Water-based acrylic emulsion adhesive capable of releasing negative ions and preparing method

A water-based acrylic and adhesive technology, applied in the direction of non-polymer adhesive additives, adhesive types, ester copolymer adhesives, etc., can solve problems such as human health hazards and chemical pollution, and achieve the elimination of pollution and odor , the effect of purifying the air

Active Publication Date: 2016-11-09
TECHNICAL INST OF PHYSICS & CHEMISTRY - CHINESE ACAD OF SCI
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, with the improvement of people's living standards, there is more and more demand for furniture, and the adhesives used in the furniture processing process, especially synthetic resin adhesives, will bring chemical pollution such as formaldehyde and benzene, which will cause harm to human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A water-based acrylic emulsion adhesive capable of releasing negative ions, comprising the following components in parts by weight: 1 part of acrylic acid, 20 parts of isooctyl acrylate, 27 parts of methyl methacrylate; 3 parts of styrene, sodium dodecylbenzenesulfonate 0.5 parts, 0.5 parts of alkylphenol polyoxyethylene ether formaldehyde condensate, 0.1 parts of ammonium persulfate, 0.8 parts of sodium bicarbonate, 0.1 parts of N-methylol acrylamide, 2 parts of modified nano-anion powder, 45 parts of deionized water share.

[0047] A kind of preparation method of the aqueous acrylic acid emulsion adhesive that can release negative ion, comprises the steps:

[0048] Step 1 prepares modified nano anion powder

[0049] Dissolve 100 parts of nano-anion powder in 300 parts of deionized water and ultrasonicate for 2 hours to obtain a suspension containing nano-anion powder; adjust the pH of the suspension to 9 with ammonia water, and then mix the suspension with 5 parts of...

Embodiment 2

[0056] A water-based acrylic emulsion adhesive capable of releasing negative ions, comprising the following components in parts by weight: 1 part of acrylic acid, 22 parts of isooctyl acrylate, 28 parts of methyl methacrylate, 1 part of sodium dodecylbenzenesulfonate, alkyl 1 part of phenol polyoxyethylene ether formaldehyde condensate, 0.1 part of ammonium persulfate, 0.8 part of sodium bicarbonate, 0.1 part of N-methylol acrylamide, 3 parts of modified nano-anion powder, 43 parts of deionized water.

[0057] A kind of preparation method of the aqueous acrylic acid emulsion adhesive that can release negative ion, comprises the steps:

[0058] The preparation method of modified nano negative ion powder is the same as embodiment 1

[0059] Step 2 Prepare water-based acrylic emulsion adhesive

[0060] 1) adding all the modified nano-anion powders to 5% deionized water, and then supersonicating to obtain a suspension containing modified nano-anion powders; adding all the ammoniu...

Embodiment 3

[0065] A water-based acrylic emulsion adhesive capable of releasing negative ions, comprising the following components in parts by weight: 1 part of acrylic acid; 20 parts of isooctyl acrylate; 27 parts of methyl methacrylate; 3 parts of styrene, sodium dodecylbenzenesulfonate 0.5 parts, 0.5 parts of alkylphenol polyoxyethylene ether formaldehyde condensate, 0.1 parts of ammonium persulfate, 0.8 parts of sodium bicarbonate, 0.1 parts of N-methylolacrylamide, 4 parts of modified nano-anion powder, 43 parts of deionized water share.

[0066] A kind of preparation method of the aqueous acrylic acid emulsion adhesive that can release negative ion, comprises the steps:

[0067] Step 1 prepares modified nano anion powder

[0068] The preparation method of modified nano negative ion powder is the same as embodiment 1

[0069] Step 2 Prepare water-based acrylic emulsion adhesive

[0070] 1) Add all the modified nano-anion powders to 10% deionized water, then perform ultrasonic trea...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based acrylic emulsion adhesive capable of releasing negative ions. The water-based acrylic emulsion adhesive capable of releasing negative ions is prepared from acrylic acid, iso-octyl acrylate, methyl methacrylate, styrene, anionic emulsifying agent, non-ionic emulsifying agent, initiating agent, pH buffering agent, cross-linking agent, modified nanometer negative ion powder and deionized water. According to the water-based acrylic emulsion adhesive capable of releasing the negative ions, the modified nanometer negative ion powder is grafted to a water-based acrylic adhesive with the chemical method, and the water-based acrylic adhesive capable of releasing negative ions is obtained; the water-based acrylic adhesive can be used for bonding between non-porous materials such as all kinds of cloth and wood and porous materials such as sponges, and pollution caused by an organic solvent adhesive to the environment is eliminated; meanwhile, the negative ions can be further released, the effects of purifying air and eliminating peculiar smell are achieved.

Description

technical field [0001] The invention relates to the technical field of adhesives. More specifically, it relates to a water-based acrylic emulsion adhesive capable of releasing negative ions and a preparation method thereof. Background technique [0002] With the increasing awareness of people's environment and health, the society no longer only pays attention to the adhesive performance of adhesives, and the environmental protection requirements for adhesives are becoming more and more stringent. The development of environmentally friendly green adhesives that meet the three requirements of "environmental protection, health, and safety" has become a reality. It is imperative. At the same time, with the improvement of people's living standards, there is more and more demand for furniture, and the adhesives used in furniture processing, especially synthetic resin adhesives, will bring chemical pollution such as formaldehyde and benzene, which will cause harm to human health. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/12C09J11/04C08F220/14C08F220/18C08F220/06C08F212/08C08F220/58C08F2/44
CPCC08F2/44C08F220/14C08F220/18C08F220/1808C08K3/00C08K9/06C08K2201/011C09J11/04C09J133/12C08F220/06C08F212/08C08F220/58
Inventor 李樾王凤奇杨辉
Owner TECHNICAL INST OF PHYSICS & CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com