A kind of preparation method of cationic water-soluble polymer aqueous dispersion without stabilizer

A water-soluble polymer, cationic technology, applied in the field of preparing cationic water-soluble polymer aqueous dispersion, to achieve the effect of high effective solid content

Active Publication Date: 2019-02-19
ZHEJIANG UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The main purpose of the present invention is to overcome the deficiencies of using inorganic salt or polymer stabilizer in the existing polymerization method, utilize the interaction between cationic monomer and cationic water-soluble polymer itself, provide a kind of cationic water-soluble polymer without stabilizer Preparation method of polymer aqueous dispersion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Weigh 200g of acrylamide, 200g of methacryloyloxyethyltrimethylammonium chloride, and 400g of deionized water, pour them into a 1000mL jacketed reactor equipped with a stirrer and a thermometer, start nitrogen, heat up and stir , rotate at 150 rpm, wait for it to completely dissolve and heat up to 50°C, add 0.02g VA044 initiator, react for 12 hours, then add 0.02g VA044 initiator, and react for another 12 hours to obtain a uniform milky dispersion.

Embodiment 2

[0031] Weigh 60g of acryloyloxyethyl dimethyl benzyl ammonium chloride, 20g of methacryloyl oxyethyl dimethyl benzyl ammonium chloride, 720g of deionized water, pour into a 1000mL container equipped with a stirrer and a thermometer In the jacketed reactor, start to pass nitrogen, heat up and stir, and the speed is 10 rpm. After it is completely dissolved and heated to 40°C, add a redox initiator composed of 0.44g potassium persulfate and 0.2g sodium sulfite, and react for 0.5 After h, a homogeneous milky dispersion was obtained.

Embodiment 3

[0033]Weigh 40g of acrylamide, 40g of methacrylamide, 120g of acryloyloxyethyltrimethylammonium chloride, and 600g of deionized water, pour them into a 1000mL jacketed reactor equipped with a stirrer and a thermometer, and start to pass nitrogen , heat up and stir, the speed is 50 rpm, until it is completely dissolved and the temperature is raised to 20°C to be constant, add a redox initiator composed of 0.14g ammonium persulfate and 0.06g sodium bisulfite, and react for 8 hours to obtain a uniform milky Dispersions.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a stabilizer-free cationic water-soluble polymer aqueous dispersing liquid. Monomers are stirred in water, dissolved, heated to 20-70 DEG C and polymerized under the action of an initiator, wherein the weight ratio of the monomers to water is (1:1)-(1:9); the monomers comprise water-soluble cationic monomers. The monomers are matched with a polymerization condition synergistically, no inorganic salt is added in the polymerization process, no polymer stabilizers are added, the production cost is low, the content of effective solids in the water-soluble polymer dispersing liquid is high, the water-soluble polymer aqueous dispersing liquid can be used for white water recycling in the papermaking industry, waste water treatment in the printing and dyeing industry and the building material industry and can also be applied in occasions where inorganic salt and polymer stabilizers are forbidden, such as ore dressing, thickening of cosmetics, reinforcement of high-grade paper and the like, and the application field of the cationic water-soluble polymer aqueous dispersing liquid is broadened.

Description

technical field [0001] The present invention relates to a new method for preparing cationic water-soluble polymer aqueous dispersion, that is to say, there is no need to add inorganic salt or polymer stabilizer in the preparation process. Background technique [0002] Cationic water-soluble polymers have become the most widely used synthetic water-soluble polymers in the world. They are widely used in many fields such as sewage treatment, oil exploration, papermaking, textile printing and dyeing, mineral processing, and soil improvement. Industrial monosodium glutamate" and other reputation. [0003] At present, the industrial production methods of cationic water-soluble polymers include aqueous solution polymerization, inverse emulsion polymerization and inverse suspension polymerization. Each of these methods has its own advantages, but there are some insurmountable problems. Aqueous solution polymerization is currently the most important production method for cationic wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/56C08F220/34C08F226/02
CPCC08F220/34C08F220/56C08F226/02
Inventor 单国荣范维骁李志丹
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap