Anti-mildew plastic and preparation method thereof

A kind of anti-mildew, plastic technology, applied in the field of plastics

Inactive Publication Date: 2016-07-06
ANHUI YUEERWEI PLASTIC MACHINE CO LTD
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, plastics are often made into containers to hold objects, and after the objects are placed in plastic containers for a long time, mildew or a large number of bacteria will often occur at the contact between the objects and the container, thereby accelerating the corruption of the stored objects, especially is when the object is food

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention provides a method for preparing mildew-resistant plastics, the preparation method comprising:

[0014] 1) Mixing silicon dioxide, asbestos, kaolin, zinc borate, Chinese herbal medicine and water, decocting, and then filtering to take the filter cake to obtain antibacterial activators;

[0015] 2) Polyvinyl chloride, ethylene-ethyl acrylate copolymer, polyimide, tris (2,4-di-tert-butylphenyl) phosphite, sodium lauramide ethyl sulfate, carbon nanotubes, zirconium phosphate , bamboo leaf ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial activator are mixed, and then processed and molded to obtain mildew-proof plastic;

[0016] Among them, the Chinese herbal medicine contains Platycodon grandiflorum, Sophora japonica, Artemisia chinensis, Southern star, Huoxiang, Toon bark, Guan Zhong, Sanchaku, Chuantong bark, Schisandra chinensis, Jiuliming, Shanjiao and Sage chinensis.

[0017] In step 1) of the present invention, the consumption of each ...

Embodiment 1

[0027] 1) Silica, asbestos, kaolin, zinc borate, platycodon grandiflorum, sophora japonica, artemisia, southern star, Huoxiang, toona bark, Guanzhong, trichaku, Chuantongpi, Schisandra, Jiuliming, Shanjiao, Maqian Seedlings and water are mixed according to 100:68:19:12:29:24:21:27:35:39:17:30:7:24:17:26:13:600 and then decocted at 150°C for 30 hours. Then filter to get the filter cake to make the antibacterial active substance;

[0028] 2) Polyvinyl chloride (weight average molecular weight is 6000), ethylene-ethyl acrylate copolymer (weight average molecular weight is 10000), polyimide (weight average molecular weight is 5000), three (2,4-di-tert-butyl phenyl) phosphite, sodium lauramide ethyl sulfate, carbon nanotubes, zirconium phosphate, bamboo ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial active substances according to the ratio of 100:90:66:10 :25:9:17:19:17:60:53 Knead at 200°C for 5 hours, then extrude (die temperature at 193°C) to obtain anti-mi...

Embodiment 2

[0030] 1) Silica, asbestos, kaolin, zinc borate, platycodon grandiflorum, sophora japonica, artemisia, southern star, Huoxiang, toona bark, Guanzhong, trichaku, Chuantongpi, Schisandra, Jiuliming, Shanjiao, Maqian Seedlings and water are mixed according to the ratio of 100:50:17:9:23:21:17:25:31:36:14:27:4:21:14:24:10:500 and decocted at 140°C for 20 hours. Then filter to get the filter cake to make the antibacterial active substance;

[0031] 2) Polyvinyl chloride (weight average molecular weight is 5000), ethylene-ethyl acrylate copolymer (weight average molecular weight is 9000), polyimide (weight average molecular weight is 3000), three (2,4-di-tert-butyl phenyl) phosphite, sodium lauramide ethyl sulfate, carbon nanotubes, zirconium phosphate, bamboo ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial active substances according to the ratio of 100:80:45:8 : 20: 7: 15: 17: 13: 50: 45 Mixed at 195°C for 4 hours, and then extruded (die temperature at 190°C) ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a mildew-resistant plastic and a preparation method thereof. The method comprises: 1) decocting after mixing silicon dioxide, asbestos, kaolin, zinc borate, Chinese herbal medicine and water, and then filtering to obtain a filter cake to obtain Antibacterial activator; 2) Polyvinyl chloride, ethylene-ethyl acrylate copolymer, polyimide, three (2,4-di-tert-butylphenyl) phosphite, sodium lauramide ethyl sulfate, carbon nano tube, zirconium phosphate, bamboo leaf ketone, wollastonite fiber, vinyltrimethoxysilane and antibacterial activator are mixed, and then processed to make anti-mildew plastic; , Huoxiang, Chunpi, Guanzhong, Sanchaku, Chuantongpi, Schisandra, Jiuliming, Shanjiao and Horse Qianzi. The plastic prepared by the method has excellent antibacterial properties and mechanical strength, and at the same time, the raw material of the method is easy to obtain and the process is simple.

Description

technical field [0001] The invention relates to plastics, in particular to a mildew-resistant plastic and a preparation method thereof. Background technique [0002] Plastic is a high molecular compound polymerized by addition polymerization or polycondensation reaction with monomer as raw material. It is commonly known as plastic or resin. It can freely change its composition and shape. , Colorants and other additives. The main component of plastic is resin. The term resin was originally named after the lipids secreted by animals and plants, such as rosin, shellac, etc. Resin refers to a polymer compound that has not been mixed with various additives. Resin accounts for about 40%-100% of the total weight of plastic. The basic properties of plastics are mainly determined by the nature of the resin, but additives also play an important role. Some plastics are basically composed of synthetic resins, with no or few additives, such as plexiglass, polystyrene, etc. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/08C08L79/08C08K13/04C08K3/36C08K7/12C08K3/34C08K3/38C08K7/24C08K5/526C08K3/32C08K7/10C08K5/5425
CPCC08L27/06C08K2201/003C08K2201/011C08L23/0869C08L2205/03C08L79/08C08K13/04C08K3/36C08K7/12C08K3/346C08K2003/387C08K7/24C08K5/526C08K2003/321C08K7/10C08K5/5425
Inventor 水晓萍钱万水汤涛
Owner ANHUI YUEERWEI PLASTIC MACHINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap