Graphene-containing polyurethane antimicrobial adhesive and preparation method thereof

A graphene and antibacterial glue technology, applied in adhesive additives, non-polymer adhesive additives, etc., can solve the problems of bacteria, mold growth, affecting the aesthetics, service life and practical functions of the application carrier, and improve antibacterial performance, remarkable technological progress, and unique effects of technical formulas

Inactive Publication Date: 2017-01-04
JIUSHENG WOOD
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the actual application process of polyurethane adhesives, when the temperature and humidity conditions are suitable, bacteria, molds and other fungi will often be caused to grow, which will seriously affect the aesthetics, service life and actual functions of the application carrier.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-containing polyurethane antimicrobial adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1: a kind of polyurethane antibacterial adhesive with graphene, a kind of polyurethane antibacterial adhesive with graphene, is made of the raw material of following parts by weight: polytetrahydrofuran diol (molecular weight 3000) 60 parts, diphenyl 10 parts of methyl methane diisocyanate, 1 part of graphene oxide, 1.0 parts of polyoxyethylene polyoxypropylene pentaerythritol ether, 0.10 parts of Dabco33-LV, 15 parts of diisooctyl phthalate, p-toluenesulfonyl isocyanate 0.07 parts, 0.07 parts of γ-aminopropyltriethoxysilane, and 0.10 parts of 3,5-di-tert-butyl-4-hydroxyphenylpropionic acid octadecanoate.

[0043] Concrete preparation steps are:

[0044] 1) Weigh 600g of polytetrahydrofuran diol with a molecular weight of 3000 and put it into a reaction kettle, stir and heat to 100°C, and vacuumize and dehydrate for 4 hours;

[0045] 2) Add 10 g of polyoxyethylene polyoxypropylene pentaerythritol ether to polytetrahydrofuran diol cooled to room temperature a...

Embodiment 2

[0049] Embodiment 2: a kind of polyurethane antibacterial adhesive with graphene is made of the raw materials of following parts by weight: polytetrahydrofuran diol (molecular weight 3000) 60 parts, diphenylmethane diisocyanate 10 parts, graphene oxide 1.5 parts , 1.0 parts of polyoxyethylene polyoxypropylene pentaerythritol ether, 0.10 parts of Dabco33-LV, 15 parts of diisooctyl phthalate, 0.07 parts of p-toluenesulfonyl isocyanate, γ-aminopropyl triethoxy 0.07 parts of silane, 0.10 parts of 3,5-di-tert-butyl-4-hydroxyphenylpropionic acid octadecanoate.

[0050] Concrete preparation steps are:

[0051] 1) Weigh 600g of polytetrahydrofuran diol with a molecular weight of 3000 and put it into a reaction kettle, stir and heat to 100°C, and vacuumize and dehydrate for 4 hours;

[0052] 2) Add 10 g of polyoxyethylene polyoxypropylene pentaerythritol ether to polytetrahydrofuran diol cooled to room temperature after dehydration treatment, and mechanically stir to obtain a combined...

Embodiment 3

[0056] Embodiment 3: a kind of polyurethane antibacterial adhesive with graphene is made of the following raw materials in parts by weight: polytetrahydrofuran diol 48g, diphenylmethane diisocyanate 16g, graphene oxide 1.5g, polyoxyethylene polyoxygen Propylene pentaerythritol ether is 0.7g, Dabco33-LV is 0.12g, diisooctyl phthalate is 13g, p-toluenesulfonyl isocyanate is 0.09g, γ-aminopropyltriethoxysilane is 0.13g, 3,5 - 0.08 g of di-tert-butyl-4-hydroxyphenylpropanoic acid octadecanoate.

[0057] Concrete preparation steps are:

[0058] 1) Weigh polytetrahydrofuran diol with a molecular weight of 3000 and put it into a reaction kettle, stir and heat to 100°C, and vacuumize and dehydrate for 4 hours;

[0059] 2) Pour polyoxyethylene polyoxypropylene pentaerythritol ether into polytetrahydrofuran diol cooled to room temperature after dehydration treatment, and mechanically stir to obtain a combined material;

[0060] 3) Add graphene oxide to diphenylmethane diisocyanate, st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a graphene-containing polyurethane antimicrobial adhesive and a preparation method thereof. The graphene-containing polyurethane antimicrobial adhesive is prepared from the following raw materials in parts by weight: 5-20 parts of polyisocyanate, 0.2-2 parts of functionalized graphene, 40-60 parts of polylol, 10-20 parts of plasticizer, 0.05-0.15 part of catalyst, 0.1-1.5 parts of defoaming agent, 0.05-0.10 part of dehydrator, 0.05-0.20 part of coupling agent and 0.05-0.20 part of antioxidant. The method effectively improves the antibacterial property of the polyurethane adhesive and widens the application range of the polyurethane adhesive, thereby performing an active promoting function on industrial production of the high-performance polyurethane adhesive and wide application of the polyurethane adhesive in national industry.

Description

technical field [0001] The invention relates to a polyurethane antibacterial adhesive with graphene and a preparation method thereof, belonging to the technical field of adhesive production. Background technique [0002] Polyurethane adhesives are able to form a good chemical bond with the substrate and therefore exhibit excellent bonding. After decades of rapid development, polyurethane series adhesives have been widely used in various fields of national industry. [0003] However, in the actual application of polyurethane adhesives, when the temperature and humidity conditions are suitable, bacteria, molds and other fungi will often grow, which will seriously affect the aesthetics, service life and actual functions of the application carrier. Therefore, the development of polyurethane adhesives with excellent antibacterial properties has important social significance, and can also bring huge market returns. [0004] Graphene is called "the material of the 21st century". ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/08C09J11/06C09J11/04C08G18/48
CPCC08G18/48C09J11/04C09J11/06C09J175/08C08G18/4808C08G18/4837C08G18/4854C08K3/04C08K5/11C08K5/544C08K9/04C08K13/06
Inventor 孙龙祥吴忠其王艳伟黄成建
Owner JIUSHENG WOOD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap