A kind of preparation method of glass fiber filter material with v-mo-ti denitration system

Abstract

The invention relates to a method for preparing a glass fiber filter material with a V-Mo-Ti denitrification system, which belongs to the technical field of industrial denitrification, and comprises the following steps: Step 1, preparation of dipping emulsion; Step 2, filter material dipping treatment; Step 3, High temperature setting treatment. The technical solution uses the "dipping-heat setting" process on the glass fiber filter material to thermally decompose the precursor in the denitrification catalyst, and the formed catalyst powder is firmly combined with the glass fiber filter material, so that the surface of the filter material forms a "V- The denitrification structure of Mo‑Ti denitrification system makes the treated glass fiber filter not only retain the strong dust removal and PM2. The beneficial effect is remarkable.

Description

technical field [0001] The invention relates to a preparation method of a glass fiber filter material with a V-Mo-Ti denitration system, belonging to the technical field of industrial denitration. Background technique [0002] With the vigorous development of my country's economy, the total amount of NOx emitted by the cement industry is increasing. At the same time, the country's requirements for environmental protection standards are becoming more and more stringent. At present, my country's cement kiln denitrification technology is still in its infancy. The reactor adopts low-dust and low-temperature arrangement, so it is generally arranged after the dust collector. At this time, the dust content in the working environment of the denitrification reactor is low, and the flue gas temperature is only about 200°C, and the denitrification catalyst commonly used in the denitrification reactor Most of the catalytic temperatures are higher than 300 ° C, resulting in poor denitrific...

AI Technical Summary

Problems solved by technology

[0002] With the vigorous development of my country's economy, the total amount of NOx emitted by the cement industry is increasing. At the same time, the country's requirements for environmental protection standards are becoming more and more stringent. At present, my country's cement kiln denitrification technology is still in its infancy. The reactor adopts low-dust and low-temperature arrangement, so it is generally arranged after the dust collector. At this time, the dust content in the working environment of the denitrification reactor is low, and the flue gas temperature is only about 200°C, and the denitrification catalyst commonly used in the denitrification reactor Most of the catalytic temperature is higher than 300 ℃, resulting in poor denitrification effect, and because of the need to use two sets of equipment for dust removal and denitrification, the production cost is high

Images