A kind of ceramic flower plate manufacturing process

A production process and a technology for flower discs, which are applied in the field of ceramic flower disc production technology, can solve problems such as undisclosed process methods, and achieve the effects of bright colors, clear textures and exquisite artistic techniques.

Active Publication Date: 2018-02-27
福建省德化县宝源陶瓷研究所
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ceramics have a long history in our country, and ceramic products have been loved by people throughout the ages. There are many kinds of ceramic products and they are widely used. They pervade our daily necessities and household items, as well as some exquisite ceramic handicrafts in different shapes, etc. , and for the existing ceramic handicrafts, the prior art has not disclosed the process of using ceramics to make flower discs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The ceramic faceplate manufacturing process of the present embodiment consists of the following steps:

[0026] a. Material selection

[0027] Dehua kaolin with pure white texture and few impurities is selected as the ceramic blank.

[0028] b. Modeling

[0029] According to the design concept of the faceplate, the pattern of the bottom faceplate is molded with a gypsum car to form a plaster mold. The size of the plaster mold should be enlarged according to the total shrinkage, taking into account the drying shrinkage and firing shrinkage, and then dried.

[0030] c. Forming of the base faceplate

[0031] First, put the processed ceramic blank into the wire pressing machine, and press it into porcelain lines with different thicknesses according to the needs; secondly, place the plaster mold on the wheel, and put the pressed porcelain lines on the dry plaster mold according to the Weave the hanging plate with texture. When weaving, weave from the inside to the outside...

Embodiment 2

[0048]The difference from Example 1 is that in step a, quartz is selected as the ceramic blank; in step d, the kiln door is first opened to allow the moisture in the green body to evaporate for 1 hour and then the kiln door is closed. The temperature of this process is controlled at 100 ° C. The time is 1 hour, and then the firing temperature is controlled at about 800 °, and the firing time is 3 hours, then the fire is turned off, and it is dried naturally; in step h, when the firing starts, there is a gap of 20 cm in the kiln door for water and air to discharge. When the firing temperature is 250°C, close the kiln door tightly. When the temperature inside the kiln reaches 1250°C, open the kiln door by 20 cm. After 6 hours, gradually cool down to 100°C, and then fully open the kiln door to cool down for 0.5 hour. After the temperature drops below 50°C, it starts to leave the kiln, and the green body is taken out for later use; in step i, the fired green body is dyed with patte...

Embodiment 3

[0050] The difference from Example 1 is that in step a, feldspar is selected as the ceramic blank; in step d, the kiln door is first opened to allow the moisture in the blank body to evaporate for 2 hours and then the kiln door is closed. The temperature of this process is controlled at 400 ° C. The firing time is 3 hours, and then the firing temperature is controlled at about 900°, the firing time is 6 hours, then the fire is turned off, and it is dried naturally; in step h, a 40 cm gap is left at the kiln door for water to escape when firing starts , when the firing temperature is 400°C, close the kiln door tightly, and when the temperature inside the kiln reaches 1400°C, open the kiln door by 40 cm. After 9 hours, gradually cool down to 300°C, and then fully open the kiln door to cool down for 2 hours. After the temperature drops below 200°C, the kiln starts to leave, and the green body is taken out for later use; in step i, the fired green body is dyed with a pattern outlin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing process of a ceramic faceplate, which is composed of the following steps: a. selecting materials such as quartz, feldspar or kaolin as a ceramic blank; b. using a gypsum car to mold the pattern of the bottom faceplate to form a plaster mold; c. Forming Press the ceramic blank to make porcelain lines; weave the porcelain lines on the plaster mold for hanging plates, demould and dry in the shade after weaving; d. Put the biscuit body into the kiln for baking; e. Glaze the body with dipping Glazing by glaze method; f, shaking the colored soil; g, carving decoration, first knead the branches with colored clay and paste them on the green body with mud, then paste flowers and leaves on the branches, and paste porcelain flowers on the flowers and leaves; h, Load and burn the green body into the kiln chamber for firing, first leave a gap in the kiln door, and then fire at low temperature, open the kiln door to cool down after firing, and take out the green body for later use; Painting on glaze. The ceramic faceplate processed by the invention is lifelike and has strong ornamental value.

Description

technical field [0001] The invention relates to a manufacturing process of a ceramic handicraft, in particular to a manufacturing process of a ceramic faceplate. Background technique [0002] Ceramics have a long history in our country, and ceramic products have been loved by people throughout the ages. There are many types of ceramic products and they are widely used. They pervade our daily necessities and household items, as well as some exquisite ceramic handicrafts in different shapes, etc. , and for the existing ceramic handicrafts, the prior art has not disclosed the process of utilizing pottery to make flower discs. Contents of the invention [0003] The object of the present invention is to provide a manufacturing process of using ceramics to process faceplate handicrafts. The ceramic faceplates processed by this manufacturing process are bright in color, clear in texture, lifelike, and have strong ornamental value. [0004] The manufacturing process of the cerami...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/622
Inventor 郑燕婷
Owner 福建省德化县宝源陶瓷研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap