Quenching oil dedicated to small module gears and preparation method of quenching oil

A technology of small modulus gears and quenching oil, applied in quenching agents, manufacturing tools, heat treatment equipment, etc., can solve problems such as large deformation, inability to complete self-blackening, and uneven film formation on the alveolar surface, so as to improve efficiency , good quenching effect, reduce the effect of the process

Active Publication Date: 2016-09-21
马鞍山金泉工业介质科技有限公司
View PDF13 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the problems of large amount of deformation, inability to complete self-blackening in the quenching process and uneven film formation on the alveo

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0031] Example 1

[0032] A special quenching oil that can make small-modulus gears (gears with a modulus less than 1 mm) turn black after quenching. 0.6 part of blackening compound, 0.5 part of brightener, 0.6 part of surfactant, 0.04 part of antioxidant, and the kinematic viscosity of the refined base oil is 80~115mm 2 / s, acid value≤0.02mgKOH / g. The cooling compounding agent is a mixture of polyisobutylene and dialkylnaphthalene (the mass ratio of the two is 2:1); the blackening compounding agent is a short oil alkyd resin (purchased from Shanghai Yuanbang Paint Manufacturing Co., Ltd.), dyeing agent and The mixture of wetting agents (mass ratio is 5:1:1); brightener is the mixture of imidazoline oleate and methyl terpene resin (mass ratio is 1:1); antioxidant is alkylated diphenylamine ( CAS No.68921-45-9); the coloring agent is disperse black 9 (CAS No.12222-69-4); the wetting agent is nonylphenol polyoxyethylene ether (CAS No.9016-45-9); the surface The active agent w...

Example Embodiment

[0041] Example 2

[0042] A special quenching oil that can make small modulus gears (gears with a modulus less than 1 mm) turn black after quenching. 0.8 part of blackening compound, 0.7 part of brightener, 0.7 part of surfactant, 0.06 part of antioxidant, and the kinematic viscosity of the refined base oil is 80~115mm 2 / s, acid value≤0.02mgKOH / g. The cooling compounding agent is a mixture of polyisobutylene and dialkylnaphthalene (the mass ratio of the two is 2:1); the blackening compounding agent is a short oil alkyd resin (purchased from Shanghai Yuanbang Paint Manufacturing Co., Ltd.), dyeing agent and The mixture of wetting agents (mass ratio is 5:1:1); brightener is the mixture of imidazoline oleate and methyl terpene resin (mass ratio is 1:1); antioxidant is alkylated diphenylamine ( CAS No.68921-45-9); the coloring agent is disperse black 9 (CAS No.12222-69-4); the wetting agent is nonylphenol polyoxyethylene ether (CAS No.9016-45-9); the surface The active agent w...

Example Embodiment

[0051] Example 3

[0052] A special quenching oil that can make small modulus gears (gears with a modulus less than 1 mm) turn black after quenching. part, 0.5 part of blackening compound, 0.3 part of brightener, 0.8 part of surfactant, 0.05 part of antioxidant, and the kinematic viscosity of the refined base oil is 80~115mm 2 / s, acid value≤0.02mgKOH / g. The cooling compounding agent is a mixture of polyisobutylene and dialkylnaphthalene (the mass ratio of the two is 2:1); the blackening compounding agent is a short oil alkyd resin (purchased from Shanghai Yuanbang Paint Manufacturing Co., Ltd.), dyeing agent and The mixture of wetting agents (mass ratio is 5:1:1); brightener is the mixture of imidazoline oleate and methyl terpene resin (mass ratio is 1:1); antioxidant is alkylated diphenylamine ( CAS No.68921-45-9); the coloring agent is disperse black 9 (CAS No.12222-69-4); the wetting agent is nonylphenol polyoxyethylene ether (CAS No.9016-45-9); the surface The active a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Kinematic viscosityaaaaaaaaaa
Acid valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses quenching oil dedicated to small module gears and a preparation method of quenching oil, and belongs to the technical field of metal heat treatment. The quenching oil comprises the following components in parts by mass: 35 to 40 parts of refined base oil, 2 to 3 parts of a cooling compound agent, 0.5 to 0.8 part of a blackening compound agent, 0.3 to 0.7 part of a brightening agent, 0.6 to 0.8 part of a surfactant and 0.04 to 0.06 part of an antioxidant. The quenching oil is specially developed for the small module gears of which the module is 1 mm or below, the optimal utilization temperature is 100 to 110 DEG C, the fluidity of the quenching oil is good in the temperature range, the cooling velocity for the small module gears is moderate, protective films are formed on the surfaces of the gears through automatic blackening during quenching, the secondary coating antirust treatment on the surfaces after heat treatment is reduced, the resources are saved, the procedure is reduced, and the efficiency is improved.

Description

technical field [0001] The invention belongs to the technical field of metal heat treatment, and more specifically relates to a special quenching oil for small modulus gears and a preparation method thereof. Background technique [0002] A gear is a mechanical element with teeth on the rim that can continuously mesh to transmit motion and power. The application of gears in transmission has appeared very early. At the end of the 19th century, the principle of generative gear cutting method and special machine tools and cutting tools using this principle appeared one after another. With the development of production, the stability of gear operation was paid more attention. Gears and their gear products are important basic parts of mechanical equipment, and the main transmission parts of most complete sets of mechanical equipment are gear transmissions. China's gear industry is developing rapidly, and the scale of the industry is constantly expanding. During the "Eleventh Fiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C21D1/58C21D9/32
CPCC21D1/58C21D9/32
Inventor 郑益刘进刘祥李海岩郑景亮刘凌
Owner 马鞍山金泉工业介质科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka