A kind of preparation method of barium titanate nanotube array

A nanotube array and barium titanate technology, which is applied in the field of nanomaterial preparation and photocatalysis, can solve the problems of slow ion diffusion rate, template deformation, fracture, etc., and achieve the effect of delaying gelation time and preventing collapse

Active Publication Date: 2018-12-04
CHANGZHOU UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anodized aluminum template method is a common method for preparing nanotube arrays, but this method is subject to the confinement of the template, the ion diffusion rate in the template channel is slow, the path is long, and the reaction time is long. If the reaction time is too long, it will easily lead to deformation of the template. fragmentation, hydrolysis of reactants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The anodic alumina template with a pore diameter of 100nm was soaked with 5wt% phosphoric acid to obtain a double-pass porous alumina template; the double-pass porous alumina template was placed in the middle of the reactor, fixed, and the reactor was separated into two parts to form a double chamber reactor. Add 0.01M barium nitrate solution on one side of the double-chamber reactor; add 0.012M Ti(OC 4 H 9 ) 4 And 1.2×10 -3 M silver nitrate solution; the pH value of the solutions on both sides is controlled at 4-6; let stand in the air for 6 hours; take out the template, wipe the surface clean and dry it under an infrared lamp, in a muffle furnace at 5℃ The heating rate per minute was increased to 750°C for 1 hour; the excess AAO template in the product was removed with a 2mol / L NaOH solution to obtain a barium titanate nanotube array.

Embodiment 2

[0014] The anodic alumina template with a pore diameter of 100nm was soaked with 5wt% phosphoric acid to obtain a double-pass porous alumina template; the double-pass porous alumina template was placed in the middle of the reactor, fixed, and the reactor was separated into two parts to form a double chamber reactor. Add 0.01M barium nitrate solution on one side of the double-chamber reactor; add 0.014M Ti(OC 4 H 9 ) 4 And 1.4×10 -3 M silver nitrate solution; the pH value of the solutions on both sides is controlled at 4-6; let stand in the air for 6 hours; take out the template, wipe the surface clean and dry it under an infrared lamp, in a muffle furnace at 5℃ The heating rate per minute is increased to 750°C for 1 hour for annealing treatment. A 2mol / L NaOH solution was used to remove the excess AAO template in the product to obtain a barium titanate nanotube array.

Embodiment 3

[0016] The anodic alumina template with a pore diameter of 100nm was soaked with 5wt% phosphoric acid to obtain a double-pass porous alumina template; the double-pass porous alumina template was placed in the middle of the reactor, fixed, and the reactor was separated into two parts to form a double chamber reactor. Add 0.01M barium nitrate solution on one side of the dual-chamber reactor; add 0.016M Ti(OC 4 H 9 ) 4 And 1.6×10 -3 M silver nitrate solution; the pH value of the solutions on both sides is controlled at 4-6; let stand in the air for 6 hours; take out the template, wipe the surface clean and dry it under an infrared lamp, in a muffle furnace at 5℃ The heating rate per minute is increased to 750°C for 1 hour for annealing treatment. After removing the excess AAO template in the product with a 2mol / L NaOH solution, the titanate nanotube array was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a barium titanate nanotube array. According to the method, the barium titanate nanotube array is prepared through a two-way porous anodised aluminum template in a double-chamber reactor. Through use of silver nitrate as a Ti(OC4H9)4 stabilizer in the reaction process, gelation time is prolonged and soil with long-term stability is obtained. According to a diffusion coefficient and viscosity difference of cations in a water solution, a cationic ratio is adjusted and the barium titanate nanotube array structure with an ideal stoichiometric ratio is obtained.

Description

Technical field [0001] The invention relates to a method for preparing a barium titanate nanotube array, belonging to the technical field of nano material preparation and the technical field of photocatalysis. Background technique [0002] Barium titanate is a typical perovskite type ferroelectric body, BaTiO 3 The application research of the company mainly focuses on the fields of transducers, sensitive components and capacitors. The preparation of barium titanate nanomaterials is mainly nanocrystals, in addition to barium titanate nanorods and films. In recent years, people have discovered that BaTiO 3 As a perovskite-type oxide, it is also a type of photocatalyst. It can also generate photo-generated electrons and photo-generated holes under ultraviolet or visible light irradiation, which makes it have a wide range of application prospects in the field of photocatalysis. Barium titanate is used in the field of photocatalysis. The application of it puts forward new requirement...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/02
CPCB01J23/02B01J35/004
Inventor 陈智慧李志伟杨亚邱建华丁建宁袁宁一
Owner CHANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap