Fiber-reinforced porous explosion-proof concrete with negative poisson's ratio effect, and preparation

A technology of porous concrete and negative Poisson's ratio, which is applied in the construction field to improve the ability to resist and absorb blast load energy, improve the storage modulus, and improve the absorption capacity.

Active Publication Date: 2017-03-15
QINGDAO TECHNOLOGICAL UNIVERSITY
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the problems existing in the explosion-proof aspect of existing concrete, the present invention provides fiber-reinforced porous explosion-proof concrete and a preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber-reinforced porous explosion-proof concrete with negative poisson's ratio effect, and preparation
  • Fiber-reinforced porous explosion-proof concrete with negative poisson's ratio effect, and preparation
  • Fiber-reinforced porous explosion-proof concrete with negative poisson's ratio effect, and preparation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Example 1: Fiber-reinforced porous explosion-proof concrete with a continuous pore structure and a hexagonal concave fiber structure unit oriented orderly dense array reinforcement

[0044] A fiber-reinforced porous explosion-proof concrete with a negative Poisson's ratio effect. The fiber-reinforced porous explosion-proof concrete consists of a porous concrete matrix with a connected pore structure and a number of fiber structural units with special shapes; the fiber structural units are arranged in parallel The fiber hinge is composed of two layers of fiber hinges, the fiber hinge is a six-sided concave structure; the concave angle is β 1 =90°, the layer spacing is 15mm, the diameter of the circumscribed circle of the hexagonal axisymmetric polygon is 24mm, and the fiber is a fiber bundle with a diameter of 5mm spun from a steel fiber with a diameter of 0.2mm. Each fiber structure unit further includes a fixed fiber bundle in a vertical direction, and the plane of the fib...

Embodiment 2

[0061] Example 2: Fiber-reinforced porous explosion-proof concrete with a continuous hole structure and a hexagonal concave fiber structure unit oriented ordered barrier array reinforcement

[0062] The difference from Example 1 is that the fiber reinforced porous explosion-proof concrete with negative Poisson's ratio effect, the fiber structure unit is composed of three layers of fiber hinges arranged in parallel, and the concave angle is β 1 =120°, the layer spacing is 20mm, the diameter of the circumscribed circle of the hexagonal axisymmetric polygon is 20mm, and the fiber is a fiber bundle with a diameter of 4mm spun from a steel fiber with a diameter of 0.1mm. Among the plurality of fiber structural units that make up the explosion-proof fiber concrete is a directional and ordered barrier array (special concave / normal structure layer alternately and orderly arranged fiber concrete), such as Image 6 Shown in b. The cementing material is Portland cement, and the foam stabiliz...

Embodiment 3

[0065] Example 3: Fiber-reinforced porous explosion-proof concrete with directional and ordered interlayer cross-inlaid array reinforcements with connected pore structure and hexagonal concave fiber structure units

[0066] The difference from Example 1 is that the fiber reinforced porous explosion-proof concrete with negative Poisson's ratio effect, the fiber structure unit is composed of 4 layers of fiber hinges arranged in parallel, and the concave angle is β 1 =150°, the layer spacing is 30mm, the diameter of the circumscribed circle of the hexagonal axisymmetric polygon is 50mm, and the fiber is a fiber bundle with a diameter of 6mm spun from a steel fiber with a diameter of 0.6mm. The plurality of fiber structure units that make up the explosion-proof fiber concrete are oriented and ordered interlayer cross mosaic arrays (special concave / common structure ABA strip inlaid fiber concrete), such as Image 6 c is shown. The gelling material is expanded cement, and the foam stabi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses fiber-reinforced porous explosion-proof concrete with a negative poisson's ratio effect. The fiber-reinforced porous explosion-proof concrete consists of a porous concrete base body which is of an intercommunicating pore structure or an inwards sunken hole structure, and a reinforcing body array consisting of a plurality of fiber structure units with special forms, wherein each fiber structure unit with the special form consists of 2 to 4 layers of fiber hinges distributed in parallel, and an interlayer spacing is 10 to 50 mm; the fiber hinges are of axisymmetric polygonal structures with inwards sunken corners; the diameter of an external circle of each axisymmetric polygon is 9 to 54 mm. By combination of the porous concrete base body with the negative poisson's ratio effect and the specially-formed fiber structure units with the negative poisson's ratio effect, the minimum poisson's ratio of the original porous concrete base body can be -0.53 and -0.98 respectively, and the energy storage modulus is increased by 320 percent and 418 percent; the absorption capacity of an explosive load is improved more substantially, and the original structure cannot be damaged to an extremely large extent.

Description

Technical field [0001] The invention belongs to the field of construction, and relates to a fiber-reinforced porous concrete and a preparation method thereof, in particular to a fiber-reinforced porous explosion-proof concrete with a negative Poisson's ratio effect and a preparation method thereof. Background technique [0002] In recent years, there have been endless explosions in the domestic and international communities. The most direct measure for the destruction of personal property caused by explosive loads is to design effective explosion-proof materials for infrastructure. However, the traditional design concept of concrete is mainly to improve its own strength, and it cannot play a positive role in the dredging of the explosion process and the elimination of energy transfer. From the perspective of mechanics, the basic problem of explosion is energy rather than force. Therefore, when the load strength exceeds the critical value of strength, traditional concrete direct...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B28/04C04B28/14C04B28/34C04B28/06C04B38/02
CPCC04B28/00C04B28/04C04B28/06C04B28/14C04B28/34C04B2111/40C04B2201/50C04B38/02C04B24/383C04B22/08C04B2103/302C04B14/48C04B24/04
Inventor 马衍轩张颖锐杨蒙蒙管泽鑫李子哲黄胜扬汪鹤健
Owner QINGDAO TECHNOLOGICAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap