GH4169 alloy steel electroslag remelting refining slag and method for performing electroslag re-melting on GH4169 alloy steel

A GH4169, electroslag remelting technology, which is applied in the field of electrometallurgy and black metal materials, can solve the problems of weak removal of harmful elements and inclusions, easy burning, poor surface finish of steel ingots, etc., and achieves unstable oxidation The effect of low content of substances and variable price oxides, simple preparation process, and good market application prospects

Active Publication Date: 2016-07-06
宝武特冶航研科技有限公司
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

GH4169 alloy steel is a nickel-based superalloy strengthened by body-centered square γ" and face-centered cubic γ' phase precipitation. The GH4169 alloy steel remelting slag used in the prior art makes the GH4169 alloy ste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • GH4169 alloy steel electroslag remelting refining slag and method for performing electroslag re-melting on GH4169 alloy steel
  • GH4169 alloy steel electroslag remelting refining slag and method for performing electroslag re-melting on GH4169 alloy steel
  • GH4169 alloy steel electroslag remelting refining slag and method for performing electroslag re-melting on GH4169 alloy steel

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1

[0029] A GH4169 alloy steel electroslag remelting refining slag, including the following components by weight: 65 parts of CaF 2 , 15 parts Al 2 O 3 , 12 parts CaO, 3 parts MgO and 5 parts TiO 2 .

[0030] The method of electroslag remelting GH4169 alloy steel using the above electroslag remelting refining slag includes the following steps:

[0031] 1) Prepare remelted refining slag according to the formula described in this embodiment, and bake the remelted refining slag at 800°C for 7 hours;

[0032] 2) Using GH4169 alloy steel as a consumable electrode, the electroslag remelting furnace is assembled, and the remelting refining slag baked in step 1) is added to the mold of the electroslag remelting furnace, and aluminum powder and The ferro-titanium powder is set to a voltage of 58V and a current of 2500A to be energized and arced to establish a slag pool; wherein the mass ratio of the aluminum powder, the ferro-titanium powder and the remelted refining slag is 10...

Example Embodiment

[0037] Example 2

[0038] A GH4169 alloy steel electroslag remelting refining slag, including the following components by weight: 60 parts of CaF 2 , 20 parts Al 2 O 3 , 10 parts CaO, 5 parts MgO and 5 parts TiO 2 .

[0039] The method of electroslag remelting GH4169 alloy steel using the above electroslag remelting refining slag includes the following steps:

[0040] 1) Prepare remelted refining slag according to the formula described in this embodiment, and bake the remelted refining slag at 750°C for 9 hours;

[0041] 2) Using GH4169 alloy steel as a consumable electrode, the electroslag remelting furnace is assembled, and the remelting refining slag baked in step 1) is added to the mold of the electroslag remelting furnace, and aluminum powder and Ferro-titanium powder, set a voltage of 57V and a current of 2700A to energize and start an arc to establish a slag pool; wherein the mass ratio of aluminum powder, ferro-titanium powder and the remelted refining slag is 11:8:100;

[0042...

Example Embodiment

[0046] Example 3

[0047] A GH4169 alloy steel electroslag remelting refining slag, including the following components by weight: 70 parts of CaF 2 , 15 parts Al 2 O 3 , 5 parts CaO, 6 parts MgO and 4 parts TiO 2 .

[0048] The method of electroslag remelting GH4169 alloy steel using the above electroslag remelting refining slag includes the following steps:

[0049] 1) Prepare remelted refining slag according to the formula described in this embodiment, and bake the remelted refining slag at 750°C for 8 hours;

[0050] 2) Using GH4169 alloy steel as a consumable electrode, the electroslag remelting furnace is assembled, and the remelting refining slag baked in step 1) is added to the mold of the electroslag remelting furnace, and aluminum powder and Ferro-titanium powder, set a voltage of 55V and a current of 3000A to energize and start an arc to establish a slag pool; wherein the mass ratio of aluminum powder, ferro-titanium powder and the remelted refining slag is 13:10:100;

[0051...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides GH4169 alloy steel electroslag remelting refining slag and a method for performing electroslag remelting on GH4169 alloy steel. The GH4169 alloy steel electroslag remelting refining slag comprises the following components in parts by weight: 60-70 parts of CaF2, 15-20 parts of Al2O3, 5-15 parts of CaO, 3-6 parts of MgO and 4-8 parts of TiO2. The method comprises: baking the remelting refining slag, taking the GH4169 alloy steel as a consumable electrode, assembling an electroslag remelting furnace, adding the baked remelting refining slag, aluminum powder and ferrotitanium powder into a crystallizer, turning on power for arc starting so as to establish a slag bath, and then performing remelting smelting on the consumable electrode under the protection of an inert gas. The refining slag provided by the invention has the characteristics of low melting point, low viscosity, high specific resistance, and relatively low air permeability in a high-temperature liquid state, and by adopting the refining slag, less aluminum and titanium elements during remelting of a GH4169 alloy can be over-burnt, so that the obtained steel ingots have bright and clean surfaces and also have qualified and uniform components.

Description

technical field [0001] The invention belongs to the technical field of electrometallurgy of black metal materials and relates to the technical field of electrometallurgy, in particular to GH4169 alloy steel electroslag remelting refining slag and a method for electroslag remelting of GH4169 alloy steel. Background technique [0002] "If you want to make good steel, you must make good slag" not only explains the relationship between slag and steel quality, but also points out the relationship between slag and steel quality and the importance of slag quality. The slag used for electroslag remelting is one of the key factors determining the quality of remelted steel and alloys. The selection of electroslag metallurgical slag system, proportion and slag amount has great significance for the metallurgical quality of electroslag steel, smelting technical and economic indicators and environmental protection. significance. Therefore, it is extremely important to select the slag sys...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B9/18B22D23/10C22C38/54C22C38/50C22C38/48C22C38/44C22C38/42
CPCB22D23/10C22B9/18C22C38/42C22C38/44C22C38/48C22C38/50C22C38/54
Inventor 秦洪伟
Owner 宝武特冶航研科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap