Ceramic brake pad

A technology of brake pads and ceramics, which is applied in the field of ceramic brake pads, can solve the problems of easily damaged friction discs, decreased wear resistance, and reduced strength and rigidity, and achieves the effects of no damage to friction discs, long service life, and high cost performance

Inactive Publication Date: 2017-02-22
马乐群
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the brake pads used in automobiles are mainly semi-metal brake pads, but the main disadvantages of this product are: (1) high density and high hardness, so it is easy to damage the friction disc, and it is easy to produce vibration and braking noise; (2) ) The thermal conductivity is high, and it is easy to cause air resistance in the braking system at high temperature, which can cause the friction layer to be separated from the steel plate, resulting in dangerous accidents; (3) Steel fibers are prone to rust, and the product is easy to wear decrease in strength and stiffness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] A ceramic brake pad, which is composed of the following components: nitrile rubber powder 1-5kg, sound-absorbing powder 5-10kg, resin 6-10kg, whiskers 3-8kg, brass fiber 3-8kg, short fiber 1-4kg, Friction powder 1~5kg, long fiber 1~4kg, ceramic fiber 8~16kg, high temperature barium 3~8kg, flake graphite (-195) 4~9kg, iron 0.5~3kg, petroleum coke 2~6kg, ceramic additive 8~ 13kg, wear-resistant powder 8-13kg, aramid fiber 0.5-3kg, wood fiber 1-4kg, ceramic grinding agent 2-6kg, antimony sulfide 1-4kg, stabilizer 3-8kg.

[0012] When making, weigh according to the above formula requirements, grind the material into fine particles, and then send it to the mixer for mixing; use the hot pressing mold for the prepared steel back and ingredients at a temperature of 160°C, a pressure of 115MPa, and a time of Hot press forming under the condition of 10min, put the above hot press formed product into a temperature-controlled drying furnace for heat treatment; finally, it can be us...

Embodiment 2

[0014] A ceramic brake pad consisting of the following components: nitrile rubber powder 3kg, silencing powder 7kg, resin 8kg, whisker 6kg, brass fiber 5kg, short fiber 2kg, friction powder 3 kg, long fiber 2kg, ceramic fiber 11kg , high temperature barium 5kg, flake graphite (-195) 6kg, iron 1.5kg, petroleum coke 4kg, ceramic additive 10kg, wear-resistant powder 10kg, aramid fiber 1.5kg, wood fiber 2kg, ceramic grinding agent 4kg, antimony sulfide 2kg, Stabilizer 5kg.

[0015] When making, weigh according to the above formula requirements, grind the material into fine particles, and then send it to the mixer for mixing; use the hot pressing mold for the prepared steel back and ingredients at a temperature of 160°C, a pressure of 115MPa, and a time of Hot press forming under the condition of 10min, put the above hot press formed product into a temperature-controlled drying furnace for heat treatment; finally, it can be used after spraying and trimming.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a ceramic brake pad, and belongs to the technical field of automobile brake. The ceramic brake pad is prepared from the following components: 1-5 kg of acrylonitrile butadiene rubber powder, 5-10 kg of noise reduction powder, 6-10 kg of resin, 3-8 kg of whiskers, 3-8 kg of brass fiber, 1-4 kg of short fiber, 1-5 kg of frictional powder, 1-4 kg of long fiber, 8-16 kg of ceramic fiber, 3-8 kg of high-temperature barium, 4-9 kg of crystalline flake graphite(-195), 0.5-3 kg of iron, 2-6 kg of petroleum coke, 8-13 kg of ceramic additives, 8-13 kg of wear-resisting powder, 0.5-3 kg of aramid fiber, 1-4 kg of wood fiber, 2-6 kg of ceramic toughening agents, 1-4 kg of antimony sulfide, and 3-8 kg of stabilizers. The ceramic brake pad has the characteristics that a friction disk is not damaged, no brake noise is generated, the temperature resistance is high, the service life is long, and stable braking is realized.

Description

technical field [0001] The invention relates to a ceramic brake pad, which belongs to the technical field of automobile braking. Background technique [0002] The automobile braking system is a key system that affects the safety of the automobile, and the stability and reliability of the braking system are directly determined by the comprehensive performance of the brake pads. At present, the brake pads used in automobiles are mainly semi-metal brake pads, but the main disadvantages of this product are: (1) high density and high hardness, so it is easy to damage the friction disc, and it is easy to produce vibration and braking noise; (2) ) The thermal conductivity is high, and it is easy to cause air resistance in the braking system at high temperature, which can cause the friction layer to be separated from the steel plate, resulting in dangerous accidents; (3) Steel fibers are prone to rust, and the product is easy to wear Decreased strength and rigidity. Thereby develo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): F16D69/02C09K3/14
CPCC09K3/149F16D69/02F16D2200/0039F16D2200/006
Inventor 马乐群
Owner 马乐群
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap