Low-gain and large-scattering angle metal film screen optical coating material, preparation method and spraying method thereof

A technology of optical coatings and scattering angles, applied in the direction of reflection/signal coatings, fireproof coatings, coatings, etc., can solve the problems that the screen cannot meet the needs of use, and achieve the effects of reducing gain, prolonging service life, and ensuring uniformity

Active Publication Date: 2016-12-21
WUHU STAR IMAX
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the application of laser light source movie projectors, the requirements for the screen have also changed. The brightness coefficient of the screen can be appropriately reduced on the original basis, and it becomes more important to improve the effective scattering angle of the screen. The ratio index and the uniformity of the surface are also very important, and the traditional screen can no longer meet the needs of use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-gain and large-scattering angle metal film screen optical coating material, preparation method and spraying method thereof
  • Low-gain and large-scattering angle metal film screen optical coating material, preparation method and spraying method thereof
  • Low-gain and large-scattering angle metal film screen optical coating material, preparation method and spraying method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Low-gain, large-scattering-angle metal screen optical coating, its components and the mass percent of each component are:

[0048]

[0049] The optimal mass percent of each component is:

[0050]

[0051]

[0052] The preparation method of metal screen optical coating with low gain and large scattering angle, the preparation steps are as follows:

[0053] Step 1: According to the proportion of each component, mix other raw materials except curing agent to prepare fabric, add a little prepared diluent to dilute to reduce viscosity and facilitate sanding;

[0054] Step 2: Grind the diluted fabric with a sand mill for 1 hour, take it out and use a bucket device, and store it in a sealed container for 24 hours;

[0055] Step 3: Take part of the solvent after 24 hours, add the curing agent in proportion and stir for 10 minutes, then let it stand for 1 hour, then add the prepared diluent, and the batcher adjusts the viscosity according to the temperature during batc...

Embodiment 2

[0070] Low-gain, large-scattering-angle metal screen optical coating, its components and the mass percent of each component are:

[0071]

[0072] The preparation method and spraying method of the low-gain and large-scattering-angle metal screen optical coating are the same as the first embodiment.

Embodiment 3

[0074] Low-gain, large-scattering-angle metal screen optical coating, its components and the mass percent of each component are:

[0075]

[0076] The preparation method and spraying method of the low-gain and large-scattering-angle metal screen optical coating are the same as the first embodiment.

[0077] In order to prove the effect brought by the present invention, a comparative experiment is carried out, the contrast group is a traditional screen, and the experimental group is the screen made by the technical scheme of embodiment two of the present invention, and the screen luminance coefficient and effective scattering angle and polarization Comparison test, the experimental test data of the comparison group see Figure 1 to Figure 3 , the screen brightness coefficient is 1.67, the polarization ratio is 140:1, and the effective scattering angle is 48°; the test data of the present invention is shown in Figure 4 to Figure 6 , the screen brightness coefficient is 1.65...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polarizationaaaaaaaaaa
degree of polarizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to low-gain and large-scattering angle metal film screen optical coating material, a preparation method and a spraying method thereof, wherein the components comprise, by mass, 30-35% of a A450 resin, 22-27% of flaky aluminum powder, 3-7% of a leveling agent, 3-4% of polysiloxane, 11-15% of overweight fine calcium carbonate, 5-8% of fumed silica, 1-2% of di-tert-butyl dimethylamino p-cresol, 7-10% of a N75 curing agent, 1-2% of methyl silicone oil, and 2-4% of a halogen-free flame retardant agent. According to the film screen treated through the preparation method and the spraying method, the effective scattering angle of the film screen is improved, the polarization ratio index of the film screen is ensured, the gain is reduced, the uniformity of the film screen surface is ensured, and the service life of the film screen is prolonged.

Description

technical field [0001] The invention relates to a screen optical coating, in particular to a metal screen optical coating with low gain and large scattering angle, a preparation method and a spraying method thereof. Background technique [0002] Screen, which refers to the white screen that displays the projection when playing a movie, is more common in many movie theaters and amusement parks. The viewing effect of movies is also affected by the quality of the screen to a certain extent. For example, the gain of the screen is the reflection ability of the screen to light, which is determined by the surface material of the screen. The main materials used in the market are white plastic, glass beads and metal curtains. Gain ranges from 0.8 to 2.4. With the application of laser light source movie projectors, the requirements for the screen have also changed. The brightness coefficient of the screen can be appropriately reduced on the original basis, and it becomes more import...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D201/00C09D5/18C09D5/33C09D7/12C09D7/06C09D7/00B05D1/02B05D3/04C09D7/47