Flux-cored wire capable of enhancing welding partition continuous self-protection effect and preparation method thereof

A technology of flux-cored welding wire and self-protection, which is applied in welding equipment, welding medium, welding/cutting medium/material, etc., can solve the problems of enhancing the continuous self-protection effect of welding partitions, which has not yet been seen, and achieves a simple and repeatable preparation method. The effect of uniform surface hardness and stable arc

Active Publication Date: 2016-10-12
JIANGSU UNIV OF SCI & TECH
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no technical report on enhancing the continuous self-protection effect of the welding zone by controlling the particle size of the components

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flux-cored wire capable of enhancing welding partition continuous self-protection effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A flux-cored welding wire that enhances the continuous self-protection effect of the welding zone, including a low-carbon steel strip and a flux core, the flux core is filled in the steel strip, and the composition of the flux core is prepared according to the following quality: including the low-carbon steel strip and the flux core, and the flux core The core is filled in the steel strip, and the composition of the drug core is prepared according to the following quality: 85g of 100 mesh high carbon ferrochromium, 1g of 100 mesh ferroboron, 8.5g of deoxidizer, 1g of arc stabilizer, 4.5g of 100 mesh iron pink. Among them, the deoxidizer is a mechanical mixture composed of silicon-manganese alloys of different particle sizes, graphite, aluminum powder and magnesium powder, specifically: 3g of 230-mesh silicon-manganese alloy, 3g of 50-mesh graphite, 2g of 50-mesh aluminum powder, 0.5 g of 50-mesh magnesium powder, the arc stabilizer is a mechanical mixture composed of po...

Embodiment 2

[0032] A flux-cored welding wire that enhances the continuous self-protection effect of the welding zone, including a low-carbon steel strip and a flux core, the flux core is filled in the steel strip, and the composition of the flux core is prepared according to the following quality: including the low-carbon steel strip and the flux core, and the flux core The core is filled in the steel strip, and the drug core components are prepared according to the following quality: 80g of 100 mesh high carbon ferrochrome, 2g of 100 mesh ferroboron, 13g of deoxidizer, 3g of arc stabilizer, and 2g of 100 mesh iron powder. Among them, the deoxidizer is a mechanical mixture composed of silicon-manganese alloys of different particle sizes, graphite, aluminum powder and magnesium powder, specifically: 4g of 230-mesh silicon-manganese alloy, 4g of 50-mesh graphite, 4g of 50-mesh aluminum powder, 1g The 50-mesh magnesium powder, the arc stabilizer is a mechanical mixture composed of potassium s...

Embodiment 3

[0034]A flux-cored welding wire that enhances the continuous self-protection effect of the welding zone, including a low-carbon steel strip and a flux core, the flux core is filled in the steel strip, and the composition of the flux core is prepared according to the following quality: including the low-carbon steel strip and the flux core, and the flux core The core is filled in the steel strip, and the composition of the drug core is prepared according to the following quality: 75g of 100 mesh high carbon ferrochrome, 3g of 100 mesh ferroboron, 14.5g of deoxidizer, 4g of arc stabilizer, 3.5g of 100 mesh iron pink. Among them, the deoxidizer is a mechanical mixture composed of silicon-manganese alloys of different particle sizes, graphite, aluminum powder and magnesium powder, specifically: 5g of 230-mesh silicon-manganese alloy, 5g of 50-mesh graphite, 3g of 50-mesh aluminum powder, 1.5 g of 50-mesh magnesium powder, and the arc stabilizer is a mechanical mixture composed of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a flux-cored wire capable of enhancing the welding partition continuous self-protection effect and a preparation method thereof. A low-carbon steel strip serves as a skin. A flux core is prepared from 70-85wt% of high-carbon ferrochrome, 1-3.5wt% of ferroboron, 8.5-18.5wt% of a deoxidizing agent, 1-5wt% of an arc stabilizing agent and the balance ferrous powder. By the total weight of the flux core, the deoxidizing agent is prepared from 3-6wt% of 230-mesh silicomanganese alloy, 3-6wt% of 50-mesh graphite, 2-4.5wt% of 50-mesh aluminum powder and 0.5-2wt% of 50-mesh magnesium powder. The arc stabilizing agent is a mechanical mixture formed by sodium potassium silicate and sodium carbonate, and the flux core accounts for 54-59wt% of the mass of the wire. The wire can effectively enhance the self-protection effect of various partitions (at the melting stage, the globular transfer stage and the molten pool stage) of the wire, an arc is stable, the manufacturability is good, and a surfacing layer is attractive in shape, high in hardness and good in wear resistance.

Description

technical field [0001] The invention belongs to the field of welding in material processing engineering, and in particular relates to a flux-cored welding wire which enhances the continuous self-protection effect of welding zones and a preparation method thereof. Background technique [0002] Self-shielded flux-cored wire is widely used in the field of wear-resistant surfacing welding due to its advantages of easy operation, no need for additional shielding gas, and high deposition efficiency. According to the theory of welding metallurgy, the whole welding process is carried out in "partition and continuous", the reaction is not limited to one molten pool, and the reaction has a staged characteristic. For traditional electrodes, it can generally be divided into three areas: coating reaction area, droplet reaction area and molten pool reaction area. By analogy, it can be considered that the welding metallurgical process of welding wire can generally be divided into three ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30B23K35/368B23K35/40
CPCB23K35/0266B23K35/3086B23K35/368B23K35/406
Inventor 刘大双魏萍
Owner JIANGSU UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap