Additive capable of improving mechanical properties of ordinary starch and preparation method of additive

A technology of mechanical properties and additives, applied in the field of additives that can improve the mechanical properties of ordinary starch and its preparation, can solve problems such as unsatisfactory mechanical properties, hard and brittle starch size film, etc., to increase fluidity and increase elongation at break Elongation, the effect of improving mechanical properties

Inactive Publication Date: 2016-07-20
ZHEJIANG YUBO TEXTILE CO LTD
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the starch film is hard and brittle, and its mechanical properties are not satisfactory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Additive capable of improving mechanical properties of ordinary starch and preparation method of additive
  • Additive capable of improving mechanical properties of ordinary starch and preparation method of additive
  • Additive capable of improving mechanical properties of ordinary starch and preparation method of additive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] This additive is a compound: it is composed of ethylene glycol, glycerin, polyoxyethylene stearate, fatty alcohol polyoxyethylene ether, and silicone compound.

[0012] Components (unit, KG) of an auxiliary agent that can improve the mechanical properties (adhesion, abrasion resistance) of ordinary starch:

[0013]

[0014]

[0015] Described fatty alcohol polyoxyethylene ether is: emulsifier (nonionic surfactant), and its melting point is 20 ℃. The polyoxyethylene stearate is an emulsifier; its melting point is 40°C. The ethylene glycol is a solvent. The glycerol is a solvent. The silicone compound is a softener.

[0016] Auxiliary preparation method

[0017] Put the above materials into the container step by step, emulsify step by step with a high-speed emulsifier, then add each emulsified component into the same container, and then further emulsify into an emulsion, that is, the finished product.

[0018] Detailed additive preparation method: According to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an additive capable of improving the mechanical properties of ordinary starch. The additive comprises the following components in parts by mass: 15-30 parts of glycol, 20-30 parts of glycerin, 20-30 parts of fatty alcohol-polyoxyethylene ether, 10-20 parts of stearic acid polyoxyethylene ether and 5-10 parts of an organic silicon compound, wherein the melting point of the fatty alcohol-polyoxyethylene ether is 20 DEG C, and the melting point of the stearic acid polyoxyethylene ether is 40 DEG C. A preparation method of the additive comprises the following steps: adding the materials into containers in different steps, emulsifying by using a high-speed emulsifier in different steps, adding the emulsified components into one same container, and further emulsifying, thereby obtaining an emulsion, namely, a finished product. By adopting the additive, the mechanical properties (adhesion property and wearing resistance) of the ordinary starch can be improved.

Description

technical field [0001] The invention relates to an auxiliary agent capable of improving the mechanical properties of ordinary starch and a preparation method thereof. Background technique [0002] PVA (i.e. polyvinyl alcohol), starch, propylene, and wax flakes are generally used as the main slurry in the existing slurry formulations. However, this type of slurry has poor miscibility and poor film-forming integrity, especially for polyester-containing warp yarns. , the protective effect is not ideal. Propylene-based slurry has the disadvantage of moisture absorption and stickiness. PVA biochemical treatment takes a long time, which takes 900 days, and it is designated as unclean slurry by the Ministry of Environmental Protection. As a renewable plant resource, starch has a wide range of sources, low price, good biocompatibility and environmental friendliness, and has been used as an important size in the textile industry. However, the starch size film is hard and brittle, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/11D06M15/53D06M13/148C08L3/02C08L71/02C08K5/053
CPCD06M15/11C08K2201/014C08L3/02C08L71/02C08L2205/025C08L2205/03D06M13/148D06M15/53C08K5/053
Inventor 胡玉华
Owner ZHEJIANG YUBO TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products