Polyethylene seven-hole cinquefoil pipe and preparation method thereof

A plum-blossom tube and polyethylene technology, which is applied in the field of polyethylene seven-hole plum-blossom tube and its preparation, can solve the problems of inconvenient storage and transportation, poor low-temperature resilience, high density, etc., and achieves low friction coefficient, good low-temperature resilience and excellent Effects of rigidity and toughness

Inactive Publication Date: 2016-10-12
安庆市悦发管业有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the unreasonable ratio of raw materials, the commonly used plum tubes have a high density, inconvenient storage and transportation, and poor low-temperature resilience.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1. Preparation of filler masterbatch:

[0026] Weigh 50 parts of high-density polyethylene, 10 parts of alkali-free glass fiber, 0.3 parts of antioxidant, 5 parts of calcium carbonate, 5 parts of kaolin, 0.3 parts of coupling agent, 0.3 parts of compatibilizer, and 0.1 part of lubricant Add them together into a high-speed mixer and mix evenly, then add them into a twin-screw extruder, melt, extrude, water-cool, and pelletize to obtain filled masterbatches;

[0027] Among them, the processing temperature of the extruder is 140°C, 155°C, 160°C, 160°C, 165°C from the feeding port to the die port, the main engine speed is 60rpm, and the vacuum degree is 0.3MPa;

[0028] 2. Preparation of polyethylene seven-hole plum blossom tube:

[0029] Weigh 80 parts of low-density polyethylene, 4 parts of alkali-free glass fiber, 5 parts of filler masterbatch, 0.1 part of antioxidant, and 0.1 part of compatibilizer by weight, mix them together in a high-speed mixer, and then add them t...

Embodiment 2

[0032] 1. Preparation of filler masterbatch:

[0033] Weigh 60 parts of high-density polyethylene, 15 parts of alkali-free glass fiber, 0.4 parts of antioxidant, 8 parts of calcium carbonate, 10 parts of kaolin, 0.5 parts of coupling agent, 0.1 part of compatibilizer, and 1 part of toughening agent. Parts are added to a high-speed mixer and mixed evenly, then added to a twin-screw extruder, melted, extruded, water-cooled, and pelletized to obtain filled masterbatches;

[0034] Among them, the processing temperature of the extruder is 140°C, 155°C, 160°C, 160°C, 165°C from the feeding port to the die port, the main engine speed is 80rpm, and the vacuum degree is 0.3MPa;

[0035] 2. Preparation of polyethylene seven-hole plum blossom tube:

[0036] Weigh 70 parts of low-density polyethylene, 6 parts of alkali-free glass fiber, 1 part of filler masterbatch, 0.4 part of antioxidant, and 0.5 part of compatibilizer by weight, mix them together in a high-speed mixer, and then add th...

Embodiment 3

[0039] 1. Preparation of filler masterbatch:

[0040] Weigh 70 parts of high-density polyethylene, 5 parts of alkali-free glass fiber, 0.1 part of antioxidant, 10 parts of calcium carbonate, 7 parts of kaolin, 0.1 part of coupling agent, 0.5 part of compatibilizer, and 1 part of lubricant and 0.6 parts of toughening agent are added to a high-speed mixer and mixed evenly, then added to a twin-screw extruder, melted, extruded, water-cooled, and pelletized to obtain a filled masterbatch;

[0041] Among them, the processing temperature of the extruder is 140°C, 155°C, 160°C, 160°C, 165°C from the feeding port to the die port, the main engine speed is 75rpm, and the vacuum degree is 0.3MPa;

[0042] 2. Preparation of polyethylene seven-hole plum blossom tube:

[0043] Weigh 60 parts of low-density polyethylene, 8 parts of alkali-free glass fiber, 10 parts of filler masterbatch, 0.3 parts of antioxidant, and 0.3 parts of compatibilizer, mix them in a high-speed mixer, and then add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyethylene seven-hole cinquefoil pipe and a preparation method thereof. The polyethylene seven-hole cinquefoil pipe is composed of the following components by weight: 60-80 parts of low density polyethylene, 4-8 parts of alkali-free glass fiber, 1-10 parts of filling masterbatch, 0.1-0.4 part of an antioxidant, and 0.1-0.5 part of a compatilizer. The filling masterbatch is prepared from the following components by weight: 50-70 parts of high density polyethylene, 5-15 parts of alkali-free glass fiber, 0.1-0.4 part of an antioxidant, 5-10 parts of calcium carbonate, 5-10 parts of kaolin, 0.1-0.5 part of a coupling agent, 0.1-0.5 part of a compatilizer, and 0-1 part of a toughening agent. The polyethylene seven-hole cinquefoil pipe provided by the invention has the advantages of excellent rigidity and toughness, environmental corrosion resistance, oxidation resistance, and ageing resistance. The polyethylene seven-hole cinquefoil pipe provided by the invention has smooth inner wall and small friction coefficient, is convenient for optical cables or coaxial cables to pass through, cannot damage optical cables or coaxial cables, and is suitable for installation and use of communication lines in telecommunications, electric power and railway.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polyethylene (PE) plum blossom tube with seven holes and a preparation method thereof. Background technique [0002] Plum blossom tube is a plum blossom-shaped communication tube, which is suitable for the insertion of many cables such as optical cables, cables, and coaxial cables, and is widely used in telecommunications, radio and television, railways, military and other communication power. With the increasing demand for plum-blossom pipes, plum-blossom pipe manufacturers must control production costs and improve product quality as the top priority in order to stabilize or even expand their market share. [0003] The plum blossom tube adopts a porous integrated structure, which has good rigidity and uniform force. The friction coefficient of the inner wall of the product is small, the cable threading is light and fast, and the construction is simple and easy. Wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L51/06C08K13/04C08K7/14C08K3/26C08K3/34C08J3/22B29C47/92B29C48/92
CPCC08L23/06B29C48/92B29C2948/9258B29C2948/92704C08J3/226C08J2323/06C08J2423/06C08K2201/003C08K2201/014C08L2201/08C08L2203/18C08L2205/025C08L2205/035C08L2207/062C08L2207/066C08L51/06C08K13/04C08K7/14C08K2003/265C08K3/346
Inventor 季琨舒玉法舒琳季汝来马刚刘学辉
Owner 安庆市悦发管业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap