Medical quick biological rhinal styptic powder and preparation method thereof

A technology of hemostatic powder and nasal cavity, which is applied in the field of medical materials, can solve the problems of long production cycle, high production cost, and unsatisfactory hemostasis effect, and achieve the effect of repairing wounds, shortening coagulation time, and promoting wound healing

Active Publication Date: 2015-12-09
DONGGUAN DAQING MEDICAL DEVICES CO LTD +2
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chitosan-based hemostatic materials are already on the market, but it usually takes a few minutes for a single-component chitosan hemostatic product to promote the formation of a blood clot, so the hemostatic effect is not ideal in the case of large bleeding, and it is di

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0082] A kind of quick hemostatic powder of medical biological nasal cavity, described medical biological quick hemostatic powder of nasal cavity comprises the raw material of following weight portion:

[0083] Puffball Extract 65 parts

[0084] Sodium carboxymethyl cellulose 10 parts

[0085] 1 part large thistle extract

[0086] 1 part coriander root extract

[0087] Sophora japonica extract 1 part

[0088] 1 part snakeberry extract

[0089] 0.5 part of orientalis leaf extract.

[0090] The sodium carboxymethylcellulose has a melting point of 270°C and a density of 1.5g / cm 3 croscarmellose sodium.

[0091] The medical biological nasal cavity rapid hemostatic powder also includes 1 part of calcium salt, which is a mixture of calcium lactate, calcium malate and calcium citrate in a weight ratio of 0.8:1:1.5.

[0092] A preparation method of medical biological nasal cavity quick hemostatic powder, comprising the steps of:

[0093] Step A, Weighing: Weigh the puffball ex...

Embodiment 2

[0097] A kind of quick hemostatic powder of medical biological nasal cavity, described medical biological quick hemostatic powder of nasal cavity comprises the raw material of following weight portion:

[0098] Puffball Extract 70 parts

[0099] Sodium carboxymethyl cellulose 11 parts

[0100] 2 parts large thistle extract

[0101] 2 parts coriander root extract

[0102] Sophora japonica extract 2 parts

[0103] 2 parts snakeberry extract

[0104] 0.8 part of orientalis leaf extract.

[0105] The sodium carboxymethylcellulose has a melting point of 272°C and a density of 1.55g / cm 3 croscarmellose sodium.

[0106] The medical biological nasal cavity rapid hemostatic powder also includes 2 points of sodium alginate, which is nano-scale ultrafine sodium alginate powder with a particle size of 30nm produced by aerosolized powder making technology.

[0107] A preparation method of medical biological nasal cavity quick hemostatic powder, comprising the steps of:

[0108] Ste...

Embodiment 3

[0112] A kind of quick hemostatic powder of medical biological nasal cavity, described medical biological quick hemostatic powder of nasal cavity comprises the raw material of following weight portion:

[0113] Puffball Extract 75 parts

[0114] Sodium carboxymethyl cellulose 12 parts

[0115] 3 parts large thistle extract

[0116] 3 parts coriander root extract

[0117] Sophora japonica extract 3 parts

[0118] 3 parts snakeberry extract

[0119] 1.0 part of Arborvitae leaf extract.

[0120] The sodium carboxymethyl cellulose is cross-linked sodium carboxymethyl cellulose with a melting point of 274° C. and a density of 1.6 g / cm3.

[0121] The medical biological nasal cavity rapid hemostatic powder also includes 3 parts of calcium salt, which is a mixture of calcium lactate, calcium malate and calcium citrate in a weight ratio of 1:1:2.

[0122] The medical biological nasal cavity rapid hemostatic powder also includes 3 points of sodium alginate, which is a nano-scale ult...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Densityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of medical materials, in particular to medical quick biological rhinal styptic powder and a preparation method thereof. The medical quick biological rhinal styptic powder is composed of, by weight, 65-85 parts of lasiosphaera seu calvatia extracts, 10-14 parts of sodium carboxymethylcellulose, 1-5 parts of cirsium japonicum extracts, 1-5 parts of lalang grass rhizome extracts, 1-5 parts of flos sophorae extracts, 1-5 parts of Indian mockstrawberry extracts and 0.5-1.5 parts of cacumen platycladi extracts. The medical quick biological rhinal styptic powder is capable of realizing stypticity by various means and evidently shortening blood clotting time, further has functions of bacteriostasis, antibiosis, analgesia and acceleration of wound healing and is widely applicable to postoperation quick hemostasis, pain relief and wound repair for nasal cavities, oral cavities and throats.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to a medical biological nasal cavity rapid hemostatic powder and a preparation method thereof. Background technique [0002] Blood coagulation process is very complicated, and there are about 13 factors participating in the reaction, and calcium is one of them. There is a folk practice of burning eggshells to stop bleeding, the principle is the role of calcium. The hemostatic properties of chitosan have been reported in a large number of literatures. The hemostatic mechanism is that positively charged amino groups combine with negatively charged red blood cells and platelet surfaces to form mucoadhesive clots and activate the traditional coagulation pathway. [0003] Chitosan is an alkaline polysaccharide obtained by deacetylation of chitin. Due to the amino group in chitosan molecule, it has many excellent properties such as biocompatibility, biodegradability, hemostasis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/40A61L15/28A61L15/44A61L15/42
Inventor 梁奕福
Owner DONGGUAN DAQING MEDICAL DEVICES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap