Air filter for engine
An air filter and engine technology, applied in the direction of engine components, machines/engines, combustion air/combustion-air treatment, etc., can solve the problems of extended service life of filter elements, and achieve extended service life, good air filtration capacity, The effect of enhancing the self-cleaning ability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0047] A surface treatment process for a dust-falling board, comprising the following steps:
[0048] Step 1. Put the dust-falling board into the heat treatment furnace, and heat-treat the dust-falling board under an inert protective gas, place the dust-falling board in the heat treatment furnace at 1MPa, heat it to below 800°C in an inert protective gas, and keep it warm The time is 0.5h, and then when it is cooled to 50°C with the furnace, take it out and air-cool;
[0049] Step 2, after the heat treatment is completed, put it into a lubrication tank for surface lubrication treatment, the lubrication time is 3h, wherein the lubricating liquid is turbine oil, and the turbine oil contains 10wt% oil-soluble organic copper compound;
[0050] Step 3. After the surface lubrication treatment is completed, cold treatment is performed on the dust-falling board, and the cold treatment temperature is -80°C;
[0051] Step 4: After the cold treatment is completed, low-temperature temper...
Embodiment 2
[0053] A surface treatment process for a dust-falling board, comprising the following steps:
[0054] Step 1. Put the dust-falling board into the heat treatment furnace, and heat-treat the dust-falling board under an inert protective gas, place the dust-falling board in the heat treatment furnace at 2MPa, heat it to below 700°C in an inert protective gas, and keep it warm The time is 2 hours, and then when it is cooled to 50°C with the furnace, it is taken out and air-cooled;
[0055] Step 2, after the heat treatment is completed, put it into a lubrication tank for surface lubrication treatment, the lubrication time is 3h, wherein the lubricating liquid is turbine oil, and the turbine oil contains 10wt% oil-soluble organic copper compound;
[0056] Step 3. After the surface lubrication treatment is completed, cold treatment is performed on the dust-falling board, and the cold treatment temperature is -90°C;
[0057] Step 4. After the cold treatment is completed, low-temperatu...
Embodiment 3
[0059] A surface treatment process for a dust-falling board, comprising the following steps:
[0060] Step 1. Put the dust-falling board into the heat treatment furnace, and heat-treat the dust-falling board under an inert protective gas, place the dust-falling board in the heat treatment furnace at 1MPa, heat it to below 730°C in an inert protective gas, and keep it warm The time is 1h, and then when it is cooled to 50°C with the furnace, take it out and air cool;
[0061] Step 2, after the heat treatment is completed, put it into a lubrication tank for surface lubrication treatment, the lubrication time is 3h, wherein the lubricating liquid is turbine oil, and the turbine oil contains 10wt% oil-soluble organic copper compound;
[0062] Step 3. After the surface lubrication treatment is completed, cold treatment is performed on the dust-falling board, and the cold treatment temperature is -83°C;
[0063] Step 4. After the cold treatment is completed, low-temperature temperin...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com