Wide-adaptability double-mechanism self-lubricating bearing material

A self-lubricating bearing and dual-mechanism technology, applied in the field of powder metallurgy, can solve problems such as gaps, achieve stable performance, excellent resistance to dry wear, and reduce shrinkage

Inactive Publication Date: 2016-03-16
LIXIN JIANGHUAI YANGTIAN AUTOMOBILE
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although aluminum-based bearing materials have many excellent properties, there is still a big gap from practical application due to the limitations of aluminum-based powder metallurgy. Due to the problems in the manufacturing process, the quality of fired products needs to be improved, and further Improve performance Mass production expand its range of applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A wide-adaptation double-mechanism self-lubricating bearing material, made of the following raw materials in parts by weight (kg): aluminum 85, zinc 5, copper 3, tin 1, boron 0.5, polytetrafluoroethylene powder 3, molybdenum disulfide 0.8, Stearic acid 2, methyl cellulose 0.6, graphite 1, talcum powder 1, paraffin 0.6, iron powder 0.5, oleic acid amount;

[0015] Said a wide-adaptive double-mechanism self-lubricating bearing material is prepared by the following specific steps:

[0016] (1) Pour aluminum, zinc, copper, tin and boron powder into a mortar and grind them evenly, then add the mixed powder to a ball mill, add an appropriate amount of alcohol for wet ball milling, the ball milling speed is 20 rpm, After ball milling for 1 hour, the mixed powder is added to a vacuum oven, dried at 70°C and placed for subsequent use;

[0017] (2) Mix oleic acid and graphite into an ultrasonic oscillator to disperse evenly, then add the mixed powder prepared in step (1) and ult...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
crushing strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Vickers hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wide-adaptability double-mechanism self-lubricating bearing material. The material is prepared from, by weight, 85-90 parts of aluminum, 5-8 parts of zinc, 3-4 parts of copper, 1-2 parts of tin, 0.5-1 part of boron, 3-4 parts of polytetrafluoroethylene powder, 0.8-1.5 parts of molybdenum disulfide, 2-3 parts of stearic acid, 0.6-1 part of methylcellulose, 1-1.5 parts of graphite, 1-1.5 parts of talcum powder, 0.6-0.9 part of paraffin, 0.5-0.7 part of iron powder and an appropriate amount of oleic acid. The prepared material has good performance such as dry-grinding resistance, self-lubrication and inadhesion, and is uniform in structure and stable in performance.

Description

technical field [0001] The invention relates to the technical field of powder metallurgy, in particular to a self-lubricating bearing material with wide adaptability and dual mechanisms. Background technique [0002] Metal sintered oil-impregnated bearings are a kind of sintered material made by powder metallurgy process with metal powder as raw material. Metal sintered oil-containing products are inherently porous, and have the advantage that the number, size and distribution of voids can be freely adjusted during the manufacturing process. Sintered metal oil-impregnated bearings have been widely used in many fields such as automobiles, household appliances, transportation machinery, agricultural machinery, instruments and meters. Sintered metal oil-impregnated bearings mainly used in modern industry can be divided into copper-based, iron-based, copper-iron-based, etc. according to the base material. Aluminum is one of the most widely distributed elements in the earth's c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/05C22C21/10
CPCC22C1/05C22C21/10C22C32/0084C22C32/0089B22F2998/10B22F1/10B22F3/10B22F3/04
Inventor 邵磊邵凤耀靳怀卫于永涛胡志国
Owner LIXIN JIANGHUAI YANGTIAN AUTOMOBILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap