30~36.5wt%;

[0042] Calcium fluoride powder 20~26.5wt%.

[0043] The preparation method of this embodiment is: according to the composition and content of the coating, firstly, ethanol and triethanolamine are mixed in a ball mill for 15 to 18 minutes to obtain a premix. Then, silica powder and calcium fluoride powder are added to the premix, and ball milled for 8-10 hours to obtain slurry I. Then add water glass to the slurry I and ball mill for 4 to 5 hours to obtain slurry II. Finally, polyvinyl butyral and butyl benzyl phthalate are added to the slur...

Example Embodiment

[0048] Example 2

[0049] A paint used for an auxiliary electrode of a fixed silicon sensor and a preparation method thereof. The composition and content of the paint used to fix the auxiliary electrode of the silicon sensor in this embodiment are:

[0050] Ethanol 34~39wt%;

[0051] Triethanolamine 0.6~0.8wt%;

[0052] Butyl benzyl phthalate 0.6~0.8wt%;

[0053] Water glass 4.8~6.8wt%;

[0054] Polyvinyl butyral 0.6~0.8wt%;

[0055] Silica 30.5~37wt%;

[0056] Calcium fluoride powder 20.5~27wt%.

[0057] The preparation method of this embodiment is: according to the composition and content of the coating, firstly, ethanol and triethanolamine are mixed in a ball mill for 18-22 minutes to obtain a premix. Then add silica powder and calcium fluoride powder to the premix, and ball mill for 10-12 hours to obtain slurry I. Then add water glass to the slurry I and ball mill for 5-6 hours to obtain slurry II. Finally, polyvinyl butyral and butyl benzyl phthalate are added to the slurry II, and...

Example Embodiment

[0062] Example 3

[0063] A paint used for an auxiliary electrode of a fixed silicon sensor and a preparation method thereof. The composition and content of the paint used to fix the auxiliary electrode of the silicon sensor in this embodiment are:

[0064] Ethanol 33~38wt%;

[0065] Triethanolamine 0.7~0.9wt%;

[0066] Butyl benzyl phthalate 0.7~0.9wt%;

[0067] Water glass 5.4~7.4wt%;

[0068] Polyvinyl butyral 0.7~0.9wt%;

[0069] Silica 31~37.5wt%;

[0070] Calcium fluoride powder 21~27.5wt%.

[0071] The preparation method of this embodiment is: according to the composition and content of the coating, first mix ethanol and triethanolamine in a ball mill for 22~26 minutes to obtain a premix; then add silica powder to the premix , Calcium fluoride powder, ball mill for 12-14h to obtain slurry Ⅰ. Then add water glass to the slurry I and ball mill for 6-7 hours to obtain slurry II. Finally, polyvinyl butyral and butyl benzyl phthalate were added to the slurry II, and the coating was pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a coating for a silicon determination sensor auxiliary electrode and a preparation method thereof. The coating for the silicon determination sensor auxiliary electrode contains, by weight, ethyl alcohol 32-40%, triethanolamine 0.5-1%, butyl benzyl phthalate 0.5-1%, water glass 4-8%, polyvinyl butyral 0.5-1%, silicon dioxide powder 32-38% and calcium fluoride powder 20-28%. The ethyl alcohol and the triethanolamine are firstly mixed in a ball grinding mill according to the components and contents for 15-30 minutes, the silicon dioxide powder and the calcium fluoride powder are added to perform ball grinding for 8-16 hours, then the water glass is added to perform ball grinding for 4-8 hours, and finally the polyvinyl butyral and the butyl benzyl phthalate are added to perform ball grinding for 8-16 hours so as to obtain the coating for the silicon determination sensor auxiliary electrode. The preparation method is simple, and the prepared coating for the silicon determination sensor auxiliary electrode has the advantages of being high in strength, excellent in high-temperature adhesion performance and good in using effect.

Description

technical field [0001] The invention belongs to the technical field of coatings. In particular, it relates to a coating for auxiliary electrodes of silicon-fixed sensors and a preparation method thereof. Background technique [0002] Silicon determination sensors for metallurgy can quickly and accurately measure the silicon content of molten iron or steel, and perform corresponding process operations based on the detected data, which is of great significance to speed up smelting and improve product quality. However, due to the poor adhesion between the traditional silicon-fixed sensor and the substrate at low and high temperatures, the surface of the auxiliary electrode coating is facing the problem of cracking at low temperature and falling off at high temperature, which makes the solid electrolyte surface coating at high temperature The auxiliary electrode paint of the silicon-fixed sensor cannot fully contact the melt to be measured, the conduction of oxygen ions in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D1/00C09D1/04C09D7/12
Inventor 王文长谢光远林寒月赵芃邹航贾晓飞
Owner WUHAN UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap