High-temperature-resisting water-based potassium silicate zinc-rich primer for surface treatment of steel structure and manufacturing method of high-temperature-resisting water-based potassium silicate zinc-rich primer

A technology of surface treatment and zinc-rich primer, which is applied in the direction of alkali metal silicate coatings, anti-corrosion coatings, fire-proof coatings, etc., can solve the problems of zinc powder easy to settle, easy to agglomerate, poor decorative effect, etc., to achieve enhanced repulsion and The effect of steric hindrance, increasing relative contact angle, storage and not easy to settle

Inactive Publication Date: 2017-04-26
TIANCHANG JULONG TRAVEL PAINT
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Inorganic substances have better electrical conductivity than organic substances, so zinc powder has a stronger cathodic protection effect. The corrosion resistance of water-based inorganic zinc-rich primers is far superior to organic zinc-rich coatings, but it also has the common problems of inorganic coatings, such as coating film Brittle and easy to crack, poor adhesion, poor decorative effect, etc., and organic materials have better flexibility after film formation, so some water-soluble emulsion can be added to the water-based inorganic zinc-rich primer as auxiliary film-forming material to make organic matter Fill in the "-Si-O-Si-" network structure to improve the flexibility of the coating. For example, the literature "Research on the Modification of Zinc-rich Coatings by Styrene-Acrylic Emulsion" prepared styrene-acrylic emulsion as a modifier. A kind of waterborne inorganic zinc-rich paint modified by styrene-acrylic emulsion
[0004] However, the literature only introduces the amount of styrene-acrylic emulsion added and the flexibility of the coating. With the continuous optimization of the production process and formula, it is found that the scale-shaped zinc powder is better than the spherical zinc powder in terms of covering ability, floating ability and shielding ability. The advantages are outstanding, so the scaly zinc powder has gradually become the preferred filler for zinc-rich coatings, but its activity is too strong in water-based inorganic silicate alkaline coatings, poor anti-sedimentation, and easy to agglomerate, resulting in rapid failure of the coating and uneven surface. To a certain extent, the application of coatings is limited
Therefore, it is an urgent problem to be solved at this stage to study a new multifunctional water-based inorganic zinc-rich anti-corrosion primer formula that can overcome the problems of easy sedimentation and poor dispersibility of zinc powder.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A water-based potassium silicate zinc-rich primer for surface treatment of high-temperature resistant steel structures, which is made of the following raw materials in parts by weight: flake zinc powder 102, potassium silicate 15, styrene-acrylic emulsion 10, turpentine 0.9, glass fiber 6, vinyl Trimethoxysilane 3.6, lanthanum nitrate 0.9, conductive carbon black 8, polyvinylpyrrolidone 0.2, nano zinc oxide 1.4, kelp extract 1, sodium benzoate 0.7, deionized water 25.

[0016] A method for preparing a water-based potassium silicate zinc-rich primer for surface treatment of high-temperature-resistant steel structures, comprising the following steps:

[0017] (1) Slowly add turpentine to the styrene-acrylic emulsion, heat up to 70-80°C, react at constant temperature for 20-30 minutes, cool to 50-60°C, add nano-zinc oxide for ultrasonic treatment for 25-30 minutes, add kelp extract to continue Ultrasonic treatment for 10-15 minutes to obtain modified styrene-acrylic emulsi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses high-temperature-resisting water-based potassium silicate zinc-rich primer for surface treatment of a steel structure. The high-temperature-resisting water-based potassium silicate zinc-rich primer is prepared from the following raw materials in parts by weight: 102 to 106 parts of flake zinc powder, 15 to 18 parts of potassium silicate, 10 to 11 parts of styrene-acrylic emulsion, 0.9 to 1.5 parts of turpentine oil, 6 to 8 parts of glass fiber, 3.6 to 3.9 parts of vinyl trimethoxy silane, 0.9 to 1.2 parts of lanthanum nitrate, 8 to 9 parts of conductive carbon black, 0.2 to 0.4 part of polyvinylpyrrolidone, 1.4 to 1.8 parts of nano zinc oxide, 1 to 2 parts of kelp extract, 0.7 to 0.9 part of sodium benzoate and 25 to 28 parts of de-ionized water. According to the high-temperature-resisting water-based potassium silicate zinc-rich primer, the styrene-acrylic emulsion is modified by the turpentine oil and then is added into the raw materials to be compounded with a potassium silicate solution; silane is doped with rare earth to commonly modify the flake zinc powder, and other effective auxiliary agents are matched to prepare the zinc-rich primer; the obtained zinc-rich primer has the advantages of high temprature resistance, good storage property and uneasiness of being precipitated; the one-step film forming thickness can reach 200mu.m; the zinc-rich primer is not cracked and does not fall off, and the salt fog resistance of a coating reaches 10000 hours.

Description

technical field [0001] The invention relates to the technical field of zinc-rich coatings, in particular to a water-based potassium silicate zinc-rich primer for surface treatment of high-temperature-resistant steel structures and a preparation method thereof. Background technique [0002] Zinc-rich primer is a type of anti-corrosion coating product that uses zinc powder with a sacrificial anode function as the main anti-rust pigment. It has a cathodic protection effect on steel substrates and has been widely used for ships, offshore oil production platforms, containers, docks, and gates for a long time. , storage tanks, pipelines and bridges, etc. protection. Currently commonly used mainly epoxy zinc-rich primers, alcohol-soluble inorganic zinc-rich primers and water-based inorganic zinc-rich primers. [0003] The water-based inorganic zinc-rich primer is a heavy-duty anti-corrosion coating with water as the solvent, silicate (including potassium silicate, sodium silicate,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/04C09D5/10C09D7/12
CPCC09D1/04C09D5/106C09D5/18C09D7/65
Inventor 孙巨福戴宇钧祝盆鑫祝秀凤汪鹏程
Owner TIANCHANG JULONG TRAVEL PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products