Tile grout
A technology for grout and tile, applied in the field of grout, can solve the problems of alkali resistance, poor water resistance, no grinding, slag removal, etc., and achieve the effect of strong durability, enhanced shrinkage resistance and crack resistance.
Inactive Publication Date: 2016-08-24
CHONGQING YISHENG LIVABLE BUILDING MATERIAL SCI & TECH CO LTD
View PDF4 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, most of the currently available jointing agents on the market have poor alkali resistance and water resistance, and most of them will drop slag and will not be ground
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] The formula of tile jointing agent is: cement 15kg, silica sand 30kg, slag powder 15kg, wood cellulose 0.3kg, redispersible latex powder 2kg, thickener 0.8kg, water repellent 0.6kg and alkali inhibitor 0.6kg .
Embodiment 2
[0016] The formula of tile jointing agent is: cement 22kg, silica sand 20kg, slag powder 20kg, wood cellulose 0.2kg, redispersible latex powder 4kg, thickener 0.1kg, water repellent 1kg and alkali inhibitor 0.4kg.
Embodiment 3
[0018] The formula of tile jointing agent is: cement 18kg, silica sand 26kg, slag powder 17kg, wood cellulose 0.27kg, redispersible latex powder 3kg, thickener 0.4kg, water repellent 0.9kg and alkali inhibitor 0.5kg .
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a tile grout. The grout comprises the following components in parts by weight: 15-22 parts of cement, 20-30 parts of silica sand, 15-20 parts of slag powder, 0.2-0.3 part of lignocellulose, 2-4 parts of redispersible emulsion powder, 0.1-0.8 part of thickeners, 0.6-1 part of water repellent and 0.4-0.6 part of alkali inhibitor. The grout has the advantages of strong durability, no slag falling, waterproofness, resistance to alkali, wear and stain and capability of reinforcing shrinkage and crack resistance.
Description
technical field [0001] The invention relates to a jointing agent commonly used in the construction field, in particular to a ceramic tile jointing agent. Background technique [0002] Tile grout is a joint material used to fill the gaps between tiles and stones. It can be used with decorative materials such as tiles and stones to provide beautiful finishes and ensure the bonding and anti-seepage between the finishes. However, most of the pointing agents currently available on the market have poor alkali resistance and water resistance, and most of them will drop slag and will not be ground. Contents of the invention [0003] The purpose of the present invention is to provide a tile grouting agent. The purpose of the present invention is to realize through the following technical solutions: [0004] A ceramic tile jointing agent, the components of the jointing agent and the parts by weight of various components are: 15-22 parts of cement, 20-30 parts of silica sand, 15-20...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
Inventor 张帮勇
Owner CHONGQING YISHENG LIVABLE BUILDING MATERIAL SCI & TECH CO LTD