Aluminum alloy processing liquid as well as preparation method and application thereof

A technology of aluminum alloy and processing fluid, which is applied in the petroleum industry, lubricating composition, etc., can solve the problems of insufficient lubricity, foam resistance to hard water, and high requirements for finished product deployment, achieving reasonable proportioning, improved antibacterial ability, The effect of easy operation

Active Publication Date: 2016-10-12
上海壹萨化学科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is also a small amount of fully synthetic fluid used for aluminum alloy processing, but there are more or less defects such as insufficient lubrication, foam, and poor resistance to hard water.
The existing aluminum alloy processing fluids have the following defects: (1) Conventional semi-synthetic or microemulsions rely heavily on mineral oil, and semi-synthetic fluids and microemulsions with better performance often contain more than 20 kinds of additives, which

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1

[0024] The aluminum alloy processing fluid of the present invention comprises the following components in parts by mass: 25 kg of water-soluble polyester, 1 kg of phosphoric acid ester, 3 kg of boric acid, 25 kg of mixed alcohol amine, 3 kg of antirust agent, 3 kg of bactericide, 0.1 kg of defoaming agent, slow release Agent 0.3kg, pure water 39.6kg.

[0025] Wherein, the mixed alcohol amine includes 5 kg of monoethanolamine and 20 kg of triethanolamine. The antirust agent is a trivalent carboxylic acid, the sustained release agent is a benzotriazole derivative, and the fungicide is a fungicide MBM. TDS of pure water <20ms / cm. The use of mixed alcohol amines can adjust the pH value of the processing fluid. When the pH of the processing fluid is controlled at 8.8-9.2, the rust resistance of iron-based materials and the antibacterial ability of the product are greatly improved. Since monoethanolamine is relatively corrosive to aluminum alloys, we should not...

Example Embodiment

[0033] Example 2

[0034] The aluminum alloy processing fluid of the present invention includes the following components in parts by mass: 30 kg of water-soluble polyester, 2 kg of phosphoric acid ester, 23 kg of mixed alcohol amine, 4 kg of rust inhibitor, 3 kg of bactericide, 0.1 kg of defoamer, and 0.5 kg of slow-release agent , 37.4kg of purified water.

[0035] Wherein, the mixed alcohol amine includes 3kg of monoethanolamine and 20kg of diethanolamine. The antirust agent is a trivalent carboxylic acid, the sustained release agent is a benzotriazole derivative, and the fungicide is a fungicide MBM. TDS of pure water <20ms / cm.

[0036] Water-soluble polyester was purchased from ISA Company, model ES550; phosphate ester was purchased from ISA Company, model PE518; fungicide MBM was purchased from ISA Company; boric acid was purchased from Sanxiang Company of the United States; tricarboxylic acid was purchased from BASF Company, model It is L190; the benzotriazole derivat...

Example Embodiment

[0043] Example 3

[0044] The aluminum alloy processing fluid of the present invention includes the following components in parts by mass: 40 kg of water-soluble polyester, 1 kg of phosphoric acid ester, 3 kg of boric acid, 30 kg of mixed alcohol amine, 2 kg of antirust agent, 3 kg of bactericide, 0.1 kg of defoaming agent, slow release Agent 0.3kg, purified water 20.6kg.

[0045] Wherein, 5 kg of diethanolamine and 25 kg of diisopropanolamine are included in the mixed alcohol amine. The antirust agent is dibasic carboxylic acid, the sustained release agent is methyl benzotriazole, and the bactericide is bactericide MBM. TDS of pure water <20ms / cm.

[0046] Water-soluble polyester was purchased from ISA Company, model ES550; phosphate ester was purchased from ISA Company, model PE518; fungicide MBM was purchased from ISA Company; boric acid was purchased from Sanxiang Company of the United States; tricarboxylic acid was purchased from BASF Company, model It is L190; the ben...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses aluminum alloy processing liquid as well as a preparation method and application thereof. The aluminum alloy processing liquid comprises the following components in parts by mass: 25-40 parts of water-soluble polyester, 1-2 parts of phosphate, 0-3 parts of boric acid, 20-30 parts of mixed alcohol amine, 2-4 parts of antirust agent, 1-3 parts of antibacterial agent, 0.05-0.15 part of antifoaming agent, 0.3-0.5 part of slow release agent and 20-42 parts of purified water. The aluminum alloy processing liquid is prepared by the following steps: adding the purified water, boric acid, antirust agent, mixed alcohol amine, slow release agent, water-soluble polyester, phosphate, antibacterial agent, purified water and antifoaming agent into a blending kettle according to certain order; and then stirring uniformly. The aluminum alloy processing liquid disclosed by the invention is used for processing aluminum alloy. In the invention, the water-soluble polyester and phosphate are applied to the aluminum alloy processing liquid for the first time, and the proportion is reasonable; the preparation method is simple in steps and convenient to operate; and the prepared aluminum alloy processing liquid is obviously transparent in color without turbidness and has good lubricating property, foam stability, hard water resistance and antirust property.

Description

technical field [0001] The invention relates to a metal processing fluid, in particular to an aluminum alloy processing fluid and its preparation method and application. Background technique [0002] With the rapid development of the mechanical processing industry, the development and application of various new metal materials and the continuous improvement of the level of metal processing technology, the original metal processing fluids in my country have been continuously developed and eliminated. Aluminum alloy is currently a metal material widely used in automotive engines, transmissions, aviation equipment and other mechanical equipment industries. Therefore, the demand for aluminum alloy processing fluids is also very important. [0003] Conventional aluminum alloy processing fluids are mainly semi-synthetic or microemulsified metal processing fluids containing a certain amount of mineral oil. There is also a small amount of fully synthetic fluid used for aluminum all...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/02C10N30/06C10N30/12C10N30/18C10N40/20
CPCC10M173/02C10M2201/085C10M2201/087C10M2207/10C10M2209/102C10M2215/042C10M2215/223C10M2229/041C10N2030/06C10N2030/12C10N2030/18C10N2040/245
Inventor 许栋杰夏帅
Owner 上海壹萨化学科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap