A kind of first-class strengthening sanding agent for wood-plastic floor processing

A wood-plastic floor and sanding technology, applied in the field of floor processing, can solve the problems of waste of production costs and materials, a large amount of debris and powder, and the thinning of the floor, so as to improve the sanding effect and prevent the loss of materials.

Active Publication Date: 2017-07-04
安徽温禾新材料科技股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the sanding process uses a sanding machine. Although the sanding efficiency is high, a large amount of debris and powder will be generated during the sanding process, and the floor will become much thinner after sanding, which wastes production costs and materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] (1) First add 110 parts of gypsum powder, 35 parts of modified bamboo powder and 20 parts of eggshell powder into a high-speed mixer, heat up to 65-70°C and mix for 10 minutes, then add 15 parts of sugarcane wax, 15 parts of lard and 10 parts of Part rosin, continue to heat up to 95-100 ° C and mix for 15 minutes to obtain material I;

[0022] (2) Add 12 parts of humic acid and 12 parts of starch to 350 parts of water at room temperature, ultrasonicate for 20 minutes at an ultrasonic frequency of 22 kHz and a power of 100 W, then add 15 parts of bauxite, 8 parts of cyclodextrin and 15 parts of castor oil , and continued ultrasonic treatment for 15 minutes to obtain material II;

[0023] (3) Crush 15 parts of oil meal into powder, then add 10 parts of silica airgel, 12 parts of magnesium stearate and 6 parts of tartaric acid, mix well, heat up to 50-55°C and keep it for 20 minutes, then cool to After room temperature, add 6 parts of dibutyl phthalate, 5 parts of sodium ...

Embodiment 2

[0027] (1) First add 120 parts of gypsum powder, 30 parts of modified bamboo powder and 25 parts of eggshell powder into a high-speed mixer, heat up to 65-70°C and mix for 10 minutes, then add 20 parts of sugarcane wax, 15 parts of lard and 12 Part rosin, continue to heat up to 95-100 ° C and mix for 15 minutes to obtain material I;

[0028] (2) 14 parts of humic acid and 13 parts of starch were added to 380 parts of water at room temperature, ultrasonically treated at an ultrasonic frequency of 22kHz and a power of 100W for 20min, and then 15 parts of bauxite, 10 parts of cyclodextrin and 18 parts of castor oil were added , and continued ultrasonic treatment for 15 minutes to obtain material II;

[0029] (3) Crush 15 parts of oil meal into powder, then add 15 parts of silica airgel, 10 parts of magnesium stearate and 8 parts of tartaric acid, mix well, heat up to 50-55°C and keep it for 20 minutes, then cool to After room temperature, add 8 parts of dibutyl phthalate, 6 part...

Embodiment 3

[0033] (1) First add 120 parts of gypsum powder, 35 parts of modified bamboo powder and 22 parts of eggshell powder into a high-speed mixer, heat up to 65-70°C and mix for 10 minutes, then add 20 parts of sugarcane wax, 18 parts of lard and 10 parts of part rosin, continue to heat up to 95-100°C and mix for 15min to obtain material I;

[0034] (2) Add 15 parts of humic acid and 12 parts of starch to 400 parts of water at room temperature, ultrasonicate for 20 minutes at an ultrasonic frequency of 22 kHz and a power of 100 W, then add 15 parts of bauxite, 12 parts of cyclodextrin and 15 parts of castor oil , and continued ultrasonic treatment for 15 minutes to obtain material II;

[0035] (3) Crush 18 parts of oil meal into powder, then add 10 parts of silica airgel, 10 parts of magnesium stearate and 10 parts of tartaric acid, mix well, heat up to 50-55°C and keep it for 20 minutes, then cool to After room temperature, add 10 parts of dibutyl phthalate, 8 parts of sodium poly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a first-grade strengthened sanding agent for processing a wood-plastic floor, relating to the technical field of floor processing. The first-grade strengthened sanding agent is prepared from the following raw materials in parts by weight: 110-120 parts of gypsum powder, 30-35 parts of modified bamboo powder, 20-25 parts of eggshell powder, 15-20 parts of sugarcane wax, 15-20 parts of lard oil, 15-18 parts of oil meal, 12-16 parts of humic acid, 12-16 parts of starch, 10-15 parts of rosin, 10-15 parts of silica aerogels, 10-15 parts of bauxite, 8-12 parts of cyclodextrin, 8-12 parts of magnesium stearate, 6-10 parts of tartaric acid, 6-10 parts of dibutyl phthalate, 5-8 parts of sodium 3,3'-dithiodipropane sulfonate, 15-20 parts of castor oil, 35-40 parts of propylene glycol and 350-400 parts of water. The sanding agent disclosed by the invention can be directly coated on the surface of a wood-plastic floor to be sanded, and the wood-plastic floor to be sanded is sanded by using a sanding machine, so that not only can the sanding effect be improved, but also material loss caused by excessive sanding of the floor can be effectively avoided, in addition, the sanding agent can be directly wiped off after sanding, and the floor and residual toxic substances cannot be damaged.

Description

[0001] Technical field: [0002] The invention relates to the technical field of floor processing, in particular to a primary strengthening sanding agent for wood-plastic floor processing. [0003] Background technique: [0004] Wood-plastic flooring is a new type of environmentally friendly wood-plastic composite material product, which is mainly composed of wood powder (plant fiber) and thermoplastic polymer materials and processing aids, etc., mixed evenly and then heated and extruded by mold equipment. The high-tech green environmental protection material has both the performance and characteristics of wood and plastic, and can replace wood and plastic as a new type of mixed high-tech material. Wood-plastic flooring is a floor made of wood-plastic composite materials. It has the same woody feel and processing characteristics as wood. It can be sawed, drilled, and nailed with ordinary tools. It also has the water-resistant and anti-corrosion properties of plastic, making it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/02
Inventor 温中苏
Owner 安徽温禾新材料科技股份有限公司