A kind of preparation method of rare earth permanent magnet material

A rare-earth permanent magnet and material block technology, which is applied in the direction of magnetic materials, magnetic objects, electrical components, etc., can solve problems such as fusion, magnetic powder compact oxidation, and adhesion of processing chips, and achieve high utilization rate, low sintering energy consumption, The effect of short holding time

Active Publication Date: 2017-09-15
浙江三环康盈磁业有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Further, this method can solve the problems of oxidation, adhesion, fusion, and burning of magnetic powder compacts during processing. This method does not need to add any antioxidants during powder making and pressing, and does not need to apply any cooling during processing. agents, cutting fluids, lubricants or anti-fusion powders

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of rare earth permanent magnet material
  • A kind of preparation method of rare earth permanent magnet material
  • A kind of preparation method of rare earth permanent magnet material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0076] Preferred embodiments of the present invention are described below, and it should be understood that the preferred embodiments described here are only used to illustrate and explain the present invention, and are not intended to limit the present invention.

[0077] The rare earth permanent magnet material used in the specific embodiment of the present invention is R-T-B, R is at least one element selected from rare earth elements and Y, T is a transition metal element including Fe, and B is boron.

[0078] Preferably, the alloy comprises 26-31wt% of Nd and / or Pr, 0-5wt% of Dy, 0-1wt% of Co, 0-0.5wt% of Nb, 0-0.2wt% of Al, 0-0.2 Wt% Cu, B 0.9-1.1wt%, balance Fe.

[0079] The R-T-B rare earth permanent magnet material was prepared by the following preparation method.

[0080] Such as Figure 1-2 As shown, firstly, the casting sheet of R-T-B rare earth permanent magnet material is prepared by the known rapid quenching technology, which specifically includes: melting the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a rare earth permanent magnetic material preparing method comprising the steps of preparing a press blank of powder of sintered magnets, using row wires to machine the press blank and then performing sintering. All the steps are performed in a wholly sealed atmosphere. The row wire machining means line machining for the press blank formed by pressing; after the press blank is clamped and located, a driving mechanism drives the row wires to move back and forth linearly; the press blank is machined according to a preset path along with the rotation of a locating clamp and finally forms a block body or a sheet body with a preset shape and size, an arched body or other specially-shaped bodies; the final forming size contains the sintering shrinkage allowance. The rare earth permanent magnetic material preparing method has the advantages of short preparation technological process, high machining efficiency, low magnetic powder loss, and high rare earth utilization rate. The machining is near net machining, so that a finish machining procedure performed after sintering is saved.

Description

technical field [0001] The invention relates to a method for manufacturing rare earth permanent magnet materials, belongs to the technical field of sintered magnet preparation, and in particular relates to a preparation process of sintered NdFeB permanent magnet materials. Background technique [0002] Rare earth sintered magnet is a kind of rare earth permanent magnet material manufactured by the principle of powder metallurgy. In addition to equipment, sensors, magnetic separation, magnetic attraction and other fields, it is widely used in various industrial motors including automobiles, computer hard drives, wind power generation, electric tools, electric bicycles, air-conditioning compressors, elevators, aerospace and other fields middle. [0003] High-performance NdFeB materials have high requirements on production lines and preparation methods, especially for NdFeB materials prepared by sintering process, the magnetic powder particle size is finer, and the material is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F3/02B22F3/04B22F3/16H01F1/057
Inventor 汪康道
Owner 浙江三环康盈磁业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com