Oil stain removing polishing cream for metal stainless steel and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A stainless steel and degreasing technology, which is applied in the field of degreasing polishing cream and its preparation, can solve the problems of impracticality and no decontamination effect, and achieve the effect of reducing costs
Inactive Publication Date: 2016-07-27
NANCHANG UNIV
View PDF3 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, for household stainless steel furniture, these products are not practical and have no decontamination effect
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0021] Weigh 20g of palm wax, 10g of glycerin, and 35g of white oil in container A, melt at 92°C and add 2g of oily dispersant. Stir well, add 10g nano-Al 2 o 3 Powder.
[0022] In container B, weigh 20g of deionized water, add 2g of glyceryl stearate and 5g of NP-10 emulsifier, add 1g of sodium gluconate and 1g of tetrasodium edetate, and stir well.
[0023] Pour the solution in container B into container A, stir for 10 minutes, and obtain the desired cream after cooling.
Embodiment 2
[0025] Weigh 20g of palm wax, 10g of glycerin, and 25g of white oil in container A, melt at 92°C and add 5g of oily dispersant. Stir well, add 10g nano-Al 2 o 3 Powder.
[0026] In container B, weigh 25g of deionized water, add 2g of glyceryl stearate and 5g of NP-10 emulsifier, add 1g of sodium gluconate and 1g of tetrasodium edetate, and stir well.
[0027] Pour the solution in container B into container A, stir for 10 minutes, and obtain the desired cream after cooling.
Embodiment 3
[0029] Weigh 25g of palm wax, 10g of glycerin, and 25g of white oil in container A, and add 4.5g of oily dispersant after melting at 92°C. Stir well, add 15g nano-Al 2 o 3 Powder.
[0030] In container B, weigh 20g of deionized water, add 2g of glyceryl stearate and 5g of NP-10 emulsifier, add 2g of sodium gluconate and 3g of tetrasodium edetate, and stir evenly.
[0031] Pour the solution in container B into container A, stir for 10 minutes, and obtain the desired cream after cooling.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention aims to provide dirt removing bright water cream for household stainless steel appliances and a preparation method thereof. The water stainless steel bright cream adopts water as solvent, so that the volatilization of organic solvent and the carbon emission are reduced, such advantages as greenness, environmental protection, low carbon and low cost are achieved, and the staff health is protected. Palm wax is added in the formula to achieve a brightening effect; glycerin and white oil are added in the formula to achieve lubricating and humidifying effects; an oil dispersing agent is added to mainly disperse nanometer Al2O3 powder. An emulsifying agent adopts glyceride and nonyl phenol polyoxyethylene ether NP-10. A chelating agent adopts ethylene diamine tetraacetic acid tetrasodium and sodium gluconate. The product is the water cream without causing pollution to the environment, has such three effects as stainless steel dirt removal, brightening and rust removal, and can largely reduce the cost.
Description
technical field [0001] The invention relates to a degreasing and polishing cream and a preparation method thereof, in particular to a metal stainless steel degreasing and polishing cream and a preparation method thereof. Background technique [0002] At present, there are many metal stainless steel polishing wax products on the market. These products are mainly used in the grinding and polishing of stainless steel products. Polishing wax is used as brightener, stearic acid and palmitic acid are used as lubricants, and aluminum oxide, iron oxide and chromium oxide Used as an abrasive to polish stainless steel. However, for household stainless steel furniture, these products are not practical and have no decontamination effect. Contents of the invention [0003] The object of the present invention is to provide a water-based cream for cleaning and brightening household stainless steel appliances and a preparation method thereof. Water-based stainless steel bright cream use...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more