Novel foaming material

A foaming material, a new technology, applied in the field of new foaming materials, can solve the problems of poor impact resistance, poor durability, etc., and achieve good wind pressure resistance, excellent thermal insulation, and high compressive strength.

Inactive Publication Date: 2016-11-16
张莘蔓
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a new type of foaming material to solve the problems of poor impact resistance and relatively poor durability of existing foamed bricks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel foaming material
  • Novel foaming material
  • Novel foaming material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The preparation method of the environmental protection brick comprises the following steps:

[0031] S1: Preparation of hollow bricks

[0032] Mix cement, shale ore, fly ash, tailings sand, and kaolin, and stir evenly at a speed of 200-400r / min to make hollow bricks;

[0033] S2: Preparation of new foam materials

[0034] S21: Stir cement, glyoxal and water evenly at a speed of 100-300r / min to prepare a slurry;

[0035] S22: Calcium silicate, calcium sulfate, bentonite, magnesium borate, corn stalk powder, AR glass fiber, carbon fiber, water reducer, foaming agent, foam regulator, catalyst, crosslinking agent and foam stabilizer Stir for 2-3 hours at a rotational speed of 60-100r / min to obtain a foam solution;

[0036] S23: Add the foam liquid prepared in step S22 to the slurry prepared in step S21, and stir evenly at a rotating speed of 150-200r / min to prepare a new foam material;

[0037] S3: Preparation of insulation bricks

[0038] Fill the cavity of the hollow...

Embodiment 1

[0041] An environmentally friendly brick, comprising a hollow brick as a brick body shell and a new type of foam material filled in the cavity of the brick body, the hollow brick includes the following raw materials in parts by weight: 55 parts of cement, 40 parts of shale ore, powder 30 parts of coal ash, 12 parts of tailings sand, and 9 parts of kaolin; the new foaming material is in parts by weight, including the following raw materials: 35 parts of cement, 3 parts of calcium silicate, 2 parts of calcium sulfate, and 2 parts of bentonite , 2 parts of magnesium borate, 1.8 parts of corn straw powder, 0.9 parts of AR glass fiber, 0.5 parts of carbon fiber, 2 parts of water reducer, 0.6 parts of foaming agent, 0.4 parts of foam regulator, 0.2 parts of catalyst, 0.5 parts of crosslinking agent , 0.3 parts of foam stabilizer, 25 parts of glyoxal, and 280 parts of water.

[0042] The particle size of the corn stalk powder is ≤300 μm, and the moisture content is ≤14%.

[0043] Th...

Embodiment 2

[0061]An environmentally friendly brick, comprising a hollow brick as a brick body shell and a new type of foam material filled in the cavity of the brick body, the hollow brick includes the following raw materials in parts by weight: 45 parts of cement, 35 parts of shale ore, powder 25 parts of coal ash, 8 parts of tailings sand, and 6 parts of kaolin; the new foaming material includes the following raw materials in parts by weight: 25 parts of cement, 2 parts of calcium silicate, 2 parts of calcium sulfate, and 2 parts of bentonite , 1 part of magnesium borate, 1.5 parts of corn straw powder, 0.6 parts of AR glass fiber, 0.4 parts of carbon fiber, 1.5 parts of water reducer, 0.2 parts of foaming agent, 0.2 parts of foam regulator, 0.1 part of catalyst, 0.3 parts of crosslinking agent , 0.1 parts of foam stabilizer, 20 parts of glyoxal, and 240 parts of water.

[0062] The particle size of the corn stalk powder is ≤300 μm, and the moisture content is ≤14%.

[0063] The water...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel foaming material which is prepared from, by weight, 25-45 parts of cement, 2-4 parts of calcium metasilicate, 2-3 parts of calcium sulfate, 2-3 parts of bentonite, 1-2 parts of magnesium borate, 1.5-2 parts of corn straw powder, 0.6-1.2 parts of AR glass fiber, 0.4-0.6 part of carbon fiber, 1.5-2.5 parts of water reducing agent, 0.2-0.8 part of foaming agent, 0.2-0.6 part of foaming adjusting agent, 0.1-0.3 part of catalyst, 0.3-0.6 part of cross-linking agent, 0.1-0.5 part of foam stabilizer, 20-30 parts of glyoxal and 240-300 parts of water. Concrete environment-friendly bricks prepared from the environment-friendly cement foaming material has the advantages of being good in heat insulation property and sound isolation effect, low in weight, resistant to press and the like.

Description

technical field [0001] The invention belongs to the technical field of building material preparation, and in particular relates to a novel foaming material. Background technique [0002] With the popularization of building energy saving and the continuous improvement of people's demand for the comfort of living environment, thermal insulation materials have been paid more and more attention by people. Existing thermal insulation composite bricks or blocks mainly include multiple forms such as inlaying thermal insulation materials, setting thermal insulation interlayers, thermal insulation holes, and trenches. As one of the thermal insulation materials for houses, non-fired foamed bricks at room temperature are more and more popular because of their thermal insulation, sound insulation, fire prevention, and strength superior to traditional thermal insulation materials. However, the foaming materials currently on the market have disadvantages such as poor impact resistance an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/00C04B38/02
CPCC04B28/00C04B38/02C04B2201/20C04B2201/32C04B2201/50C04B14/108C04B18/08C04B18/12C04B14/106C04B22/08C04B22/143C04B14/104C04B22/0013C04B18/24C04B14/42C04B14/386C04B24/24C04B24/12C04B24/045C04B2103/10C04B24/00C04B24/42C04B24/008
Inventor 张莘蔓
Owner 张莘蔓
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com